Svechnikov, S. I., Okunev, O. V., Yagoubov, P. A., Gol'tsman, G. N., Voronov, B. M., Cherednichenko, S. I., et al. (1997). 2.5 THz NbN hot electron mixer with integrated tapered slot antenna. IEEE Trans. Appl. Supercond., 7(2), 3548–3551.
Abstract: A Hot Electron Bolometer (HEB) mixer for 2.5 THz utilizing a NbN thin film device, integrated with a Broken Linearly Tapered Slot Antenna (BLTSA), has been fabricated and is presently being tested. The NbN HEB device and the antenna were fabricated on a SiO2membrane. A 0.5 micrometer thick SiO2layer was grown by rf magnetron reactive sputtering on a GaAs wafer. The HEB device (phonon-cooled type) was produced as several parallel strips, 1 micrometer wide, from an ultrathin NbN film 4-7 nm thick, that was deposited onto the SiO2layer by dc magnetron reactive sputtering. The BLTSA was photoetched in a multilayer Ti-Au metallization. In order to strengthen the membrane, the front-side of the wafer was coated with a 5 micrometer thick polyimide layer just before the membrane formation. The last operation was anisotropic etching of the GaAs in a mixture of HNO3and H2O2.
|
Semenov, A. D., Gousev, Y. P., Renk, K. F., Voronov, B. M., Gol'tsman, G. N., Gershenzon, E. M., et al. (1997). Noise characteristics of a NbN hot-electron mixer at 2.5 THz. IEEE Trans. Appl. Supercond., 7(2), 3572–3575.
Abstract: The noise temperature of a NbN phonon cooled hot-electron mixer has been measured at a frequency of 2.5 THz for various operating conditions. We obtained for optimal operation a double sideband mixer noise temperature of /spl ap/14000 K and a system conversion loss of /spl ap/23 dB at intermediate frequencies up to 1 GHz. The dependences of the mixer noise temperature on the bias voltage, local oscillator power, and intermediate frequency were consistent with the phenomenological description based on the effective temperature approximation.
|
Zorin, M., Milostnaya, I., Gol'tsman, G. N., & Gershenzon, E. M. (1997). Fast NbN superconducting switch controlled by optical radiation. IEEE Trans. Appl. Supercond., 7(2), 3734–3737.
Abstract: The switching time and the optical control power of the NbN superconducting switch have been measured. The device is based on the ultrathin film 5-8 nm thick patterned as a structure of several narrow parallel strips (/spl sim/1 /spl mu/m wide) connected to wide current leads. The current-voltage characteristic of the switch at temperature 4.2 K demonstrated a hysteresis due to DC current self-heating. We studied the superconducting-to-resistive state transition induced by both optical and bias-current excitations. The optical pulse duration was /spl sim/20 ps and the rise time of the current step was determined to be less than 50 ps. The optical pulse was delivered to the switch by the semiconductor laser through an optical fiber. We found that the measured switching time is less than the duration of the optical excitation. The threshold optical power density does not exceed 3/spl middot/10/sup 3/ W/cm/sup 2/. The proposed device can be used in the fiber input of LTS rapid single flux quantum circuits.
|
Larrey, V., Villegier, J. - C., Salez, M., Miletto-Granozio, F., & Karpov, A. (1999). Processing and characterization of high Jc NbN superconducting tunnel junctions for THz analog circuits and RSFQ. IEEE Trans. Appl. Supercond., 9(2), 3216–3219.
Abstract: A generic NbN Superconducting Tunnel Junctions (STJ) technology has been developed using conventional substrates (Si and SOI-SIMOX) for making THz spectrometers including SIS receivers and RSFQ logic gates. NbN/MgO/NbN junctions with area of 1 /spl mu/m/sup 2/, Jc of 10 kA/cm/sup 2/ and low sub-gap leakage current (Vm>25 mV) are currently obtained from room temperature sputtered multilayers followed by a post-annealing at 250/spl deg/C. Using a thin MgO buffer layer deposited underneath the NbN electrodes, ensures lower NbN surface resistance values (Rs=7 /spl mu//spl Omega/) at 10 GHz and 4 K. Epitaxial NbN [100] films on MgO [100] with high gap frequency (1.4 THz) have also been achieved under the same deposition conditions at room temperature. The NbN SIS has shown good I-V photon induced steps when LO pumped at 300 GHz. We have developed an 8 levels Al/NbN multilayer process for making 1.5 THz SIS mixers (including Al antennas) on Si membranes patterned in SOI-SIMOX. Using the planarization techniques developed at the Si-MOS CEA-LETI Facility, we have also demonstrated on the possibility of extending our NbN technology to high level RSFQ circuit integration with 0.5 /spl mu/m/sup 2/ junction area, made on large area substrates (up to 8 inches).
|
Il'in, K. S., Currie, M., Lindgren, M., Milostnaya, I. I., Verevkin, A. A., Gol'tsman, G. N., et al. (1999). Quantum efficiency and time-domain response of superconducting NbN hot-electron photodetectors. IEEE Trans. Appl. Supercond., 9(2), 3338–3341.
Abstract: We report our studies on the response of ultrathin superconducting NbN hot-electron photodetectors. We have measured the photoresponse of few-nm-thick, micron-size structures, which consisted of single and multiple microbridges, to radiation from the continuous-wave semiconductor laser and the femtosecond Ti:sapphire laser with the wavelength of 790 nm and 400 nm, respectively. The maximum responsivity was observed near the film's superconducting transition with the device optimally current-biased in the resistive state. The responsivity of the detector, normalized to its illuminated area and the coupling factor, was 220 A/W(3/spl times/10/sup 4/ V/W), which corresponded to a quantum efficiency of 340. The responsivity was wavelength independent from the far infrared to the ultraviolet range, and was at least two orders of magnitude higher than comparable semiconductor optical detectors. The time constant of the photoresponse signal was 45 ps, when was measured at 2.15 K in the resistive (switched) state using a cryogenic electro-optical sampling technique with subpicosecond resolution. The obtained results agree very well with our calculations performed using a two-temperature model of the electron heating in thin superconducting films.
|