Romanov, N. R., Zolotov, P. I., Vakhtomin, Y. B., Divochiy, A. V., & Smirnov, K. V. (2018). Electron diffusivity measurements of VN superconducting single-photon detectors. In J. Phys.: Conf. Ser. (Vol. 1124, 051032).
Abstract: The research of ultrathin vanadium nitride (VN) films as a promising candidate for superconducting single-photon detectors (SSPD) is presented. The electron diffusivity measurements are performed for such devices. Devices that were fabricated out from 9.9 nm films had diffusivity coefficient of 0.41 cm2/s and from 5.4 nm – 0.54 cm2/s. Obtained values are similar to other typical SSPD materials. The diffusivity that increases along with decreasing of the film thickness is expected to allow fabrication of the devices with improved characteristics. Fabricated VN SSPDs showed prominent single-photon response in the range 0.9-1.55 µm.
|
Rönnung, F., Cherednichenko, S., Winkler, D., & Gol'tsman, G. N. (1999). A nanoscale YBCO mixer optically coupled with a bow tie antenna. Supercond. Sci. Technol., 12(11), 853–855.
Abstract: The bolometric response of YBa2Cu3O7-δ(YBCO) hot-electron bolometers (HEBs) to near-infrared radiation was studied. Devices were fabricated from a 50 nm thick film and had in-plane areas of 10 × 10 µm2, 2 × 0.2 µm2, 1 × 0.2µm2 and 0.5 × 0.2 µm2. We found that nonequilibrium phonons cool down more effectively for the bolometers with smaller area. For the smallest bolometer the bolometric component in the response is 10 dB less than for the largest one.
|
Rosfjord, K. M., Yang, J. K. W., Dauler, E. A., Anant, V., Berggren, K. K., Kerman, A. J., et al. (2006). Increased detection efficiencies of nanowire single-photon detectors by integration of an optical cavity and anti-reflection coating. In CLEO/QELS (JTuF2 (1 to 2)).
Abstract: We fabricate and test superconducting NbN-nanowire single-photon detectors with an integrated optical cavity and anti-reflection coating. We design the cavity and coating such as to maximize absorption in the NbN film of the detector.
|
Rubtsova, I., Korneev, A., Matvienko, V., Chulkova, G., Milostnaya, I., Goltsman, G., et al. (2004). Spectral sensitivity, quantum efficiency, and noise equivalent power of NbN superconducting single-photon detectors in the IR range. In Proc. 29th IRMMW / 12th THz (pp. 461–462).
Abstract: We have developed nanostructured NbN superconducting single-photon detectors capable of GHz-rate photon counting in the 0.4 to 5 /spl mu/m wavelength range. Quantum efficiency of 30%, dark count rate 3/spl times/10/sup -4/ s/sup -1/, and NEP=10/sup -20/ W/Hz/sup -1/2/ have been measured at the 1.3-/spl mu/m wavelength for the device operating at 2.0 K.
|
Ryabchun, S., Korneev, A., Matvienko, V., Smirnov, K., Kouminov, P., Seleznev, V., et al. (2004). Superconducting single photon detectors array based on hot electron phenomena. In Proc. 15th Int. Symp. Space Terahertz Technol. (pp. 242–247).
Abstract: In this paper we propose to use time domain multiplexing for large format arrays of superconducting single photon detectors (SSPDs) of the terahertz, visible and infrared frequency ranges based on ultrathin superconducting NbN films. Effective realization of time domain multiplexing for SSPD arrays is possible due to a short electric pulse of the SSPD as response to radiation quantum absorption, picosecond jitter and extremely low noise equivalent power (NEP). We present experimental results of testing 2×2 arrays in the infrared waveband. The measured noise equivalent power in the infrared and expected for the terahertz waveband is 10 – 21 WHz -1/2 . The best quantum efficiency (QE) of SSPD is 50% at 1.3 µm wavelength.
|