Verevkin, A. A., Zhang, J., Slysz, W., Sobolewski, R., Lipatov, A. P., Okunev, O., et al. (2002). Superconducting single-photon detectors for GHz-rate free-space quantum communications. In J. C. Ricklin, & D. G. Voelz (Eds.), Proc. SPIE (Vol. 4821, pp. 447–454). SPIE.
Abstract: We report our studies on the performance of new NbN ultrathin-film superconducting single-photon detectors (SSPDs). Our SSPDs exhibit experimentally measured quantum efficiencies from 5% at wavelength λ = 1550 nm up to 10% at λ = 405 nm, with exponential, activation-energy-type spectral sensitivity dependence in the 0.4-μm – 3-μm wavelength range. Using a variable optical delay setup, we have shown that our NbN SSPDs can resolve optical photons with a counting rate up to 10 GHz, presently limited by the read-out electronics. The measured device jitter was below 35 ps under optimum biasing conditions. The extremely high photon counting rate, together with relatively high (especially for λ > 1 μm) quantum efficiency, low jitter, and very low dark counts, make NbN SSPDs very promising for free-space communications and quantum cryptography.
|
|
|
Il'in, K. S., Currie, M., Lindgren, M., Milostnaya, I. I., Verevkin, A. A., Gol'tsman, G. N., et al. (1999). Quantum efficiency and time-domain response of superconducting NbN hot-electron photodetectors. IEEE Trans. Appl. Supercond., 9(2), 3338–3341.
Abstract: We report our studies on the response of ultrathin superconducting NbN hot-electron photodetectors. We have measured the photoresponse of few-nm-thick, micron-size structures, which consisted of single and multiple microbridges, to radiation from the continuous-wave semiconductor laser and the femtosecond Ti:sapphire laser with the wavelength of 790 nm and 400 nm, respectively. The maximum responsivity was observed near the film's superconducting transition with the device optimally current-biased in the resistive state. The responsivity of the detector, normalized to its illuminated area and the coupling factor, was 220 A/W(3/spl times/10/sup 4/ V/W), which corresponded to a quantum efficiency of 340. The responsivity was wavelength independent from the far infrared to the ultraviolet range, and was at least two orders of magnitude higher than comparable semiconductor optical detectors. The time constant of the photoresponse signal was 45 ps, when was measured at 2.15 K in the resistive (switched) state using a cryogenic electro-optical sampling technique with subpicosecond resolution. The obtained results agree very well with our calculations performed using a two-temperature model of the electron heating in thin superconducting films.
|
|
|
Sobolewski, R., Xu, Y., Zheng, X., Williams, C., Zhang, J., Verevkin, A., et al. (2002). Spectral sensitivity of the NbN single-photon superconducting detector. IEICE Trans. Electron., E85-C(3), 797–802.
Abstract: We report our studies on the spectral sensitivity of superconducting NbN thin-film single-photon detectors (SPD's) capable of GHz counting rates of visible and near-infrared photons. In particular, it has been shown that a NbN SPD is sensitive to 1.55-µm wavelength radiation and can be used for quantum communication. Our SPD's exhibit experimentally measured intrinsic quantum efficiencies from 20% at 800 nm up to 1% at 1.55-µm wavelength. The devices demonstrate picosecond response time (<100 ps, limited by our readout system) and negligibly low dark counts. Spectral dependencies of photon counting of continuous-wave, 0.4-µm to 3.5-µm radiation, and 0.63-µm, 1.33-µm, and 1.55-µm laser-pulsed radiations are presented for the single-stripe-type and meander-type devices.
|
|
|
Zhang, J., Slysz, W., Verevkin, A., Okunev, O., Chulkova, G., Korneev, A., et al. (2003). Response time characterization of NbN superconducting single-photon detectors. IEEE Trans. Appl. Supercond., 13(2), 180–183.
Abstract: We report our time-resolved measurements of NbN-based superconducting single-photon detectors. The structures are meander-type, 10-nm thick, and 200-nm wide stripes and were operated at 4.2 K. We have shown that the NbN devices can count single-photon pulses with below 100-ps time resolution. The response signal pulse width was about 150 ps, and the system jitter was measured to be 35 ps.
|
|
|
Zolotov, P. I., Divochiy, A. V., Vakhtomin, Y. B., Lubenchenko, A. V., Morozov, P. V., Shurkaeva, I. V., et al. (2018). Influence of sputtering parameters on the main characteristics of ultra-thin vanadium nitride films. In J. Phys.: Conf. Ser. (Vol. 1124, 051030).
Abstract: We researched the relation between deposition and ultra-thin VN films parameters. To conduct the experimental study we varied substrate temperature, Ar and N2 partial pressures and deposition rate. The study allowed us to obtain the films with close to the bulk values transition temperatures and implement such samples in order to fabricate superconducting single-photon detectors.
|
|