Goltsman, G. (2017). Superconducting thin film nanostructures as terahertz and infrared heterodyne and direct detectors. In 16th ISEC (Th-I-QTE-03 (1 to 3)).
Abstract: We present our recent achievements in the development of superconducting nanowire single-photon detectors (SNSPDs) integrated with optical waveguides on a chip. We demonstrate both single-photon counting with up to 90% on-chipquantum-efficiency (OCDE), and the heterodyne mixing with a close to the quantum limit sensitivity at the telecommunication wavelength using single device.
|
Verevkin, A. A., Zhang, J., Slysz, W., Sobolewski, R., Lipatov, A. P., Okunev, O., et al. (2002). Superconducting single-photon detectors for GHz-rate free-space quantum communications. In J. C. Ricklin, & D. G. Voelz (Eds.), Proc. SPIE (Vol. 4821, pp. 447–454). SPIE.
Abstract: We report our studies on the performance of new NbN ultrathin-film superconducting single-photon detectors (SSPDs). Our SSPDs exhibit experimentally measured quantum efficiencies from 5% at wavelength λ = 1550 nm up to 10% at λ = 405 nm, with exponential, activation-energy-type spectral sensitivity dependence in the 0.4-μm – 3-μm wavelength range. Using a variable optical delay setup, we have shown that our NbN SSPDs can resolve optical photons with a counting rate up to 10 GHz, presently limited by the read-out electronics. The measured device jitter was below 35 ps under optimum biasing conditions. The extremely high photon counting rate, together with relatively high (especially for λ > 1 μm) quantum efficiency, low jitter, and very low dark counts, make NbN SSPDs very promising for free-space communications and quantum cryptography.
|
Zinoni, C., Alloing, B., Li, L. H., Marsili, F., Fiore, A., Lunghi, L., et al. (2007). Single-photonics at telecom wavelengths using nanowire superconducting single photon detectors. In CLEO/QELS (QTuF6 (1 to 2)). Optical Society of America.
Abstract: Novel single-photon detectors based on NbN superconducting nanostructures promise orders-of- magnitude improvement over InGaAs APDs. We demonstrate this improved performance for the first time by measuring the g(2)(τ) on single photon states produced by a quantum dot at telecom wavelength.
|
Sobolewski, R., Zhang, J., Slysz, W., Pearlman, A., Verevkin, A., Lipatov, A., et al. (2003). Ultrafast superconducting single-photon optical detectors. In J. Spigulis, J. Teteris, M. Ozolinsh, & A. Lusis (Eds.), Proc. SPIE (Vol. 5123, pp. 1–11). SPIE.
Abstract: We present a new class of single-photon devices for counting of both visible and infrared photons. Our superconducting single-photon detectors (SSPDs) are characterized by the intrinsic quantum efficiency (QE) reaching up to 100%, above 10 GHz counting rate, and negligible dark counts. The detection mechanism is based on the photon-induced hotspot formation and subsequent appearance of a transient resistive barrier across an ultrathin and submicron-wide superconducting stripe. The devices are fabricated from 3.5-nm-thick NbN films and operate at 4.2 K, well below the NbN superconducting transition temperature. Various continuous and pulsed laser sources in the wavelength range from 0.4 μm up to >3 μm were implemented in our experiments, enabling us to determine the detector QE in the photon-counting mode, response time, and jitter. For our best 3.5-nm-thick, 10×10 μm2-area devices, QE was found to reach almost 100% for any wavelength shorter than about 800 nm. For longer-wavelength (infrared) radiation, QE decreased exponentially with the photon wavelength increase. Time-resolved measurements of our SSPDs showed that the system-limited detector response pulse width was below 150 ps. The system jitter was measured to be 35 ps. In terms of the counting rate, jitter, and dark counts, the NbN SSPDs significantly outperform their semiconductor counterparts. Already identifeid and implemented applications of our devices range from noninvasive testing of semiconductor VLSI circuits to free-space quantum communications and quantum cryptography.
|
Okunev, O., Smirnov, K., Chulkova, G., Korneev, A., Lipatov, A., Gol'tsman, G., et al. (2002). Ultrafast NBN hot-electron single-photon detectors for electronic applications. In Abstracts 8-th IUMRS-ICEM.
