Ozhegov, R. V., Smirnov, A. V., Vakhtomin, Y. B., Smirnov, K. V., Divochiy, A. V., & Goltsman, G. N. (2009). Ultrafast superconducting bolometer receivers for terahertz applications. In Proc. PIERS (867). 777 Concord Avenue, Suite 207 Cambridge, MA 02138: The Electromagnetics Academy.
Abstract: The research by the group of Moscow State Pedagogical University into the hot-electron phenomena in thin superconducting films has led to the development of new types of detectors and their use both in fundamental and applied studies. In this paper, we present the results of testing the terahertz HEB receiver systems based on ultrathin (∼ 4 nm) NbN and MoRe detectors with a response time of 50 ps and 1 ns, respectively. We have developed three types of devices which differ in the way a terahertz signal is coupled to the detector and cover the following ranges: 0.3–3 THz, 0.1–30 THz and 25–70 THz. In the case of the receiving system optimized for 0.3–3 THz, the sensitive element (a strip of asuperconductor with planar dimensions of 0.2μm (length) by 1.7μm (width)) was integrated witha planar broadband log-spiral antenna. For additional focusing ofthe incident radiation a silicon hyperhemispherical lens was used. For the 0.1–30 THz receivingsystem, the sensitive element was patterned as parallel strips(2μm wide each) filling an area of 500×500μm2with a filling factor of 0.5. In the receivingsystem of this type we used direct coupling of the incident radiation to the sensitive element. Inthe 25–70 THz range (detector type 2/2a in Table 1) we used a square-shaped superconductingdetector with planar dimensions of 10×10μm2. Incident radiation was coupled to the detectorwith the use of a germanium hyperhemispherical lens.The response time of the above receiving systems is determined by the cooling rate of the hotelectrons in the film. That depends on the electron-phonon interaction time, which is less forultrathin NbN than in MoRe.
|
|
|
Smirnov, K. V., Vakhtomin, Y. B., Divochiy, A. V., Ozhegov, R. V., Pentin, I. V., Slivinskaya, E. V., et al. (2009). Single-photon detectors for the visible and infrared parts of the spectrum based on NbN nanostructures. In Proc. Progress In Electromagnetics Research Symp. (pp. 863–864). Moscow, Russia.
Abstract: The research by the group of Moscow State Pedagogical University into the hot-electron phenomena in thin superconducting films has led to the development of new types ofdetectors [1, 2] and their use both in fundamental and applied studies [3–6]. In this paper, wepresent the results of the development and fabrication of receiving systems for the visible andinfrared parts of the spectrum optimised for use in telecommunication systems and quantumcryptography.
|
|
|
Romanov, N. R., Zolotov, P. I., Vakhtomin, Y. B., Divochiy, A. V., & Smirnov, K. V. (2018). Electron diffusivity measurements of VN superconducting single-photon detectors. In J. Phys.: Conf. Ser. (Vol. 1124, 051032).
Abstract: The research of ultrathin vanadium nitride (VN) films as a promising candidate for superconducting single-photon detectors (SSPD) is presented. The electron diffusivity measurements are performed for such devices. Devices that were fabricated out from 9.9 nm films had diffusivity coefficient of 0.41 cm2/s and from 5.4 nm – 0.54 cm2/s. Obtained values are similar to other typical SSPD materials. The diffusivity that increases along with decreasing of the film thickness is expected to allow fabrication of the devices with improved characteristics. Fabricated VN SSPDs showed prominent single-photon response in the range 0.9-1.55 µm.
|
|
|
Zolotov, P. I., Vakhtomin, Y. B., Divochiy, A. V., Seleznev, V. A., & Smirnov, K. V. (2016). Technology development of resonator-based structures for efficiency increasing of NBN detectors of IR single photons. Proc. 5th Int. Conf. Photonics and Information Optics, , 115–116.
Abstract: This paper presents a technology of fabrication of NbN superconductive single- photon detectors, using resonator structures. The main results are related to optimization of the process of NbN sputtering over substrate with metallic mirrors and SiO 2 /Si 3 N 4 layers /4 thick. Investigation of the quantum efficiency of fabricated devices at 1.6 K on 1.55 μm showed triple-magnified value compared to standard Si/NbN structures.
|
|
|
Korneeva, Y. P., Mikhailov, M. Y., Pershin, Y. P., Manova, N. N., Divochiy, A. V., Vakhtomin, Y. B., et al. (2014). Superconducting single-photon detector made of MoSi film. Supercond. Sci. Technol., 27(9), 095012.
Abstract: We fabricated and characterized nanowire superconducting single-photon detectors made of 4 nm thick amorphous Mox Si1−x films. At 1.7 K the best devices exhibit a detection efficiency (DE) up to 18% at 1.2 $\mu {\rm m}$ wavelength of unpolarized light, a characteristic response time of about 6 ns and timing jitter of 120 ps. The DE was studied in wavelength range from 650 nm to 2500 nm. At wavelengths below 1200 nm these detectors reach their maximum DE limited by photon absorption in the thin MoSi film.
|
|