Vahtomin, Y. B., Finkel, M. I., Antipov, S. V., Voronov, B. M., Smirnov, K. V., Kaurova, N. S., et al. (2002). Gain bandwidth of phonon-cooled HEB mixer made of NbN thin film with MgO buffer layer on Si. In Harvard university (Ed.), Proc. 13th Int. Symp. Space Terahertz Technol. (pp. 259–270). Cambridge, MA, USA.
Abstract: We present recently obtained values for gain bandwidth of NbN HEB mixers for different substrates and film thicknesses and for MgO buffer layer on Si at LO frequency of 0.85-1 THz. The maximal bandwidth, 5.2 GHz, was achieved for the device on MgO buffer layer on Si with a 2 nm thick NbN film. Functional devices based on NbN films of such thickness were fabricated for the first time due to an improvement of superconducting properties of NbN film deposited on MgO buffer layer on Si substrate.
|
|
|
|
Gol'tsman, G. N., Vachtomin, Y. B., Antipov, S. V., Finkel, M. I., Maslennikov, S. N., Smirnov, K. V., et al. (2005). NbN phonon-cooled hot-electron bolometer mixer for terahertz heterodyne receivers. In Proc. SPIE (Vol. 5727, pp. 95–106).
Abstract: We present the results of our studies of NbN phonon-cooled HEB mixers at terahertz frequencies. The mixers were fabricated from NbN film deposited on a high-resistivity Si substrate with an MgO buffer layer. The mixer element was integrated with a log-periodic spiral antenna. The noise temperature measurements were performed at 2.5 THz and at 3.8 THz local oscillator frequencies for the 3 x 0.2 μm2 active area devices. The best uncorrected receiver noise temperatures found for these frequencies are 1300 K and 3100 K, respectively. A water vapour discharge laser was used as the LO source. The largest gain bandwidth of 5.2 GHz was achieved for a mixer based on 2 nm thick NbN film deposited on MgO layer over Si substrate. The gain bandwidth of the mixer based on 3.5 nm NbN film deposited on Si with MgO is 4.2 GHz and the noise bandwidth for the same device amounts to 5 GHz. We also present the results of our research into decrease of the direct detection contribution to the measured Y-factor and a possible error of noise temperature calculation. The use of a square nickel cell mesh as an IR-filter enabled us to avoid the effect of direct detection and measure apparent value of the noise temperature which was 16% less than that obtained using conventional black polyethylene IR-filter.
|
|
|
|
Sobolewski, R., Xu, Y., Zheng, X., Williams, C., Zhang, J., Verevkin, A., et al. (2002). Spectral sensitivity of the NbN single-photon superconducting detector. IEICE Trans. Electron., E85-C(3), 797–802.
Abstract: We report our studies on the spectral sensitivity of superconducting NbN thin-film single-photon detectors (SPD's) capable of GHz counting rates of visible and near-infrared photons. In particular, it has been shown that a NbN SPD is sensitive to 1.55-µm wavelength radiation and can be used for quantum communication. Our SPD's exhibit experimentally measured intrinsic quantum efficiencies from 20% at 800 nm up to 1% at 1.55-µm wavelength. The devices demonstrate picosecond response time (<100 ps, limited by our readout system) and negligibly low dark counts. Spectral dependencies of photon counting of continuous-wave, 0.4-µm to 3.5-µm radiation, and 0.63-µm, 1.33-µm, and 1.55-µm laser-pulsed radiations are presented for the single-stripe-type and meander-type devices.
|
|