Abstract: The fast switching time of Ge-Sb-Te thin films between amorphous and crystalline states initiated by laser beam as well as significant change of their optical properties and the preservation of metastable states for tens of years open wide perspectives for the application of these materials to fully optical devices [1], including high-speed optical memory [2]. Here we study optical properties of the Ge2Sb2Te5 (GST225) thin films integrated with on-chip silicon nitride O-ring resonator. The rib waveguide of the resonator was formed the first stage of e-beam lithography and subsequent reactive-ion etching. We used the second stage of e-beam lithography combining with lift-off method for the formation of GST225 active region on the resonator ring surface. The amorphous GST225 thin films were prepared by magnetron sputtering, and were capped by thin silicon oxide on their tops. The length of the GST225 active region varied from 0.1 to 20 μ m. Crystallization of amorphous thin films was carried out at the temperature of 400 °C for 30 minutes. Auger electron spectroscopy and transmission electron microscopy were used for studying composition and structure of investigated GST225thin films, respectively. It was observed that crystallization of amorphous GST225 film lead to a decrease of the optical power, transmitted through the waveguide. Comparison of the optical transmittance of O-ring resonators before and after the GST225 deposition allowed to identify the change in the Q-factor and the wavelength peak shift. This can be explained by the differences of the complex refractive indexes of GST225 thin films in the amorphous and crystalline states. From the measurement data, the GST225 effective refractive index was extracted depending on the ring waveguide width of the resonator for a telecommunication wavelength of 1550 nm.

Abstract: We demonstrate experimentally that single photon detection can be achieved in micron-wide NbN bridges, with widths ranging from 0.53 μm to 5.15 μm and for photon-wavelengths from 408 nm to 1550 nm. The microbridges are biased with a dc current close to the experimental critical current, which is estimated to be about 50 % of the theoretically expected depairing current. These results offer an alternative to the standard superconducting single-photon detectors (SSPDs), based on nanometer scale nanowires implemented in a long meandering structure. The results are consistent with improved theoretical modelling based on the theory of non-equilibrium superconductivity including the vortex-assisted mechanism of initial dissipation.

Abstract: We report an experimental investigation of the hot-spot evolution in superconducting single-photon detectors made of disordered superconducting materials with different diffusivity and energy downconversion time values, i.e., 33-nm-thick NbN and 23-nm-thick NbC films. We have demonstrated that, in NbC film, only 405-nm photons produce sufficiently large hot spot to trigger a single-photon response. The dependence of detection efficiency on bias current for 405-nm photons in NbC is similar to that for 3400-nm photons in NbN. In NbC, large diffusivity and downconversion time result in 1-D critical current suppression profile compared with the usual 2-D profile in NbN.