Cherednichenko, S., Ronnung, F., Gol'tsman, G., Gershenzon, E., & Winkler, D. (1999). YBa2Cu3O7-δ hot-electron bolometer with submicron dimensions. In Proc. 10th Int. Symp. Space Terahertz Technol. (pp. 181–189).
Abstract: Photoresponse of YBa2Cu3O7-δ hot-electron bolometers to modulated near-infrared radiation was studied at a modulation .frequenc y var y ing from 0.2 MHz to 2 GHz. Bolometers were _fabricated from a 50 12 M thick film and had in-plane areas of 10x10 , um 2 . 2x0.2 s um', 1x0.2 p.m', and 0.5x0.2 jim. We found that nonequilibrium phonons cool down more effectively for the bolometers with smaller area. For the smallest bolometer the bolometric component in the response is 10 dB less than for the largest one.
|
|
|
|
Schwaab, G. W., Hübers, H. - W., Schubert, J., Erichsen, P., Gol'tsman, G., Semenov, A., et al. (1999). A high resolution spectrometer for the investigation of molecular structures in the THZ range. In Proc. 10th Int. Symp. Space Terahertz Technol. (pp. 530–538).
Abstract: A status report on the design study of a novel tunable far-infrared (TuFTR) spectrometer for the investigation of the structure of weakly bound molecular complexes is given. The goal is a sensitive TuFIR spectrometer with full frequency coverage from 1-6 THz. To hit the goal, advanced sources (e.g. p-Ge lasers) and detectors (e.g. superconducting hot electron bolometric (HEB) mixers) shall be employed to extend the technique of cavity ringdown spectroscopy, that is currently used at optical and infrared frequencies to the FIR spectral range. Critical for such a system are high-Q resonators that still allow good optical coupling, and wideband antireflection coatings to increase detector sensitivity and decrease optical path losses. 2 nd order effective media theory and an iterative multilayer algorithm have been employed to design wideband antireflection coatings for dielectrics with large dielectric constants like Ge or Si. Taking into account 6 layers, for Si bandwidths of 100% of the center frequency could be obtained with power reflectivities below 1% for both polarizations simultaneously. Wideband dielectric mirrors including absorption losses were also studied yielding a bandwidth of about 50% with reflectivities larger than 99.5%.
|
|
|
|
Lindgren, M., Currie, M., Zeng, W. - S., Sobolewski, R., Cherednichenko, S., Voronov, B., et al. (1998). Picosecond response of a superconducting hot-electron NbN photodetector. Appl. Supercond., 6(7-9), 423–428.
Abstract: The ps optical response of ultrathin NbN photodetectors has been studied by electro-optic sampling. The detectors were fabricated by patterning ultrathin (3.5 nm thick) NbN films deposited on sapphire by reactive magnetron sputtering into either a 5×10 μm2 microbridge or 25 1 μm wide, 5 μm long strips connected in parallel. Both structures were placed at the center of a 4 mm long coplanar waveguide covered with Ti/Au. The photoresponse was studied at temperatures ranging from 2.15 K to 10 K, with the samples biased in the resistive (switched) state and illuminated with 100 fs wide laser pulses at 395 nm wavelength. At T=2.15 K, we obtained an approximately 100 ps wide transient, which corresponds to a NbN detector response time of 45 ps. The photoresponse can be attributed to the nonequilibrium electron heating effect, where the incident radiation increases the temperature of the electron subsystem, while the phonons act as the heat sink. The high-speed response of NbN devices makes them an excellent choice for an optoelectronic interface for superconducting digital circuits, as well as mixers for the terahertz regime. The multiple-strip detector showed a linear dependence on input optical power and a responsivity =3.9 V/W.
|
|
|
|
Il'in, K. S., Cherednichenko, S. I., Gol'tsman, G. N., Currie, M., & Sobolewski, R. (1998). Comparative study of the bandwidth of phonon-cooled NbN hot-electron bolometers in submillimeter and optical wavelength ranges. In Proc. 9th Int. Symp. Space Terahertz Technol. (pp. 323–330).
Abstract: We report the results of the bandwidth measurements of NbN hot-electron bolometers, perfomied in the terahertz frequency domain at 140 GHz and 660 GHz and in time domain in the optical range at the wavelength of 395 nm.. Our studies were done on 3.5-nm-thick NbN films evaporated on sapphire substrates and patterned into ilin-size microbridges. In order to measure the gain bandwidth, we used two identical BWOs (140 or 660 GHz), one functioning as a local oscillator and the other as a signal source. The bandwidth we achieved was 3.5-4 GHz at 4.2 K with the optimal LO and DC biases. Time-domain measurements with a resolution below 300 fs were performed using an electro-optic sampling system, in the temperature range between 4.2 K to 9 K at various values of the bias current and optical power. The obtained response time of the NbN hot-electron bolometer to —100- fs-wide Ti:sapphire laser pulses was about 27 ps, what corresponds to the 5.9 GHz gain bandwidth.
|
|
|
|
Svechnikov, S. I., Okunev, O. V., Yagoubov, P. A., Gol'tsman, G. N., Voronov, B. M., Cherednichenko, S. I., et al. (1997). 2.5 THz NbN hot electron mixer with integrated tapered slot antenna. IEEE Trans. Appl. Supercond., 7(2), 3548–3551.
Abstract: A Hot Electron Bolometer (HEB) mixer for 2.5 THz utilizing a NbN thin film device, integrated with a Broken Linearly Tapered Slot Antenna (BLTSA), has been fabricated and is presently being tested. The NbN HEB device and the antenna were fabricated on a SiO2membrane. A 0.5 micrometer thick SiO2layer was grown by rf magnetron reactive sputtering on a GaAs wafer. The HEB device (phonon-cooled type) was produced as several parallel strips, 1 micrometer wide, from an ultrathin NbN film 4-7 nm thick, that was deposited onto the SiO2layer by dc magnetron reactive sputtering. The BLTSA was photoetched in a multilayer Ti-Au metallization. In order to strengthen the membrane, the front-side of the wafer was coated with a 5 micrometer thick polyimide layer just before the membrane formation. The last operation was anisotropic etching of the GaAs in a mixture of HNO3and H2O2.
|
|