Shurakov, A., Tong, C. -yu E., Blundell, R., & Gol’tsman, G. (2014). A microwave pumped HEB direct detector using a homodyne readout scheme. In Proc. 25th Int. Symp. Space Terahertz Technol. (129).
Abstract: We report the results of our study on the noise performance of a fast THz detector based on the repurpose of hot electron bolometer mixer (HEB). Instead of operating with an elevated bath temperature, microwave power is injected into the HEB device, which enhances the sensitivity of the detector and at the same time provide a mechanism for reading out impedance changes of the device induced by the modulated incident THz radiation [1]. We have demonstrated an improvement of the detector’s optical noise equivalent power (NEP). Furthermore, by introducing a homodyne readout scheme based on a room temperature microwave mixer, the dynamic range of the detector is increased. The HEB devices used in this work were made of 4 nm thick NbN film. The detector chips were installed into a waveguide mixer block fitted with a corrugated horn, mounted on the cold plate of a liquid helium cryostat. The HEBs were operated at a bath temperature of 4.2 K. The signal beam was terminated on black bodies at ambient and liquid nitrogen temperatures. A chopper wheel placed in front of the cryostat window operating at a frequency of 1.48 kHz modulated the input load temperature of the detector. A cold mesh filter, centered at 830 GHz, was used to define the input signal power bandwidth. Microwave was injected through a broadband directional coupler inside the cryostat. Our experiments were mostly conducted at a pump frequency of 1.5 GHz. The reflected microwave power from the HEB device was fed into a cryogenic low noise amplifier (LNA). The output of the LNA was connected to the RF input port of a room temperature microwave mixer, which beat the reflected signal from the HEB using a copy of the original 1.5 GHz injection signal in a homodyne demodulation scheme. The amplitude of the detected power was measured by a lock-in amplifier, which was synchronized to the chopper frequency. Preliminary results yield an optical NEP of ~1 pW/ Hz 1/2 which corresponds to an improvement of a factor of 3 compared to [1], driven mainly by a lowering of the system noise floor. The dynamic range was also increased by similar amount. References 1. A. Shurakov et al. “A Microwave Pumped Hot Electron Bolometric Direct Detector,” submitted on Oct 18, 2013 to Appl. Phys. Let.
|
|
|
|
Zhang, W., Miao, W., Li, S. L., Zhou, K. M., Shi, S. C., Gao, J. R., et al. (2013). Measurement of the spectral response of spiral-antenna coupled superconducting hot electron bolometers. IEEE Trans. Appl. Supercond., 23(3), 2300804.
Abstract: Measured spectral response of spiral-antenna coupled superconducting hot electron bolometers (HEBs) often drops dramatically at frequencies that are still within the frequency range of interest (e.g., ~ 5 THz). This is inconsistent with the implied low receiver noise temperatures from the same measurements. To understand this discrepancy, we exhaustively test and calibrate the thermal sources used in Fourier transform spectrometer measurements. We first investigate the absolute emission spectrum of high-pressure Hg arc lamp, then measure the spectral response of two spiral-antenna coupled NbN HEBs with a Martin-Puplett interferometer as spectrometer and 77 K blackbody as broadband signal source. The measured absolute emission spectrum of Hg arc lamp is proportional to frequency, corresponding to an equivalent blackbody temperature of 4000 K at 1 THz, 1500 K at 3 THz, and 800 K at 5 THz, respectively. Measured spectral response of spiral-antenna coupled NbN HEBs, corrected for air absorption, is nearly flat in the frequency range of 0.5-4 THz, consistent with simulated coupling efficiency between HEB and spiral-antenna. These results explain the discrepancy, and prove that spiral-antenna coupled superconducting NbN HEBs work well in a wide frequency range. In addition, this calibration method and these results are broadly applicable to other quasi-optical THz receivers.
|
|
|
|
Danerud, M., Winkler, D., Lindgren, M., Zorin, M., Trifonov, V., Karasik, B. S., et al. (1994). Nonequilibrium and bolometric photoresponse in patterned YBa2Cu3O7−δ thin films. J. Appl. Phys., 76(3), 1902–1909.
Abstract: Epitaxial laser deposited YBa2Cu3O7−δ films of ∼50 nm thickness were patterned into detectors consisting of ten parallel 1 μm wide strips in order to study nonequilibrium and bolometric effects. Typically, the patterned samples had critical temperatures around 86 K, transition widths around 2 K and critical current densities above 1×106A/cm2 at 77 K. Pulsed laser measurements at 0.8 μm wavelength (17 ps full width at half maximum) showed a ∼30 ps response, attributed to electron heating, followed by a slower bolometric decay. Amplitude modulation in the band fmod=100 kHz–10 GHz of a laser with wavelength λ=0.8 μm showed two different thermal relaxations in the photoresponse. Phonon escape from the film (∼3 ns) is the limiting process, followed by heat diffusion in the substrate. Similar relaxations were also seen for λ=10.6 μm. The photoresponse measurements were made with the film in the resistive state and extended into the normal state. These states were created by supercritical bias currents. Measurements between 75 and 95 K (i.e., from below to above Tc) showed that the photoresponse was proportional to dR/dT for fmod=1 MHz and 4 GHz. The fast response is limited by the electron‐phonon scattering time, estimated to 1.8 ps from experimental data. The responsivity both at 0.8 and 10.6 μm wavelength was ∼1.2 V/W at fmod=1 GHz and the noise equivalent power was calculated to 1.5×10−9 WHz−1/2 for the fast response.
