Abstract: Mixers based on Josephson junctions from conventional superconductor materials have demonstrated excellent performance at subgap frequencies. The advantages of Josephson mixers are low optimal power of the local oscillator and large intermediate frequency bandwidth but their noise temperature increases dramatically at frequencies corresponding to the energy gap of the superconductor, which is typically below 1 THz for widely used materials. The large energy gap of oxide superconductors makes them promising candidates for development of terahertz Josephson mixers. Here we report on experimental study of the quasioptical mixer utilizing bicrystal Josephson junction from high-transition-temperature YBa 2 Cu 3 O 7-δ film. Junctions with a width of 2 µm were fabricated from 100 nm thick laser ablated films on bicrystal MgO substrates and had the and the J C R n product of about 2 mV at 4.2 K. The planar complementary logarithmic spiral antenna incorporated into co-planar waveguide was patterned from 200 nm thick gold film thermally evaporated in situ on top of the YBa 2 Cu 3 O 7-δ film. The mixer chip was clamped to the extended hemispherical silicon lens. Performance of the mixer was investigated at 4.5 K bath temperature. We used FIR laser as a local oscillator at frequencies 0.698 and 2.52 THz. System noise temperature (DSB) was determined from Y-factor measured with 300 K and 77 K loads. At 0.698 THz the lowest noise temperature 1750 K was observed when the mixer was biased with the fixed current to the region in the vicinity of either the first Shapiro step or the critical current. Between these two bias points the noise temperature increased to ≈ 20000 K. As function of the local oscillator power the noise temperature reached the minimum when the critical current was suppressed to the half of its equilibrium value. Power of the local oscillator absorbed by the mixer at optimal operation was of the order 100 nW. The present design of our antenna limits the upper operation frequency to the value of 1.8 THz. Nevertheless, we clearly observed Shapiro steps at the frequency 2.52 THz. Bearing in mind an improved design of the antenna, we estimate the 3000 K DSB noise temperature at this frequency.

Abstract: Mixing of 1.56 µm infrared radiation from two lasers in a high quality YBa₂Cu₃O_7-δ thin film, patterned to parallel strips, was demonstrated. A mixer bandwidth of 18 GHz, limited by the measurement system, was obtained. A model based on nonequilibrium electron heating gives a good fit to the data and predicts an intrinsic mixer bandwidth in excess of 100 GHz, operating in the whole infrared spectrum. Reduction of bolometric effects and ways to decrease the conversion loss of the mixer is discussed. The minimum conversion loss is expected to be ~10 dB.

Abstract: Nanophotonic circuitry and superconducting nanowires have been successfully combined for detecting single photons, propagating in an integrated photonic circuit, with high efficiency and low noise and timing uncertainty. Waveguide-integrated superconducting nanowire single-photon detectors (SNSPDs) can nowadays be engineered to achieve subnanosecond recovery times and can potentially be adopted for applications requiring Gcps count rates. However, particular attention shall be paid to such an extreme count rate regime since artifacts in the detector functionality emerge. In particular, a count-rate dependent detection efficiency has been encountered that can compromise the accuracy of quantum detector tomography experiments. Here, we investigate the response of waveguide-integrated SNSPDs at high photon flux and identify the presence of parasitic currents due to the accumulation of charge in the readout electronics to cause the above-mentioned artifact in the detection efficiency. Our approach allows us to determine the maximum photon count rate at which the detector can be operated without adverse effects. Our findings are particularly important to avoid artifacts when applying SNSPDs for quantum tomography.
We acknowledge support through ERC Consolidator Grant No. 724707 and from the Deutsche Forschungsgemeinschaft through Project No. PE 1832/5-1,2, as well as funding by the Volkswagen Foundation. This project has received funding from the European Union's Horizon 2020 research and innovation program under the Marie Skłodowska-Curie Grant Agreement No. 675745. V.K. and G.G. acknowledge support from the Russian Science Foundation Project No. 16-12-00045 (NbN film deposition and testing). A.V. acknowledges support from the Karlsruhe School of Optics and Photonics (KSOP).