Ekström, H., Karasik, B., Kollberg, E., Gol'tsman, G., & Gershenzon, E. (1995). 350 GHz NbN hot electron bolometer mixer. In Proc. 6th Int. Symp. Space Terahertz Technol. (pp. 269–283).
Abstract: Superconducting NbN hot-electron bolometer (HEB) mixer devices have been fabricated and measured at 350 GHz. The HEB is integrated with a double dipole antenna on an extended crystalline quartz hyper hemispherical substrate lens. Heterodyne measurement gave a -3 dB bandwidth, mainly determined by the electron- phonon interaction time, of about 680 and 1000 MHz for two different films with Tc = 8.5 and 11 K respectively. The measured DSB receiver noise temperature is around 3000 K at 800 MHz IF frequency. The main contribution to the output noise from the device is due to electron temperature fluctuations with the equivalent output noise temperature TFL-100 K. TH, has the same frequency dependence as the IF response. The contribution from Johnson noise is of the order of T. The RF coupling loss is estimated to be = 6 dB. The film with lower Tc, had an estimated intrinsic low-frequency conversion loss = 7 dB, while the other film had a conversion loss as high as 14 dB. The difference in intrinsic conversion loss is explained by less uniform absorption of radiation. Measurements of the small signal impedance shows a transition of the output impedance from the DC differential resistance Rd=dV/dI in the low frequency limit to the DC resistance R 0 =Uoff 0 in the bias point for frequencies above 3 GHz. We judge that the optimum shape of the IV-characteristic is more easily obtained at THz frequencies where the main restriction in performance should come from problems with the RF coupling.
|
Zorin, M., Lindgren, M., Danerud, M., Karasik, B., Winkler, D., Gol'tsman, G., et al. (1995). Nonequilibrium and bolometric responses of YBaCuO thin films to high-frequency modulated laser radiation. J. Supercond., 8(1), 11–15.
Abstract: Picosecond nonequilibrium and slow bolometric responses to infrared radiation from a patterned high-T c superconducting (HTS) film in resistive and normal states deposited onto LaAlO3, NdGaO3, and MgO substrates were investigated using both pulse and modulation techniques. The response time of 35 ps to a laser pulse of 17 ps FWHM has been observed. The intrinsic response time of the fast process is expected to be about a few picoseconds. The modulation technique, being free from the disadvantages of pulse methods (poor sensitivity, limited dynamic range), makes the detailed study of a number of relaxation processes possible. Besides the nonequilibrium response, two kinds of bolometric processes, namely phonon transport through the film-substrate interface and phonon thermal diffusion in a substrate, manifest themselves in certain frequency dependences.
|
Semenov, A. D., Nebosis, R. S., Gousev, Y. P., Heusinger, M. A., & Renk, K. F. (1995). Analysis of the nonequilibrium photoresponse of superconducting films to pulsed radiation by use of a two-temperature model. Phys. Rev. B, 52(1), 581–590.
Abstract: Photoresponse of a superconducting film in the resistive state to pulsed radiation has been studied in the framework of a model assuming that two different effective temperatures can be assigned to the quasiparticle and phonon nonequilibrium distributions. The coupled electron-phonon-substrate system is described by a system of time-dependent energy-balance differential equations for effective temperatures. An analytical solution of the system is given and calculated voltage transients are compared with experimental photoresponse signals taking into account the radiation pulse shape and the time resolution of the readout electronics. It is supposed that a resistive state (vortices, fluxons, network of intergrain junctions, hot spots, phase slip centers) provides an ultrafast connection between electron temperature changes and changes of the film resistance and thus plays a minor role in the temporal evolution of the response. In accordance with experimental observations a two-component response was revealed from simulations. The slower component corresponds to a bolometric mechanism while the fast component is connected with the relaxation of the electron temperature. Calculated photoresponse transients are presented for different ratios of the electron and phonon specific heat, radiation pulse durations and fluences, and frequency band passes of registration electronics. From the amplitude of the bolometric component we determine the radiation energy absorbed in a film. This enables us to reveal an intrinsic electron-phonon scattering time even if it is much shorter than the time resolution of readout electronics. We analyze experimental voltage transients for NbN, YBa2Cu3O7, and TlBa2Ca2Cu3O9 superconducting films and find the electron-phonon interaction times at the transition temperatures of 17, 2.5, and 1.8 ps, respectively. The values are in reasonable agreement with data of other experiments.
|
Gol'tsman, G. N., Karasik, B. S., Okunev, O. V., Dzardanov, A. L., Gershenzon, E. M., Ekstrom, H., et al. (1995). NbN hot electron superconducting mixers for 100 GHz operation. IEEE Trans. Appl. Supercond., 5(2), 3065–3068.
