Verevkin, A. I., Ptitsina, N. G., Chulkova, G. M., Gol'tsman, G. N., Gershenzon, E. M., & Yngvesson, K. S. (1995). Electron energy relaxation in a 2D channel in AlGaAs-GaAs heterostructures under quasiequilibrium conditions at low temperatures. JETP Lett., 61(7), 591–595.
Abstract: The energy relaxation time of 2D electrons, Te, has been measured under quasiequilibrium conditions in AlGaAs—GaAs heterojunctions over the temperature range T= 1.5—20 K. At T> 4 K, Te depends only weakly on the temperature, while at T< 4 K 7;'(T) there is a dependence fr; lNT. A linear dependence 7: 1 (T) in the Bloch—-Grfineisen temperature region (T< 5 K) is unambiguous evidence that a piezoacoustic mechanism of an electron—phonon interaction is predominant in the inelastic scattering of electrons. The values of T6 in this temperature range agree very accurately with theoretical results reported by Karpus [Sov. Phys. Semicond. 22 (1988)]. At higher temperatures, where scat—tering by deformation acoustic phonons becomes substantial, there is a significant discrepancy between the experimental and theoretical re-sults.
|
Emelianov, A. V., Nekrasov, N. P., Moskotin, M. V., Fedorov, G. E., Otero, N., Romero, P. M., et al. (2021). Individual SWCNT transistor with photosensitive planar junction induced by two‐photon oxidation. Adv. Electron. Mater., 7(3), 2000872.
Abstract: The fabrication of planar junctions in carbon nanomaterials is a promising way to increase the optical sensitivity of optoelectronic nanometer-scale devices in photonic connections, sensors, and photovoltaics. Utilizing a unique lithography approach based on direct femtosecond laser processing, a fast and easy technique for modification of single-walled carbon nanotube (SWCNT) optoelectronic properties through localized two-photon oxidation is developed. It results in a novel approach of quasimetallic to semiconducting nanotube conversion so that metal/semiconductor planar junction is formed via local laser patterning. The fabricated planar junction in the field-effect transistors based on individual SWCNT drastically increases the photoresponse of such devices. The broadband photoresponsivity of the two-photon oxidized structures reaches the value of 2 × 107 A W−1 per single SWCNT at 1 V bias voltage. The SWCNT-based transistors with induced metal/semiconductor planar junction can be applied to detect extremely small light intensities with high spatial resolution in photovoltaics, integrated circuits, and telecommunication applications.
|
Kovaluyk, V., Lazarenko, P., Kozyukhin, S., An, P., Prokhodtsov, A., Goltsman, G., et al. (2019). Influence of the phase state of Ge2Sb2Te5 thin cover on the parameters of the optical waveguide structures. In Proc. Amorphous and Nanostructured Chalcogenides (pp. 47–48). Technical University of Moldova.
Abstract: The fast switching time of Ge-Sb-Te thin films between amorphous and crystalline states initiated by laser beam as well as significant change of their optical properties and the preservation of metastable states for tens of years open wide perspectives for the application of these materials to fully optical devices [1], including high-speed optical memory [2]. Here we study optical properties of the Ge2Sb2Te5 (GST225) thin films integrated with on-chip silicon nitride O-ring resonator. The rib waveguide of the resonator was formed the first stage of e-beam lithography and subsequent reactive-ion etching. We used the second stage of e-beam lithography combining with lift-off method for the formation of GST225 active region on the resonator ring surface. The amorphous GST225 thin films were prepared by magnetron sputtering, and were capped by thin silicon oxide on their tops. The length of the GST225 active region varied from 0.1 to 20 μ m. Crystallization of amorphous thin films was carried out at the temperature of 400 °C for 30 minutes. Auger electron spectroscopy and transmission electron microscopy were used for studying composition and structure of investigated GST225thin films, respectively. It was observed that crystallization of amorphous GST225 film lead to a decrease of the optical power, transmitted through the waveguide. Comparison of the optical transmittance of O-ring resonators before and after the GST225 deposition allowed to identify the change in the Q-factor and the wavelength peak shift. This can be explained by the differences of the complex refractive indexes of GST225 thin films in the amorphous and crystalline states. From the measurement data, the GST225 effective refractive index was extracted depending on the ring waveguide width of the resonator for a telecommunication wavelength of 1550 nm.
|
Ovchinnikov, O. V., Perepelitsa, A. S., Smirnov, M. S., Latyshev, A. N., Grevtseva, I. G., Vasiliev, R. B., et al. (2020). Luminescence of colloidal Ag2S/ZnS core/shell quantum dots capped with thioglycolic acid. J. Luminescence, 220, 117008 (1 to 7).
Abstract: The features of IR luminescence of colloidal AgS QDs passivated with thioglycolic acid (AgS/TGA) under the formation of AgS/ZnS/TGA core/shell QDs are considered. A 4.5-fold increase in the quantum yield of recombination IR luminescence within the band with a peak at 960 nm (1.29 eV), full width at half maximum of 250 nm (0.34 eV), and the Stokes shift with respect to the exciton absorption of 0.6 eV was found. The increase in the IR luminescence intensity of AgS/ZnS/TGA QDs is accompanied by an increase in the average luminescence lifetime from 2.9 ns to 14.3 ns, which is explained as “healing” of surface trap states during the formation of the ZnS shell. For the first time, the enhancement of the luminescence intensity photodegradation (hereinafter referred to as fatigue) was found during the formation of the AgS/ZnS/TGA core/shell QDs. The luminescence fatigue is irreversible. We conclude that the initial stage of photolysis of the AgS core QDs under laser irradiation plays a key role. Low-atomic photolytic clusters of silver formed on the AgS core QDs act as luminescence quenching centers and do not reveal structural transformations into AgS, provided that the clusters are not in contact with TGA.
|
Gershenzon, E. M., Gershenson, M. E., Goltsman, G. N., Karasik, B. S., Lyulkin, A. M., & Semenov, A. D. (1989). Fast-response superconducting electron bolometer. Pisma v Zhurnal Tekhnicheskoi Fiziki, 15(3), 88–92.
Abstract: The general design, operation, and performance characteristics of fast-response electronic bolometers using a thin superconducting Nb film on a leucosapphire substrate are briefly reviewed. The volt-watt sensitivity of the bolometrs is 2,000-200,000 V/W, the operating temperature is 1.6 K, and the time constant is 4-4.5 ns.
|