Samsonova, A. S., Zolotov, P. I., Baeva, E. M., Lomakin, A. I., Titova, N. A., Kardakova, A. I., et al. (2021). Signatures of surface magnetic disorder in niobium films. IEEE Trans. Appl. Supercond., 31(5), 1–5.
Abstract: We present our studies on the evolution of the normal and superconducting properties with thickness of thin Nb films with a low level of non-magnetic disorder ( kFl≈150 for the thickest film in the set). The analysis of the superconducting behavior points to the presence of magnetic moments, hidden in the native oxide on the surface of Nb films. Using the Abrikosov-Gorkov theory, we obtain the density of surface magnetic moments of 1013 cm −2 , which is in agreement with the previously reported data for Nb films.
|
|
|
|
Goltsman, G., Korneev, A., Minaeva, O., Rubtsova, I., Chulkova, G., Milostnaya, I., et al. (2005). Advanced nanostructured optical NbN single-photon detector operated at 2.0 K. In M. Razeghi, & G. J. Brown (Eds.), Proc. SPIE (Vol. 5732, pp. 520–529). Spie.
Abstract: We present our studies on quantum efficiency (QE), dark counts, and noise equivalent power (NEP) of the latest generation of nanostructured NbN superconducting single-photon detectors (SSPDs) operated at 2.0 K. Our SSPDs are based on 4 nm-thick NbN films, patterned by electron beam lithography as highly-uniform 100÷120-nm-wide meander-shaped stripes, covering the total area of 10x10 μm2 with the meander filling factor of 0.7. Advances in the fabrication process and low-temperature operation lead to QE as high as 30-40% for visible-light photons (0.56 μm wavelength)-the saturation value, limited by optical absorption of the NbN film. For 1.55 μm photons, QE was 20% and decreased exponentially with the wavelength reaching 0.02% at the 5-μm wavelength. Being operated at 2.0-K temperature the SSPDs revealed an exponential decrease of the dark count rate, what along with the high QE, resulted in the NEP as low as 5x10-21 W/Hz-1/2, the lowest value ever reported for near-infrared optical detectors. The SSPD counting rate was measured to be above 1 GHz with the pulse-to-pulse jitter below 20 ps. Our nanostructured NbN SSPDs operated at 2.0 K significantly outperform their semiconducting counterparts and find practical applications ranging from noninvasive testing of CMOS VLSI integrated circuits to ultrafast quantum communications and quantum cryptography.
|
|
|
|
Kitaygorsky, J., Komissarov, I., Jukna, A., Pan, D., Minaeva, O., Kaurova, N., et al. (2007). Dark counts in nanostructured nbn superconducting single-photon detectors and bridges. IEEE Trans. Appl. Supercond., 17(2), 275–278.
Abstract: We present our studies on dark counts, observed as transient voltage pulses, in current-biased NbN superconducting single-photon detectors (SSPDs), as well as in ultrathin (~4 nm), submicrometer-width (100 to 500 nm) NbN nanobridges. The duration of these spontaneous voltage pulses varied from 250 ps to 5 ns, depending on the device geometry, with the longest pulses observed in the large kinetic-inductance SSPD structures. Dark counts were measured while the devices were completely isolated (shielded by a metallic enclosure) from the outside world, in a temperature range between 1.5 and 6 K. Evidence shows that in our two-dimensional structures the dark counts are due to the depairing of vortex-antivortex pairs caused by the applied bias current. Our results shed some light on the vortex dynamics in 2D superconductors and, from the applied point of view, on intrinsic performance of nanostructured SSPDs.
|
|
|
|
Zolotov, P., Vakhtomin, Y., Divochiy, A., Seleznev, V., Morozov, P., & Smirnov, K. (2013). High-efficiency single-photon detectors based on NbN films.
Abstract: We present our resent results in development and testing of Superconducting Single-Photon Detectors (SSPD) with detection efficiencies greater than 85%. High values of obtained results are assigned to proposed design of the detector with integrated resonator structure, including two-layer optical cavity and anti-reflective coating (ARC).
|
|
|
|
Ryabchun, S. A., Tretyakov, I. V., Finkel, M. I., Maslennikov, S. N., Kaurova, N. S., Seleznev, V. A., et al. (2008). Fabrication and characterisation of NbN HEB mixers with in situ gold contacts. In Proc. 19th Int. Symp. Space Terahertz Technol. (pp. 62–67). Groningen, Netherlands.
Abstract: We present our recent results of the fabrication and testing of NbN hot-electron bolometer mixers with in situ gold contacts. An intermediate frequency bandwidth of about 6 GHz has been measured for the mixers made of a 3.5-nm NbN film on a plane Si substrate with in situ gold contacts, compared to 3.5 GHz for devices made of the same film with ex situ gold contacts. The increase in the intermediate frequency bandwidth is attributed to additional diffusion cooling through the improved contacts, which is further supported by the its dependence on the bridge length: intermediate frequency bandwidths of 3.5 GHz and 6 GHz have been measured for devices with lengths of 0.35 μm and 0.16 μm respectively at a local oscillator frequency of 300 GHz near the superconducting transition. At a local oscillator frequency of 2.5 THz the receiver has offered a DSB noise temperature of 950 K. When compared to the previous result of 1300 K obtained at the same local oscillator frequency for devices fabricated with an ex situ route, such a low value of the noise temperature may also be attributed to the improved gold contacts.
|
|