Zorin, M., Milostnaya, I., Gol'tsman, G. N., & Gershenzon, E. M. (1997). Fast NbN superconducting switch controlled by optical radiation. IEEE Trans. Appl. Supercond., 7(2), 3734–3737.
Abstract: The switching time and the optical control power of the NbN superconducting switch have been measured. The device is based on the ultrathin film 5-8 nm thick patterned as a structure of several narrow parallel strips (/spl sim/1 /spl mu/m wide) connected to wide current leads. The current-voltage characteristic of the switch at temperature 4.2 K demonstrated a hysteresis due to DC current self-heating. We studied the superconducting-to-resistive state transition induced by both optical and bias-current excitations. The optical pulse duration was /spl sim/20 ps and the rise time of the current step was determined to be less than 50 ps. The optical pulse was delivered to the switch by the semiconductor laser through an optical fiber. We found that the measured switching time is less than the duration of the optical excitation. The threshold optical power density does not exceed 3/spl middot/10/sup 3/ W/cm/sup 2/. The proposed device can be used in the fiber input of LTS rapid single flux quantum circuits.
|
Zorin, M., Lindgren, M., Danerud, M., Karasik, B., Winkler, D., Gol'tsman, G., et al. (1995). Nonequilibrium and bolometric responses of YBaCuO thin films to high-frequency modulated laser radiation. J. Supercond., 8(1), 11–15.
Abstract: Picosecond nonequilibrium and slow bolometric responses to infrared radiation from a patterned high-T c superconducting (HTS) film in resistive and normal states deposited onto LaAlO3, NdGaO3, and MgO substrates were investigated using both pulse and modulation techniques. The response time of 35 ps to a laser pulse of 17 ps FWHM has been observed. The intrinsic response time of the fast process is expected to be about a few picoseconds. The modulation technique, being free from the disadvantages of pulse methods (poor sensitivity, limited dynamic range), makes the detailed study of a number of relaxation processes possible. Besides the nonequilibrium response, two kinds of bolometric processes, namely phonon transport through the film-substrate interface and phonon thermal diffusion in a substrate, manifest themselves in certain frequency dependences.
|
Zorin, M., Gol'tsman, G. N., Karasik, B. S., Elantev, A. I., Gershenzon, E. M., Lindgren, M., et al. (1995). Optical mixing in thin YBa2Cu3O7-x films. IEEE Trans. Appl. Supercond., 5(2), 2431–2434.
Abstract: High quality, j/sub c/ (77 K)>10/sup 6/ A/cm/sup 2/, epitaxial YBa2Cu3O7-x films of 50 nm thickness were patterned into ten parallel 1 /spl mu/m wide strips. The film structure was coupled to a single-mode fiber. Mixer response was obtained at 0.78 /spl mu/m using laser frequency modulation and an optical delay line. Using two semiconductor lasers at 1.55 /spl mu/m wavelength the beating signal was used to measure the photoresponse up to 18 GHz. Nonequilibrium photoresponse in the resistive state of the superconductor was observed. Bolometric response dominates up to 3 GHz, after which the nonequilibrium response is constant up to the frequency limit of our registration system. Using an electron heating model the influence of different thermal processes on the conversion loss has been analyzed. Ways of increasing the sensitivity are also discussed.
|
Zhang, W., Li, N., Jiang, L., Miao, W., Lin, Z. - H., Yao, Q. - J., et al. (2007). Noise behaviour of a THz superconducting hot-electron bolometer mixer. Chinese Phys. Lett., 24(6), 1778–1781.
Abstract: A quasi-optical superconducting NbN hot-electron bolometer (HEB) mixer is measured in the frequency range of 0.5–2.5 THz for understanding of the frequency dependence of noise temperature of THz coherent detectors. It has been found that noise temperature increasing with frequency is mainly due to the coupling loss between the quasi-optical planar antenna and the superconducting HEB bridge when taking account of non-uniform distribution of high-frequency current. With the coupling loss corrected, the superconducting HEB mixer demonstrates a noise temperature nearly independent of frequency.
|
Zhang, W., Jiang, L., Lin, Z. H., Yao, Q. J., Li, J., Shi, S. C., et al. (2005). Development of a quasi-optical NbN superconducting HEB mixer. In Proc. 16th Int. Symp. Space Terahertz Technol. (pp. 209–213).
Abstract: In this paper, we report the performance of a quasi-optical NbN superconducting HEB (hot electron bolometer) mixer measured at 500 and 850GHz. The quasi-optical NbN superconducting HEB mixer is cryogenically cooled by a 4-K close-cycled refrigerator. Measured receiver noise temperature at 850 and 500GHz are 3000K and 2500K respectively with wire grid as beamsplitter, while the lowest receiver noise temperature is found to be approximately 1200K with Mylar film. The theoretical receiver noise temperature (taking into account the elliptical polarization of log-spiral antenna) is consistent with measured one. The receiver noise temperature and conversion gain with 15-μm Mylar film as the beamsplitter at 500GHz are thoroughly investigated for different LO pumping levels and dc biases. The stability of the mixer’s IF output power is also demonstrated.
|