Abstract: NbN is a promising superconducting material for hot-electron superconducting mixers with an IF bandwidth larger than 1 GHz. In the 1OO GHz frequency range, the following parameters were obtained for 50 /spl Aring/ thick NbN films at 4.2 K: receiver noise temperature (DSB) /spl sim/1000 K; conversion loss /spl sim/10 dB; IF bandwidth /spl sim/1 GHz; and local oscillator power /spl sim/1 /spl mu/W. An increase of the critical current of the NbN film, increased working temperature, and a better mixer matching may allow a broader IF bandwidth up to 2 GHz, reduced conversion losses down to 3-5 dB and a receiver noise temperature (DSB) down to 200-300 K.
|
Karasik, B. S., Gol'tsman, G. N., Voronov, B. M., Svechnikov, S. I., Gershenzon, E. M., Ekstrom, H., et al. (1995). Hot electron quasioptical NbN superconducting mixer. IEEE Trans. Appl. Supercond., 5(2), 2232–2235.
Abstract: Hot electron superconductor mixer devices made of thin NbN films on SiO/sub 2/-Si/sub 3/N/sub 4/-Si membrane have been fabricated for 300-350 GHz operation. The device consists of 5-10 parallel strips each 5 /spl mu/m long by 1 /spl mu/m wide which are coupled to a tapered slot-line antenna. The I-V characteristics and position of optimum bias point were studied in the temperature range 4.5-8 K. The performance of the mixer at higher temperatures is closer to that predicted by theory for uniform electron heating. The intermediate frequency bandwidth versus bias has also been investigated. At the operating temperature 4.2 K a bandwidth as wide as 0.8 GHz has been measured for a mixer made of 6 nm thick film. The bandwidth tends to increase with operating temperature. The performance of the NbN mixer is expected to be better for higher frequencies where the absorption of radiation should be more uniform.
|
Zorin, M., Gol'tsman, G. N., Karasik, B. S., Elantev, A. I., Gershenzon, E. M., Lindgren, M., et al. (1995). Optical mixing in thin YBa2Cu3O7-x films. IEEE Trans. Appl. Supercond., 5(2), 2431–2434.
Abstract: High quality, j/sub c/ (77 K)>10/sup 6/ A/cm/sup 2/, epitaxial YBa2Cu3O7-x films of 50 nm thickness were patterned into ten parallel 1 /spl mu/m wide strips. The film structure was coupled to a single-mode fiber. Mixer response was obtained at 0.78 /spl mu/m using laser frequency modulation and an optical delay line. Using two semiconductor lasers at 1.55 /spl mu/m wavelength the beating signal was used to measure the photoresponse up to 18 GHz. Nonequilibrium photoresponse in the resistive state of the superconductor was observed. Bolometric response dominates up to 3 GHz, after which the nonequilibrium response is constant up to the frequency limit of our registration system. Using an electron heating model the influence of different thermal processes on the conversion loss has been analyzed. Ways of increasing the sensitivity are also discussed.
|
Karasik, B. S., & Elantiev, A. I. (1995). Analysis of the noise performance of a hot-electron superconducting bolometer mixer. In Proc. 6th Int. Symp. Space Terahertz Technol. (pp. 229–246). Pasadena, Ca.
