2006 |
|
|
Smirnov K, Korneev A, Minaeva O, Divochij A, Rubtsova I, Antipov A, et al. Superconducting single-photon detector for near- and middle IR wavelength range. In: Proc. 16th Int. Crimean Microwave and Telecommunication Technology. Vol 2.; 2006. p. 684–5.
Abstract: Presented in this paper are the results of research of NbN-film superconducting single-photon detector. At 2 K temperature, quantum efficiency in the visible light (0.56 mum) reaches 30-40 %. With the wavelength increase quantum efficiency decreases and comes to 20% at 1.55 mum and 0.02% at 5.6 mum. Minimum dark counts rate is 2times10-4s-1. The jitter of detector is 35 ps. The detector was successfully implemented for integrated circuits non-invasive optical testing. It is also perspective for quantum cryptography systems
|
|
|
|
Svechnikov SI, Finkel MI, Maslennikov SN, Vachtomin YB, Smirnov KV, Seleznev VA, et al. Superconducting hot electron bolometer mixer for middle IR range. In: Proc. 16th Int. Crimean Microwave and Telecommunication Technology. Vol 2.; 2006. p. 686–7.
Abstract: The developed directly lens coupled hot electron bolometer (HEB) mixer was based on 5 nm superconducting NbN deposited on GaAs substrate. The layout of the structure, including 30x20 mcm^2 active area coupled with a 50 Ohm coplanar line, was patterned by photolithography. The responsivity of the mixer was measured in a direct detection mode in the 25-64 THz frequency range. The noise performance of the mixer and the directivity of the receiver were investigated in a heterodyne mode. A 10.6 mum wavelength CW CO2 laser was utilized as a local oscillator.
|
|
|
|
Vachtomin YB, Antipov SV, Maslennikov SN, Smirnov KV, Polyakov SL, Zhang W, et al. Quasioptical hot electron bolometer mixers based on thin NBN films for terahertz region. In: Proc. 16th Int. Crimean Microwave and Telecommunication Technology. Vol 2.; 2006. p. 688–9.
Abstract: Presented in this paper are the performances of HEB mixers based on 2-3.5 nm thick NbN films integrated with log-periodic spiral antenna. Double side-band receiver noise temperature values are 1300 K and 3100 K at 2.5 THz and at 3.8 THz, respectively. Mixer gain bandwidth is 5.2 GHz. Local oscillator power is 1-3 muW for mixers with different active area
|
|
|
|
Вахтомин ЮБ, Антипов СВ, Масленников СН, Смирнов КВ, Поляков СЛ, Чжан В, et al. Квазиоптические смесители терагерцового диапазона на основе эффекта разогрева электронов в тонких пленках NbN. In: Proc. 16th Int. Crimean Microwave and Telecommunication Technology. Vol 2.; 2006. p. 688–9.
Abstract: Представлены результаты измерения рактеристик смесителей на эффекте разогрева электронов в тонких сверхпроводниковых пленках NbN. Смесители были изготовлены на основе пленок NbN толщиной 2-3.5 нм осажденных на кремниевую подложку с буферным подсло- ем MgO. Смесительный элемент согласовывался с планар- ной логопериодической спиральной антенной. Лучшее зна- чение шумовой температуры приемника на основе NbN смесителя составило 1300 К и 3100 К на частотах гетеро- дина 2.5 TГц и 3.8 ТГц, соответственно. Максимальное зна- чение полосы преобразования, измеренной на частоте 900 |Ц, достигло значения 5.2 ГГц для смесителя изготовлен- ного из NbN пленки толщиной 2 нм. Оптимальная мощность Представлены результаты измерения ха- гетеродинного источника составила 1-3 мкВт для смесите- лей с различным объемом смесительного элемента.
|
|