Abstract: We present a new, simple to manufacture, single-photon detector (SPD), which can work from ultraviolet to near-infrared wavelengths of optical radiation and combines high speed of operation, high quantum efficiency (QE), and very low dark counts. The devices are superconducting and operate at temperature below 5 K. The physics of operation of our SPD is based on formation of a photon-induced resistive hotspot and subsequent appearance of a transient resistive barrier across an ultrathin and submicron-wide superconductor.
|
Casaburi, A., Ejrnaes, M., Quaranta, O., Gaggero, A., Mattioli, F., Leoni, R., et al. (2008). Experimental characterization of NbN nanowire optical detectors with parallel stripline configuration. In J. Phys.: Conf. Ser. (Vol. 97, 012265 (1 to 6)). IOP Publishing.
Abstract: We have developed a novel geometrical configuration for NbN-based superconducting single photon optical detector (SSPD) that achieves two goals: a much lower intrinsic impedance, and a consequently greater bandwidth, and a much larger signal amplitude compared to the standard meandered configuration. This has been obtained by implementing a properly designed parallel stripline structure where a cascade switching mechanism occurs when one of the striplines is hit by an optical photon. The overall switching occurs synchronously and in a very short time, giving rise to a strong and fast voltage pulse. The SSPD have been realized using state of the art NbN deposition technology and e-beam lithography. The strips are 100 nm wide and 5 μm long and have been realized with 4 nm NbN film on sapphire and Si substrate. We report on experimental characterization of such novel devices. The performances of the proposed novel type of SSPD are compared with standard SSPD design and results in terms of signal amplitude, risetime and effective detection area.
|
Slysz, W., Wegrzecki, M., Bar, J., Grabiec, P., Gol'tsman, G. N., Verevkin, M., et al. (2004). NbN superconducting single-photon detectors coupled with a communication fiber (Vol. 37).
|
Slysz, W., Wegrzecki, M., Papis, E., Gol'tsman, G. N., Verevkin, A., & Sobolewski, R. (2004). A method of optimization of the NbN superconducting single-photon detector (Vol. 36).
|
Rosfjord, K. M., Yang, J. K. W., Dauler, E. A., Anant, V., Berggren, K. K., Kerman, A. J., et al. (2006). Increased detection efficiencies of nanowire single-photon detectors by integration of an optical cavity and anti-reflection coating. In CLEO/QELS (JTuF2 (1 to 2)).
Abstract: We fabricate and test superconducting NbN-nanowire single-photon detectors with an integrated optical cavity and anti-reflection coating. We design the cavity and coating such as to maximize absorption in the NbN film of the detector.
|
Tarkhov, M., Claudon, J., Poizat, J. P., Korneev, A., Divochiy, A., Minaeva, O., et al. (2008). Ultrafast reset time of superconducting single photon detectors. Appl. Phys. Lett., 92(24), 241112 (1 to 3).
|
Sobolewski, R., Xu, Y., Zheng, X., Williams, C., Zhang, J., Verevkin, A., et al. (2002). Spectral sensitivity of the NbN single-photon superconducting detector. IEICE Trans. Electron., E85-C(3), 797–802.
Abstract: We report our studies on the spectral sensitivity of superconducting NbN thin-film single-photon detectors (SPD's) capable of GHz counting rates of visible and near-infrared photons. In particular, it has been shown that a NbN SPD is sensitive to 1.55-µm wavelength radiation and can be used for quantum communication. Our SPD's exhibit experimentally measured intrinsic quantum efficiencies from 20% at 800 nm up to 1% at 1.55-µm wavelength. The devices demonstrate picosecond response time (<100 ps, limited by our readout system) and negligibly low dark counts. Spectral dependencies of photon counting of continuous-wave, 0.4-µm to 3.5-µm radiation, and 0.63-µm, 1.33-µm, and 1.55-µm laser-pulsed radiations are presented for the single-stripe-type and meander-type devices.
|
Корнеев, А. А., Минаева, О., Рубцова, И., Милостная, И., Чулкова, Г., Воронов, Б., et al. (2005). Сверхпроводящий однофотонный детектор на основе ультратонкой пленки NbN. Квантовая электроника, 35(8), 698–700.
