Kawakami, A., Saito, S., & Hyodo, M. (2011). Fabrication of nano-antennas for superconducting Infrared detectors. IEEE Trans. Appl. Supercond., 21(3), 632–635.
Abstract: To improve the response performance of superconducting infrared detectors, we have developed a fabrication process for nano-antennas. A nano-antenna consists of a dipole antenna, and a superconducting thin film strip placed in the antenna's center. By measuring the transition temperature of the superconducting strips, we confirmed that their superconductivity maintained a good condition after the nano-antenna fabrication process. We also evaluated nano-antenna characteristics using Fourier transform infrared spectroscopy. The evaluated antenna length and width were respectively set at around 2400 nm and 400 nm, and the antennas were placed at intervals of several micrometers around the area of 1 mm2 . In an evaluation of spectral transmission characteristics, clear absorption caused by antenna effects was observed at around 1400 cm-1. High polarization dependencies were also observed.
|
Khosropanah, P. (2003). NbN and NbTiN hot electron bolometer THz mixers. Ph.D. thesis, Chalmers University of Technology, Göteborg.
Abstract: The thesis reports the development of Hot Electron Bolometer (HEB) mixers for radio astronomy heterodyne receivers in THz frequency range. Part of this work is the fabrication of HEB devices, which are based on NbN or NbTiN superconducting thin films (â‰<a4>5 nm). They are integrated with wideband spiral or double-slot planar antennas. The mixer chips are incorporated into a quasi-optical receiver. The experimental part of this work focuses on the characterization of the receiver as a whole, and the HEB mixers as a part. Double side band receiver noise temperature and the IF bandwidth are reported for frequencies from 0.7 THz up to 2.6 THz. The spectrum of the direct response of HEB integrated with dierent antennas are measured using Fourier Transform Spectrometer (FTS). The effect of the bolometer size on total receiver performance and the LO power requirements is also discussed. A high-yield and reliable process for fabrication of NbN HEB mixers have been achieved. Over 100 devices with different bolometer geometry, film property and also different antennas have been fabricated and measured. The measured data enables us to discuss the impact of different parameters to the receiver overall performance.
This work has provided NbN HEB mixers to the following receivers:
TREND (Terahertz REceiver with NbN HEB Device) operating at 1.25-1.5 THz, installed in AST/RO Submillimeter Wave Telescope, Amundsen/Scott South Pole Station, in 2002-2003.
Band 6-low (1.410-1.700 THz) and 6-high (1.700-1.920 THz) of the HIFI (Heterodyne Instrument for Far Infra-red) in the Herschel Space Observatory, due to launch in 2007 by ESA (European Space Agency).
Besides, there has been continuous efforts to develop better models to explain the mixer performance more accurately. They are based on two temperature model for electrons and phonons and solving one-dimensional heat balance equations along the bolometer. The principles of these models are illustrated and the calculated results are compared with measured data.
Keywords: HEB mixer, hot electron bolometer mixer, NbN, NbTiN, superconducting detector, heterodyne receiver, THz mixer, submillimeter mixer, quasioptical receiver, double slot antenna, twin slot antenna, spiral antenna, receiver noise, FTS, Fourier Transform Spectrometer
|
Larrey, V., Villegier, J. - C., Salez, M., Miletto-Granozio, F., & Karpov, A. (1999). Processing and characterization of high Jc NbN superconducting tunnel junctions for THz analog circuits and RSFQ. IEEE Trans. Appl. Supercond., 9(2), 3216–3219.
Abstract: A generic NbN Superconducting Tunnel Junctions (STJ) technology has been developed using conventional substrates (Si and SOI-SIMOX) for making THz spectrometers including SIS receivers and RSFQ logic gates. NbN/MgO/NbN junctions with area of 1 /spl mu/m/sup 2/, Jc of 10 kA/cm/sup 2/ and low sub-gap leakage current (Vm>25 mV) are currently obtained from room temperature sputtered multilayers followed by a post-annealing at 250/spl deg/C. Using a thin MgO buffer layer deposited underneath the NbN electrodes, ensures lower NbN surface resistance values (Rs=7 /spl mu//spl Omega/) at 10 GHz and 4 K. Epitaxial NbN [100] films on MgO [100] with high gap frequency (1.4 THz) have also been achieved under the same deposition conditions at room temperature. The NbN SIS has shown good I-V photon induced steps when LO pumped at 300 GHz. We have developed an 8 levels Al/NbN multilayer process for making 1.5 THz SIS mixers (including Al antennas) on Si membranes patterned in SOI-SIMOX. Using the planarization techniques developed at the Si-MOS CEA-LETI Facility, we have also demonstrated on the possibility of extending our NbN technology to high level RSFQ circuit integration with 0.5 /spl mu/m/sup 2/ junction area, made on large area substrates (up to 8 inches).
|
Krause, S., Mityashkin, V., Antipov, S., Gol'tsman, G., Meledin, D., Desmaris, V., et al. (2016). Study of IF bandwidth of NbN hot electron bolometers on GaN buffer layer using a direct measurement method. In Proc. 27th Int. Symp. Space Terahertz Technol. (pp. 30–32).
Abstract: In this paper, we present a reliable measurement method to study the influence of the GaN buffer layer on phonon-escape time in comparison with commonly used Si substrates and, in consequence, on the IF bandwidth of HEBs. One of the key aspects is to operate the HEB mixer at elevated bath temperatures close to the critical temperature of the NbN ultra-thin film, where contributions from electron-phonon processes and self-heating effects are relatively small, therefore IF roll-off will be governed by the phonon-escape.Two independent experiments were performed at GARD and MSPU on a similar experimental setup at frequencies of approximately 180 and 140 GHz, respectively, and have shown reproducible and consistent results. The entire IF chain was characterized by S-parameter measurements. We compared the measurement results of epitaxial NbN grown onto GaN buffer-layer with Tc of 12.5 K (4.5nm) with high quality polycrystalline NbN films on Si substrate with Tc of 10.5K (5nm) and observed a strong indication of an enhancement of phonon escape to the substrate by a factor of two for the NbN/GaN material combination.
|
Zolotov, P., Divochiy, A., Vakhtomin, Y., Moshkova, M., Morozov, P., Seleznev, V., et al. (2018). Photon-number-resolving SSPDs with system detection efficiency over 50% at telecom range. In Proc. AIP Conf. (Vol. 1936, 020019).
Abstract: We used technology of making high-efficiency superconducting single-photon detectors as a basis for improvement of photon-number-resolving devices. By adding optical cavity and using an improved NbN superconducting film, we enhanced previously reported system detection efficiency at telecom range for such detectors. Our results show that implementation of optical cavity helps to develop four-section device with quantum efficiency over 50% at 1.55 µm. Performed experimental studies of detecting multi-photon optical pulses showed irregularities over defining multi-photon through single-photon quantum efficiency.
|