Abstract: A theoretical analysis for the noise temperature of hot–electron superconducting mixer has been presented. Thecontributions of both Johnson noise and electron temperature fluctuations have been evaluated. A set of criteriaensuring low noise performance of the mixer has been stated and a simple analytic expression for the noisetemperature of the mixer device has been suggested. It has been shown that an improvement of the mixer sensitivitydoes not necessarily follow by a decrease of the bandwidth. An SSB noise temperature limit due to the intrinsic noisemechanisms has been estimated to be as low as 40–90 K for a mixer device made from Nb or NbN thin film.Furthermore, the conversion gain bandwidth can be as wide as is allowed by the intrinsic electron temperaturerelaxation time if an appropriate choice of the mixer resistance has been made. The intrinsic mixer noise bandwidthis of 3 GHz for Nb device and of 5 GHz for NbN device. An additional improvement of the theory has been madewhen a distinction between the impedance measured at high intermediate frequency (larger than the mixerbandwidth) and the mixer ohmic resistance has been taken into account.Recently obtained experimental data on Nb and NbNbolometer mixer devices are viewed in connection with thetheoretical predictions.The noise temperature limit has also been specified for the mixer device where an outdiffusion coolingmechanism rather than the electron–phonon energy relaxation determines the mixer bandwidth. A consideration ofthe noise performance of a bolometer mixer made from YBaCuO film utilizing a hot–electron effect has been done.
|
Karasik, B. S., Zorin, M. A., Milostnaya, I. I., Elantev, A. I., Gol’tsman, G. N., & Gershenzon, E. M. (1995). Subnanosecond switching of YBaCuO films between superconducting and normal states induced by current pulse. J. Appl. Phys., 77(8), 4064–4070.
Abstract: A study is reported of the current switching in high‐quality YBaCuO films deposited onto NdGaO3 and ZrO2 substrates between superconducting (S) and normal (N) states. The films 60–120 nm thick prepared by laser ablation were structured into single strips between gold contacts. The time dependence of the resistance after application of the voltage step to the film was monitored. Experiment performed within certain ranges of voltage amplitudes and temperatures has shown the occurrence of the fast stage (shorter than 400 ps) both in S‐N and N‐S transitions. A fraction of the film resistance changing within this stage in the S‐N transition increases with the current amplitude. A subnanosecond N‐S stage becomes more pronounced for shorter pulses. The fast switching is followed by the much slower change of resistance. The mechanism of switching is discussed in terms of the hot‐electron phenomena in YBaCuO. The contributions of other thermal processes (e.g., a phonon escape from the film, a heat diffusion in the film and substrate, a resistive domain formation) in the subsequent stage of the resistance dynamic have been also discussed. The basic limiting characteristics (average dissipated power, energy needed for switching, maximum repetition rate) of a picosecond switch which is proposed to be developed are estimated.
|
Ekstrom H., Karasik B. S., Kollberg E.L., & Yngvesson K.S. (1995). Conversion Gain and Noise of Niobium Superconducting Hot-Electron-Mixers. IEEE Trans. Microw. Theory Techn., 43, 938–947.
Abstract: A study has been done of microwave mixing at 20 GHz using the nonlinear (power dependent) resistance of thin niobium strips in the resistive state. Our experiments give evidence that electron-heating is the main cause of the nonlinear phenomenon. Also a detailed phenomenological theory for the determination of conversion properties is presented. This theory is capable of predicting the frequency-conversion loss rather accurately for arbitrary bias by examining the I-V-characteristic. Knowing the electron temperature relaxation time, and using parameters derived from the I-V-characteristic also allows us to predict the -3-dB IF bandwidth. Experimental results are in excellent agreement with the theoretical predictions. The require ments on the mode of operation and on the film parameters for minimizing the conversion loss (and even achieving conversion gain) are discussed in some detail. Our measurements demon-strate an intrinsic conversion loss as low as 1 dB. The maximum IF frequency defined for -3-dB drop in conversion gain, is about 80 MHz. Noise measurements indicate a device output noise temperature of about 50 K and SSB mixer noise temperature below 250 K. This type of mixer is considered very promising for use in low-noise heterodyne receivers at THz frequencies.
|
|
Hans Ekstrom, Karasik, B. S., Kollberg, E. L., & Sigfrid Yngvesson. (1995). Conversion gain and noise of niobium superconducting hot–electron–mixers. IEEE Trans. Appl. Supercond., 43(4), 938–947.
|