Abstract: We report time-resolved characterization of superconducting NbN hot-electron photodetectors using an electro-optic sampling method. Our samples were patterned into micron-size microbridges from 3.5-nm-thick NbN films deposited on sapphire substrates. The devices were illuminated with 100 fs optical pulses, and the photoresponse was measured in the ambient temperature range between 2.15 and 10.6 K (superconducting temperature transition TC). The experimental data agreed very well with the nonequilibrium hot-electron, two-temperature model. The quasiparticle thermalization time was ambient temperature independent and was measured to be 6.5 ps. The inelastic electron–phonon scattering time Ï„e–ph tended to decrease with the temperature increase, although its change remained within the experimental error, while the phonon escape time Ï„es decreased almost by a factor of two when the sample was put in direct contact with superfluid helium. Specifically, Ï„e–ph and Ï„es, fitted by the two-temperature model, were equal to 11.6 and 21 ps at 2.15 K, and 10(±2) and 38 ps at 10.5 K, respectively. The obtained value of Ï„e–ph shows that the maximum intermediate frequency bandwidth of NbN hot-electron phonon-cooled mixers operating at TC can reach 16(+4/–3) GHz if one eliminates the bolometric phonon-heating effect.

Abstract: Thin film NbN (<40 A) strips are used as waveguide mixer elements. The electron cooling mechanism for the geometry is the electron-phonon interaction. We report a receiver noise temperature of 750 K at 244 GHz, with / IF = 1.5 GHz, Af= 500 MHz, and Tphysical = 4 K. The instantaneous bandwidth for this mixer is 1.6 GHz. The local oscillator (LO) power is 0.5 1.tW with 3 dB-uncertainty. The mixer is linear to 1 dB up to an input power level 6 dB below the LO power. We report the first detection of a molecular line emission using this class of mixer, and that the receiver noise temperature determined from Y-factor measurements reflects the true heterodyne sensitivity.

Abstract: Bolometdcmucers based on Nb and NbN superconducting thin films in the resistive state have been prepared for 20, 100 GHz and 350-500 GHz operation. The mixing mechanism is presumably of electron heating origin. Our measurements indicate that a conversion loss of about 6-8 dB can rather easily be achieved, and that the noise is reasonably low. The requirements on the operation mode and on the film parameters in order to obtain small conversion losses or even gain are discussed. For NbN films the availability of nearly 1 GHz IF bandwidth is experimentally demonstrated. NbN hot-electron mucers combined with slot-line tapered antenna on Si membrane or with double-dipole antenna on SiO^ substrate have been fabricated. The devices we study are considered to be very promising for use in heterodyne receivers from microwaves to terahertz frequencies.

Abstract: The effect of heating of electrons relative to phonons is observed and investigated in a superconducting film that is made resistive by current and by an external magnetic field. The effect is manifested by an increase of the film resistance under the influence of the electromagnetic radiation, and is not selective in the frequency band 10^10-10^15 Hz. The independence of the effect of frequency under conditions of strong scattering by static defects is attributed to the decisive role of electron-electron collisions in the distribution function. The experimentally obtained characteristic time of resistance variation near the superconducting transition corresponds to the relaxation time of the order parameter, while at lower temperatures and fields it corresponds to the time of the inelastic electron-phonon interaction.

Abstract: A comprehensive investigation was made of the submillimeter photoconductivity of n -1nSb in the range of wavelengths L = 0.6-8 mm, magnetic fields H = 0-30 kOe, electric fields E = 0.01-0.5 V/cm, and temperatures T = 1.3-30 K. The kinetics of the photoconductivity processes as a function of T, E; and H is investigated. It is shown that impurity photoconductivity does exist for any degree of compensation of extremely purified n-InSb. Particular attention is paid to the hopping photoconductivity realized in strongly compensated n-1nSb (K > 0.8).

Abstract: The temperature dependence of the resistivity of Nb thin films has been studied at T=4.2-300 K. It has been shown that quantum interference between electron-phonon and electron-impurity scattering determines the temperature dependence of the resistivity of the films investigated over a broad temperature range. The magnitude of the contribution of the electron-phonon-impurity,interference is described satisfactorily by the theory developed by Reizer and Sergeev {Zh. Eksp. Teor. Fiz. 92,2291 (1987) [Sov. Phys. JETP 65, 1291 (1987)l). The interaction constants of electrons with longitudinal and transverse phonons in Nb films have been determined for the first time by comparing the experimental data with the theory. The values of the constants obtained are consistent with the data on the inelastic electron-phonon scattering times in the films investigated. The contribution of the transverse phonons is dominant both in the interference correction to the resistivity and in the electron energy relaxation.

Abstract: A new microwave technique was successfully applied for direct studies of energy relaxation times in two-dimensional AlGaAs/GaAs structures under quasi-equilibrium conditions in the nanosecond and picosecond time scale. We report our results of energy relaxation time measurements in the temperature range 1.6-50 K, in quantum Hall effect regime in magnetic fields up to 4 T.