Okunev, O., Smirnov, K., Chulkova, G., Korneev, A., Lipatov, A., Gol'tsman, G., et al. (2002). Ultrafast NBN hot-electron single-photon detectors for electronic applications. In Abstracts 8-th IUMRS-ICEM.
Abstract: We present a new, simple to manufacture, single-photon detector (SPD), which can work from ultraviolet to near-infrared wavelengths of optical radiation and combines high speed of operation, high quantum efficiency (QE), and very low dark counts. The devices are superconducting and operate at temperature below 5 K. The physics of operation of our SPD is based on formation of a photon-induced resistive hotspot and subsequent appearance of a transient resistive barrier across an ultrathin and submicron-wide superconductor.
|
Verevkin, A., Xu, Y., Zheng, X., Williams, C., Sobolewski, R., Okunev, O., et al. (2001). Superconducting NbN-based ultrafast hot-electron single-photon detector for infrared range. In Proc. 12th Int. Symp. Space Terahertz Technol. (pp. 462–468).
|
Il'in, K. S., Gol'tsman, G. N., Voronov, B. M., & Sobolewski, R. (1999). Characterization of the electron energy relaxation process in NbN hot-electron devices. In Proc. 10th Int. Symp. Space Terahertz Technol. (pp. 390–397).
Abstract: We report on transient measurements of electron energy relaxation in NbN films with 300-fs time resolution. Using an electro-optic sampling technique, we have studied the photoresponse of 3.5-nm-thick NbN films deposited on sapphire substrates and exposed to 100-fs-wide optical pulses. Our experimental data analysis was based on the two-temperature model and has shown that in our films at the superconducting transition 10.5 K the inelastic electron-phonon scattering time was about (111}+-__.2) ps. This response time indicated that the maximum intermediate-frequency band of a NbN hot-electron phonon-cooled mixer should reach (16+41-3) GHz if one eliminates the bolometric phonon-heating effect. We have suggested several ways to increase the effectiveness of phonon cooling to achieve the above intrinsic value of the NbN mixer bandwidth.
|
Verevkin, A., Zhang, J., Pearlman, A., Slysz, W., Sobolewski, R., Korneev, A., et al. (2004). Ultimate sensitivity of superconducting single-photon detectors in the visible to infrared range.
Abstract: We present our quantum efficiency (QE) and noise equivalent power (NEP) measurements of the meandertype ultrathin NbN superconducting single-photon detector in the visible to infrared radiation range. The nanostructured devices with 3.5-nm film thickness demonstrate QE up to~ 10% at 1.3–1.55 µm wavelength, and up to 20% in the entire visible range. The detectors are sensitive to infrared radiation with the wavelengths down to~ 10 µm. NEP of about 2× 10-18 W/Hz1/2 was obtained at 1.3 µm wavelength. Such high sensitivity together with GHz-range counting speed, make NbN photon counters very promising for efficient, ultrafast quantum communications and another applications. We discuss the origin of dark counts in our devices and their ultimate sensitivity in terms of the resistive fluctuations in our superconducting nanostructured devices.
|
Il'in, K. S., Lindgren, M., Currie, M. A., Semenov, D., Gol'tsman, G. N., Sobolewski, R., et al. (2000). Picosecond hot-electron energy relaxation in NbN superconducting photodetectors. Appl. Phys. Lett., 76(19), 2752–2754.
Abstract: We report time-resolved characterization of superconducting NbN hot-electron photodetectors using an electro-optic sampling method. Our samples were patterned into micron-size microbridges from 3.5-nm-thick NbN films deposited on sapphire substrates. The devices were illuminated with 100 fs optical pulses, and the photoresponse was measured in the ambient temperature range between 2.15 and 10.6 K (superconducting temperature transition TC). The experimental data agreed very well with the nonequilibrium hot-electron, two-temperature model. The quasiparticle thermalization time was ambient temperature independent and was measured to be 6.5 ps. The inelastic electron–phonon scattering time Ï„e–ph tended to decrease with the temperature increase, although its change remained within the experimental error, while the phonon escape time Ï„es decreased almost by a factor of two when the sample was put in direct contact with superfluid helium. Specifically, Ï„e–ph and Ï„es, fitted by the two-temperature model, were equal to 11.6 and 21 ps at 2.15 K, and 10(±2) and 38 ps at 10.5 K, respectively. The obtained value of Ï„e–ph shows that the maximum intermediate frequency bandwidth of NbN hot-electron phonon-cooled mixers operating at TC can reach 16(+4/–3) GHz if one eliminates the bolometric phonon-heating effect.
|