Ryabchun, S. A., Tretyakov, I. V., Finkel, M. I., Maslennikov, S. N., Kaurova, N. S., Seleznev, V. A., et al. (2008). Fabrication and characterisation of NbN HEB mixers with in situ gold contacts. In Proc. 19th Int. Symp. Space Terahertz Technol. (pp. 62–67). Groningen, Netherlands.
Abstract: We present our recent results of the fabrication and testing of NbN hot-electron bolometer mixers with in situ gold contacts. An intermediate frequency bandwidth of about 6 GHz has been measured for the mixers made of a 3.5-nm NbN film on a plane Si substrate with in situ gold contacts, compared to 3.5 GHz for devices made of the same film with ex situ gold contacts. The increase in the intermediate frequency bandwidth is attributed to additional diffusion cooling through the improved contacts, which is further supported by the its dependence on the bridge length: intermediate frequency bandwidths of 3.5 GHz and 6 GHz have been measured for devices with lengths of 0.35 μm and 0.16 μm respectively at a local oscillator frequency of 300 GHz near the superconducting transition. At a local oscillator frequency of 2.5 THz the receiver has offered a DSB noise temperature of 950 K. When compared to the previous result of 1300 K obtained at the same local oscillator frequency for devices fabricated with an ex situ route, such a low value of the noise temperature may also be attributed to the improved gold contacts.
|
|
|
Kawamura, J., Blundell, R., Tong, C. - Y. E., Papa, D. C., Hunter, T. R., Paine, St. N., et al. (2000). Superconductive hot-electron bolometer mixer receiver for 800 GHz operation (Vol. 48).
|
|
|
Smirnov, A. V., Larionov, P. A., Finkel, M. I., Maslennikov, S. N., Voronov, B. M., & Gol'tsman, G. N. (2008). NbZr films for THz phonon-cooled HEB mixers. In Proc. 19th Int. Symp. Space Terahertz Technol. (pp. 44–47). Groningen, Netherlands.
|
|
|
Baselmans, J., Kooi, J., Baryshev, A., Yang, Z. Q., Hajenius, M., Gao, J. R., et al. (2005). Full characterization of small volume NbN HEB mixers for space applications. In Proc. 16th Int. Symp. Space Terahertz Technol. (pp. 457–462). Göteborg, Sweden.
Abstract: NbN phonon cooled HEB’s are one of the most promising bolometer mixer technologies for (near) future (space) applications. Their performance is usually quantified by mea- suring the receiver noise temperature at a given IF frequency, usually around 1 – 2 GHz. However, for any real applications it is vital that one fully knows all the relevant properties of the mixer, including LO power, stability, direct detection, gain bandwidth and noise bandwidth, not only the noise temperature at low IF frequencies. To this aim we have measured all these parameters at the optimal operating point of one single, small volume quasioptical NbN HEB mixer. We find a minimum noise temperature of 900 K at 1.46 THz. We observe a direct detection effect indicated by a change in bias current when changing from a 300 K hot load to a 77 K cold load. Due to this effect we overestimate the noise temperature by about 22% using a 300 K hot load and a 77 K cold load. The LO power needed to reach the optimal operating point is 80 nW at the receiver lens front, 59 nW inside the NbN bridge. However, using the isothermal technique we find a power absorbed in the NbN bridge of 25 nW, a difference of about a factor 2. We obtain a gain bandwidth of 2.3 GHz and a noise bandwidth of 4 GHz. The system Allan time is about 1 sec. in a 50 MHz spectral bandwidth and a deviation from white noise integration (governed by the radiometer equation) occurs at 0.2 sec., which implies a maximum integration time of a few seconds in a 1 MHz bandwidth spectrometer.
|
|
|
Finkel, M. I., Maslennikov, S. N., Vachtomin, Y. B., Svechnikov, S. I., Smirnov, K. V., Seleznev, V. A., et al. (2005). Hot electron bolometer mixer for 20 – 40 THz frequency range. In Proc. 16th Int. Symp. Space Terahertz Technol. (pp. 393–397). Göteborg, Sweden.
