Abstract: Superconducting single-photon detector (SSPD) is a planar nanostructure patterned from 4-nm-thick NbN film deposited on sapphire substrate. The sensitive element of the SSPD is 100-nm-wide NbN strip. The device is operated at liquid helium temperature. Absorption of a photon leads to a local suppression of superconductivity producing subnanosecond-long voltage pulse. In infrared (at 1550 nm and longer wavelengths) SSPD outperforms avalanche photodiodes in terms of detection efficiency (DE), dark counts rate, maximum counting rate and timing jitter. Efficient single-mode fibre coupling of the SSPD enabled its usage in many applications ranging from single-photon sources research to quantum cryptography. Recently we managed to improve the SSPD performance and measured 25% detection efficiency at 1550 nm wavelength and dark counts rate of 10 s-1. We also improved photon-number resolving SSPD (PNR-SSPD) which realizes a spatial multiplexing of incident photons enabling resolving of up to 4 simultaneously absorbed photons. Another improvement is the increase of the photon absorption using a λ/4 microcavity integrated with the SSPD. And finally in our strive to increase the DE at longer wavelengths we fabricated SSPD with the strip almost twice narrower compared to the standard 100 nm and demonstrated that in middle infrared (about 3 μm wavelength) these devices have DE several times higher compared to the traditional SSPDs.

Abstract: We demonstrate experimentally that single photon detection can be achieved in micron-wide NbN bridges, with widths ranging from 0.53 μm to 5.15 μm and for photon-wavelengths from 408 nm to 1550 nm. The microbridges are biased with a dc current close to the experimental critical current, which is estimated to be about 50 % of the theoretically expected depairing current. These results offer an alternative to the standard superconducting single-photon detectors (SSPDs), based on nanometer scale nanowires implemented in a long meandering structure. The results are consistent with improved theoretical modelling based on the theory of non-equilibrium superconductivity including the vortex-assisted mechanism of initial dissipation.

Abstract: The fast switching time of Ge-Sb-Te thin films between amorphous and crystalline states initiated by laser beam as well as significant change of their optical properties and the preservation of metastable states for tens of years open wide perspectives for the application of these materials to fully optical devices [1], including high-speed optical memory [2]. Here we study optical properties of the Ge2Sb2Te5 (GST225) thin films integrated with on-chip silicon nitride O-ring resonator. The rib waveguide of the resonator was formed the first stage of e-beam lithography and subsequent reactive-ion etching. We used the second stage of e-beam lithography combining with lift-off method for the formation of GST225 active region on the resonator ring surface. The amorphous GST225 thin films were prepared by magnetron sputtering, and were capped by thin silicon oxide on their tops. The length of the GST225 active region varied from 0.1 to 20 μ m. Crystallization of amorphous thin films was carried out at the temperature of 400 °C for 30 minutes. Auger electron spectroscopy and transmission electron microscopy were used for studying composition and structure of investigated GST225thin films, respectively. It was observed that crystallization of amorphous GST225 film lead to a decrease of the optical power, transmitted through the waveguide. Comparison of the optical transmittance of O-ring resonators before and after the GST225 deposition allowed to identify the change in the Q-factor and the wavelength peak shift. This can be explained by the differences of the complex refractive indexes of GST225 thin films in the amorphous and crystalline states. From the measurement data, the GST225 effective refractive index was extracted depending on the ring waveguide width of the resonator for a telecommunication wavelength of 1550 nm.

Abstract: By adopting a travelling-wave geometry approach, integrated superconductor- nanophotonic devices were fabricated. The architecture consists of a superconducting NbN- nanowire atop of a silicon nitride (Si 3 N 4 ) nanophotonic waveguide. NbN-nanowire was operated as a single-photon counting detector, with up to 92% on-chip detection efficiency (OCDE), in the coherent mode, serving as a highly sensitive IR heterodyne mixer with spectral resolution (f/df) greater than 10^6 in C-band at 1550 nm wavelength.

Abstract: In this paper, we present a reliable measurement method to study the influence of the GaN buffer layer on phonon-escape time in comparison with commonly used Si substrates and, in consequence, on the IF bandwidth of HEBs. One of the key aspects is to operate the HEB mixer at elevated bath temperatures close to the critical temperature of the NbN ultra-thin film, where contributions from electron-phonon processes and self-heating effects are relatively small, therefore IF roll-off will be governed by the phonon-escape.Two independent experiments were performed at GARD and MSPU on a similar experimental setup at frequencies of approximately 180 and 140 GHz, respectively, and have shown reproducible and consistent results. The entire IF chain was characterized by S-parameter measurements. We compared the measurement results of epitaxial NbN grown onto GaN buffer-layer with Tc of 12.5 K (4.5nm) with high quality polycrystalline NbN films on Si substrate with Tc of 10.5K (5nm) and observed a strong indication of an enhancement of phonon escape to the substrate by a factor of two for the NbN/GaN material combination.