Tret’yakov, I. V., Ryabchun, S. A., Kaurova, N. S., Larionov, P. A., Lobastova, A. A., Voronov, B. M., et al. (2010). Optimum absorbed heterodyne power for superconducting NbN hot-electron bolometer mixer. Tech. Phys. Lett., 36(12), 1103–1105.
Abstract: Absorbed heterodyne power has been measured in a low-noise broadband hot-electron bolometer (HEB) mixer for the terahertz range, operating on the effect of electron heating in the resistive state of an ultrathin superconducting NbN film. It is established that the optimum absorbed heterodyne power for the HEB mixer operating at 2.5 THz is about 100 nW.
|
|
|
|
Manova, N. N., Korneeva, Y. P., Korneev, A. A., Slysz, W., Voronov, B. M., & Gol'tsman, G. N. (2011). Superconducting NbN single-photon detector integrated with quarter-wave resonator. Tech. Phys. Lett., 37(5), 469–471.
Abstract: The spectral dependence of the quantum efficiency of superconducting NbN single-photon detectors integrated with quarter-wave resonators based on Si3N4, SiO2, and SiO layers has been studied.
|
|
|
|
Voronov, B. M., Gershenzon, E. M., Gol'tsman, G. N., Gubkina, T. O., & Semash, V. D. (1994). Superconductive properties of ultrathin NbN films on different substrates. Sverkhprovodimost': Fizika, Khimiya, Tekhnika, 7(6), 1097–1102.
Abstract: A study was made on dependence of surface resistance, critical temperature and width of superconducting transition on application temperature and thickness of NbN films, which varied within the range of 3-10 nm. Plates of sapphire, fused and monocrystalline quartz, MgO, as well as Si and silicon oxide were used as substrates. NbN films with 160 μθ·cm specific resistance and 16.5 K (Tc) critical temperature were obtained on sapphire substrates. Intensive growth of ΔTc was noted for films, applied on fused quartz, with increase of precipitation temperature. This is explained by occurrence of high tensile stresses in NbN films, caused by sufficient difference of thermal coefficients of expansion of NbN and quartz.
|
|
|
|
Voronov, B. M., Gershenzon, E. M., Gol'tsman, G. N., Gogidze, I. G., Gusev, Y. P., Zorin, M. A., et al. (1992). Picosecond range detector base on superconducting niobium nitride film sensitive to radiation in spectral range from millimeter waves up to visible light. Sverkhprovodimost': Fizika, Khimiya, Tekhnika, 5(5), 955–960.
Abstract: Fast-operating picosecond detector of electromagnetical radiation is developed on the basis of fine superconducting film of niobium nitride with high sensitivity within spectral range from millimetric waves up to visible light. Detector sensitive element represents structure covering narrow parallel strips with micron sizes included in the rupture of microstrip line. Detecting ability of the detector and time constant measured using amplitude-simulated radiation of reverse wave tubes and pulse radiation of picosecond gas and solid-body lasers, constitute D*≅1010 W-1·cm·Hz-1/2 and τ≤5 ps respectively, at 10 K temperature. The expected value of time constant of the detector at 10 K obtained via extrapolation of directly measured dependence that is, τ ∝ τ-1, constitutes 20 ps. Experimental data demonstrate that detection mechanism is linked with electron heating effect.
|
|
|
|
Budyanskij, M. Y., Sejdman, L. A., Voronov, B. M., & Gubkina, T. O. (1992). Increase of reproducibility in production of superconducting thin films of niobium nitride. Sverkhprovodimost': Fizika, Khimiya, Tekhnika, 5(10), 1950–1954.
Abstract: Technique to control the composition of gas medium in the reactive magnetron discharge and the composition of the deposited films of niobium nitride using electrical parameters of discharge only, in particular, by δU = Up – Uar value at contant stabilized discharge current is described. Technique to select optimal condition for deposition of niobium nitride films when the films have composition meeting chemical formula, is suggested. Thin films of niobium nitride with up to 7 nm thickness and with rather high temperature of transition into superconducting state Tk > 10 K) and with low width of transition (δ < 0.6 K), are obtained. It is determined, that substrate material and dielectric sublayer do not affect. Tk value, while difference in coefficients of thermal expansion of substrate and of film affects δTk value.
|
|