Abstract: The developed HEB mixer was based on a 5 nm thick NbN film deposited on a GaAs substrate. The active area of the film was patterned as a 30×20 μm 2 strip and coupled with a 50 Ohm coplanar line deposited in situ. An extended hemispherical germanium lens was used to focus the LO radiation on the mixer. The responsivity of the mixer was measured in a direct detection mode in the 25÷64 THz frequency range. The noise performance of the mixer and the directivity of the receiver were investigated in a heterodyne mode. A 10.6 μm wavelength CW CO 2 laser was utilized as a local oscillator.
|
|
|
Gol'tsman, G. N., Vachtomin, Y. B., Antipov, S. V., Finkel, M. I., Maslennikov, S. N., Smirnov, K. V., et al. (2005). NbN phonon-cooled hot-electron bolometer mixer for terahertz heterodyne receivers. In Proc. SPIE (Vol. 5727, pp. 95–106).
Abstract: We present the results of our studies of NbN phonon-cooled HEB mixers at terahertz frequencies. The mixers were fabricated from NbN film deposited on a high-resistivity Si substrate with an MgO buffer layer. The mixer element was integrated with a log-periodic spiral antenna. The noise temperature measurements were performed at 2.5 THz and at 3.8 THz local oscillator frequencies for the 3 x 0.2 μm2 active area devices. The best uncorrected receiver noise temperatures found for these frequencies are 1300 K and 3100 K, respectively. A water vapour discharge laser was used as the LO source. The largest gain bandwidth of 5.2 GHz was achieved for a mixer based on 2 nm thick NbN film deposited on MgO layer over Si substrate. The gain bandwidth of the mixer based on 3.5 nm NbN film deposited on Si with MgO is 4.2 GHz and the noise bandwidth for the same device amounts to 5 GHz. We also present the results of our research into decrease of the direct detection contribution to the measured Y-factor and a possible error of noise temperature calculation. The use of a square nickel cell mesh as an IR-filter enabled us to avoid the effect of direct detection and measure apparent value of the noise temperature which was 16% less than that obtained using conventional black polyethylene IR-filter.
|
|
|
Maslennikov, S. N., Finkel, M. I., Antipov, S. V., Polyakov, S. L., Zhang, W., Ozhegov, R., et al. (2006). Spiral antenna coupled and directly coupled NbN HEB mixers in the frequency range from 1 to 70 THz. In Proc. 17th Int. Symp. Space Terahertz Technol. (pp. 177–179). Paris, France.
Abstract: We investigate both antenna coupled and directly coupled HEB mixers at several LO frequencies within the range of 2.5 THz to 70 THz. H20 (2.5+10.7 THz), and CO2 (30 THz) gas discharge lasers are used as the local oscillators. The noise temperature of antenna coupled mixers is measured at LO frequencies of 2.5 THz, 3.8 THz, and 30 THz. The results for both antenna coupled and directly coupled mixer types are compared. The devices with in—plane dimensions of 5x5 ,um 2 are pumped by LO radiation at 10.7 THz. The directly coupled HEB demonstrates nearly flat dependence of responsivity on frequency in the range of 25+64 THz.
|
|
|
Gol'tsman, G., Korneev, A., Minaeva, O., Antipov, A., Divochiy, A., Kaurova, N., et al. (2006). Middle-infrared to visible-light ultrafast superconducting single-photon detector. In Proc. ASC. Seattle.
|
|
|
Smirnov, K., Korneev, A., Minaeva, O., Divochiy, A., Tarkhov, M., Ryabchun, S., et al. (2007). Ultrathin NbN film superconducting single-photon detector array. In J. Phys.: Conf. Ser. (Vol. 61, pp. 1081–1085).
Abstract: We report on the fabrication process of the 2 × 2 superconducting single-photon detector (SSPD) array. The SSPD array is made from ultrathin NbN film and is operated at liquid helium temperatures. Each detector is a nanowire-based structure patterned by electron beam lithography process. The advances in fabrication technology allowed us to produce highly uniform strips and preserve superconducting properties of the unpatterned film. SSPD exhibit up to 30% quantum efficiency in near infrared and up to 1% at 5-μm wavelength. Due to 120 MHz counting rate and 18 ps jitter, the time-domain multiplexing read-out is proposed for large scale SSPD arrays. Single-pixel SSPD has already found a practical application in non-invasive testing of semiconductor very-large scale integrated circuits. The SSPD significantly outperformed traditional single-photon counting avalanche diodes.
|
|
|