Abstract: Представлены результаты исследований сверхпроводящих однофотонных детекторов, изготовленных из ультратонкой пленки NbN. Развитие технологического процесса изготовления детекторов, а также снижение рабочей температуры до 2 К позволили существенно увеличить квантовую эффективность: для видимого света (λ = 0.56 мкм) она составила 30%–40%, т.е. достигла предела, определяемого коэффициентом поглощения пленки. С ростом длины волны квантовая эффективность экспоненциально падает, составляя ~20% на λ=1.55 мкм и ~0.02% на λ = 5 мкм. При скорости темнового счета ~10-4s-1 экспериментально измеренная эквивалентная мощность шума составила 1.5 × 10-20 Вт/Гц-1/2; в дальнейшем она может быть уменьшена до рекордно низкого значения 5 × 10-21 Вт/Гц-1/2. Временное разрешение детектора равно 30 пс.
|
Korneev, A., Minaeva, O., Rubtsova, I., Milostnaya, I., Chulkova, G., Voronov, B., et al. (2005). Superconducting single-photon ultrathin NbN film detector. Quantum Electronics, 35(8), 698–700.
Abstract: Superconducting single-photon ultrathin NbN film detectors are studied. The development of manufacturing technology of detectors and the reduction of their operating temperature down to 2 K resulted in a considerable increase in their quantum efficiency, which reached in the visible region (at 0.56 μm) 30%—40%, i.e., achieved the limit determined by the absorption coefficient of the film. The quantum efficiency exponentially decreases with increasing wavelength, being equal to ~20% at 1.55 μm and ~0.02% at 5 μm. For the dark count rate of ~10-4s-1, the experimental equivalent noise power was 1.5×10-20 W Hz-1/2; it can be decreased in the future down to the record low value of 5×10-21 W Hz-1/2. The time resolution of the detector is 30 ps.
|
Rosfjord, K. M., Yang, J. K. W., Dauler, E. A., Kerman, A. J., Vikas Anant, Voronov, B. M., et al. (2006). Nanowire Single-photon detector with an integrated optical cavity and anti-reflection coating. Opt. Express, 14(2), 527–534.
Abstract: We have fabricated and tested superconducting single-photon detectors and demonstrated detection efficiencies of 57% at 1550-nm wavelength and 67% at 1064 nm. In addition to the peak detection efficiency, a median detection efficiency of 47.7% was measured over 132 devices at 1550 nm. These measurements were made at 1.8K, with each device biased to 97.5% of its critical current. The high detection efficiencies resulted from the addition of an optical cavity and anti-reflection coating to a nanowire photodetector, creating an integrated nanoelectrophotonic device with enhanced performance relative to the original device. Here, the testing apparatus and the fabrication process are presented. The detection efficiency of devices before and after the addition of optical elements is also reported.
|
Sobolewski, R., Verevkin, A., Gol'tsman, G. N., Lipatov, A., & Wilsher, K. (2003). Ultrafast superconducting single-photon optical detectors and their applications. IEEE Trans. Appl. Supercond., 13(2), 1151–1157.
Abstract: We present a new class of ultrafast single-photon detectors for counting both visible and infrared photons. The detection mechanism is based on photon-induced hotspot formation, which forces the supercurrent redistribution and leads to the appearance of a transient resistive barrier across an ultrathin, submicrometer-width, superconducting stripe. The devices were fabricated from 3.5-nm- and 10-nm-thick NbN films, patterned into <200-nm-wide stripes in the 4 /spl times/ 4-/spl mu/m/sup 2/ or 10 /spl times/ 10-/spl mu/m/sup 2/ meander-type geometry, and operated at 4.2 K, well below the NbN critical temperature (T/sub c/=10-11 K). Continuous-wave and pulsed-laser optical sources in the 400-nm-to 3500-nm-wavelength range were used to determine the detector performance in the photon-counting mode. Experimental quantum efficiency was found to exponentially depend on the photon wavelength, and for our best, 3.5-nm-thick, 100-/spl mu/m/sup 2/-area devices varied from >10% for 405-nm radiation to 3.5% for 1550-nm photons. The detector response time and jitter were /spl sim/100 ps and 35 ps, respectively, and were acquisition system limited. The dark counts were below 0.01 per second at optimal biasing. In terms of the counting rate, jitter, and dark counts, the NbN single-photon detectors significantly outperform their semiconductor counterparts. Already-identified applications for our devices range from noncontact testing of semiconductor CMOS VLSI circuits to free-space quantum cryptography and communications.
|