|
|
|
|
Danerud, M., Winkler, D., Zorin, M., Trifonov, V., Karasik, B., Gershenzon, E. M., et al. (1993). Picosecond detection of infrared radiation with YBa2Cu3O7-δ thin films. In J. R. Birch, & T. J. Parker (Eds.), Proc. SPIE (Vol. 2104, pp. 183–184). Spie.
Abstract: Picosecond nonequilibrium and slow bolometric responses from a patterned high-Tc superconducting (HTS) film due toinfrared radiation were investigated using both modulation and pulse techniques. Measurements at A, = 0.85 [tm andA, = 10.6 lim have shown a similar behaviour of the response vs modulation frequency f. The responsivity of the HTS filmbased detector at f ..- 0.6-1 GHz is estimated to be 10-2 – 10-1 V/W.
|
|
|
|
Semenov, A. D., Goghidze, I. G., Gol’tsman, G. N., Sergeev, A. V., Aksaev, E. E., & Gershenzon, E. M. (1993). Non-equilibrium quasiparticle response to radiation and bolometric effect in YBaCuO films. IEEE Trans. Appl. Supercond., 3(1), 2132–2135.
Abstract: The voltage photoresponse of structured current biased YBCO films on different substrates to 20-ps laser pulses of 0.63- mu m and 1.54- mu m wavelengths and to continuously modulated radiation of 2-mm wavelength is measured to temperatures around Tc. Fast picosecond decay of the response to pulsed radiation is followed by slow exponential relaxation with a nanosecond characteristic time depending on the substrate material and film dimensions. The slow component does not depend on wavelength and is attributed to the bolometric effect, while the magnitude of the fast component associated with nonequilibrium response rises with wavelength. More than an order-of-magnitude increase of the nonequilibrium response is seen from near-infrared to millimeter-wave range. This dependence plausibly reflects the low efficiency of multiplication of photoexcited electrons in YBaCuO compared to conventional superconductors.
|
|
|
|
Voronov, B. M., Gershenzon, E. M., Gol'tsman, G. N., Gogidze, I. G., Gusev, Y. P., Zorin, M. A., et al. (1992). Picosecond range detector base on superconducting niobium nitride film sensitive to radiation in spectral range from millimeter waves up to visible light. Sverkhprovodimost': Fizika, Khimiya, Tekhnika, 5(5), 955–960.
Abstract: Fast-operating picosecond detector of electromagnetical radiation is developed on the basis of fine superconducting film of niobium nitride with high sensitivity within spectral range from millimetric waves up to visible light. Detector sensitive element represents structure covering narrow parallel strips with micron sizes included in the rupture of microstrip line. Detecting ability of the detector and time constant measured using amplitude-simulated radiation of reverse wave tubes and pulse radiation of picosecond gas and solid-body lasers, constitute D*≅1010 W-1·cm·Hz-1/2 and τ≤5 ps respectively, at 10 K temperature. The expected value of time constant of the detector at 10 K obtained via extrapolation of directly measured dependence that is, τ ∝ τ-1, constitutes 20 ps. Experimental data demonstrate that detection mechanism is linked with electron heating effect.
|
|
|
|
Gershenzon, E. M., Gol'tsman, G. N., Karasik, B. S., Lugovaya, G. Y., Serebryakova, N. A., & Chinkova, E. V. (1992). Infrared radiation detectors on the base of electron heating in resistive state films from traditional superconducing materials. Sverkhprovodimost': Fizika, Khimiya, Tekhnika, 5(6), 1129–1140.
Abstract: Characteristics of infrared radiation detectors based on electron heating in thin superconducting films transformed at T ≤ Tc to a resistive state by transport current and, if necessary, by magnetic field are investigated. A comparison is made of the characteristics of the detectors fabricated of different materials: aluminium, niobium, Mo0.5Re0.5. Some devices with different topology of the reception area are considered. Electron heating detectors are comparable by their sensitivity with superconducting bolometers, but differ in a high fast-response.
|
|
|
|
Gershenzon, E. M., Goltsman, G., Orlova, S., Ptitsina, N., & Gurvich, Y. (1971). Germanium hot-electron narrow-band detector. Sov. Radio Engineering And Electronic Physics, 16(8), 1346.
|
|