Yagoubov, P., Gol'tsman, G., Voronov, B., Svechnikov, S., Cherednichenko, S., Gershenzon, E., et al. (1996). Quasioptical phonon-cooled NbN hot-electron bolometer mixer at THz frequencies. In Proc. 7th Int. Symp. Space Terahertz Technol. (pp. 303–317).
Abstract: In our experiments we tested phonon-cooled hot-electron bolometer (HEB) quasioptical mixer based on spiral antenna designed for 0.5-1.2 THz frequency band and fabricated on sapphire, Si-coated sapphire and high resistivity silicon substrates. HEB devices were produced from thin superconducting NbN film 3.5-6 nm thick with the critical temperature of about 11-12 K. For these devices we achieved the receiver noise temperature T R (DSB) = 3000 K in the 500-700 GHz frequency range and an IF bandwidth of 3-4 GHz. Prelimanary measurements at frequencies 1-1.2 THz resulted the receiver noise temperature about 9000 K (DSB).
|
Gerecht, E., Musante, C. F., Wang, Z., Yngvesson, K. S., Mueller, E. R., Waldman, J., et al. (1996). Optimization of hot eleciron bolometer mixing efficiency in NbN at 119 micrometer wavelength. In Proc. 7th Int. Symp. Space Terahertz Technol. (pp. 584–600).
Abstract: We describe an investigation of a NbN HEB mixer for 2.5 THz. An intrinsic conversion loss of 23 dB has been measured with a two-laser measurement technique. The conversion loss was limited by the LO power available and is expected to decrease to 10 dB or less when sufficient LO power is available. For this initial experiment we used a prototype device which is directly coupled to the laser beams. We present results for a back-short technique that improves the optical coupling to the device and describe our progress for an antenna-coupled device with a smaller dimension. Based on our measured data for conversion loss and device output noise level, we predict that NbN HEB mixers will be capable of achieving DSB receiver noise temperatures of ten times the quantum noise limit in the THz range.
|
Kawamura, J., Blundell, R., Tong, C. - Y. E., Gol'tsman, G., Gershenzon, E., & Voronov, B. (1995). NbN hot-electron mixer measurements at 200 GHz. In Proc. 6th Int. Symp. Space Terahertz Technol. (pp. 254–261).
Abstract: We present noise and gain measurements of resistively driven NbN hot-electron mixers near 200 GHz. The device geometry is chosen so that the dominant cooling process of the hot-electrons is their interaction with the lattice. Except for a single batch, the intermediate frequency cut-off of these mixer elements is – 3 700 MHz, and has shown little variation among other batches of devices. At 100 MHz we measured intrinsic mixer losses as low as —3 dB. We measured the noise temperatures at several intermediate frequencies, and for the best de- vice at 137 MHz with 20 MHz bandwidth, we measured 2000 K; using a low-noise first- stage amplifier at 1.5 GHz with 200 MHz bandwidth, the receiver noise temperature measured 2800 K. We estimate that the noise contribution from the mixer is 500 K and the total losses are —15 dB at 137 MHz.
|
Gerecht, E., Musante, C. F., Schuch, R., Lutz, C. R., Jr., Yngvesson, K. S., et al. (1995). Hot electron detection and mixing experiments in NbN at 119 micrometer wavelength. In Proc. 6th Int. Symp. Space Terahertz Technol. (pp. 284–293).
Abstract: We have performed preliminary experiments with the goal of demonstrating a Hot Electron Bolometric (HEB) mixer for a 119 micrometer wavelength (2.5 THz). We have chosen a NbN device of size 700 x 350 micrometers. This device can easily be coupled to a laser LO source, which is advantageous for performing a prototype experiment. The relatively large size of the device means that the LO power required is in the mW range; this power can be easily obtained from a THz laser source. We have measured the amount of laser power actually absorbed in the device, and from this have estimated the best optical coupling loss to be about 10 di . We are developing methods for improving the optical coupling further. Preliminary measurements of the response of the device to a chopped black-body have not yet resulted in a measured receiver noise temperature. We expect to be able to complete this measurement in the near future.
|
Voronov, B. M., Gershenzon, E. M., Gol'tsman, G. N., Gubkina, T. O., & Semash, V. D. (1994). Superconductive properties of ultrathin NbN films on different substrates. Sverkhprovodimost': Fizika, Khimiya, Tekhnika, 7(6), 1097–1102.
Abstract: A study was made on dependence of surface resistance, critical temperature and width of superconducting transition on application temperature and thickness of NbN films, which varied within the range of 3-10 nm. Plates of sapphire, fused and monocrystalline quartz, MgO, as well as Si and silicon oxide were used as substrates. NbN films with 160 μθ·cm specific resistance and 16.5 K (Tc) critical temperature were obtained on sapphire substrates. Intensive growth of ΔTc was noted for films, applied on fused quartz, with increase of precipitation temperature. This is explained by occurrence of high tensile stresses in NbN films, caused by sufficient difference of thermal coefficients of expansion of NbN and quartz.
|
Voronov, B. M., Gershenzon, E. M., Gol'tsman, G. N., Gogidze, I. G., Gusev, Y. P., Zorin, M. A., et al. (1992). Picosecond range detector base on superconducting niobium nitride film sensitive to radiation in spectral range from millimeter waves up to visible light. Sverkhprovodimost': Fizika, Khimiya, Tekhnika, 5(5), 955–960.
Abstract: Fast-operating picosecond detector of electromagnetical radiation is developed on the basis of fine superconducting film of niobium nitride with high sensitivity within spectral range from millimetric waves up to visible light. Detector sensitive element represents structure covering narrow parallel strips with micron sizes included in the rupture of microstrip line. Detecting ability of the detector and time constant measured using amplitude-simulated radiation of reverse wave tubes and pulse radiation of picosecond gas and solid-body lasers, constitute D*≅1010 W-1·cm·Hz-1/2 and τ≤5 ps respectively, at 10 K temperature. The expected value of time constant of the detector at 10 K obtained via extrapolation of directly measured dependence that is, τ ∝ τ-1, constitutes 20 ps. Experimental data demonstrate that detection mechanism is linked with electron heating effect.
|
Budyanskij, M. Y., Sejdman, L. A., Voronov, B. M., & Gubkina, T. O. (1992). Increase of reproducibility in production of superconducting thin films of niobium nitride. Sverkhprovodimost': Fizika, Khimiya, Tekhnika, 5(10), 1950–1954.
Abstract: Technique to control the composition of gas medium in the reactive magnetron discharge and the composition of the deposited films of niobium nitride using electrical parameters of discharge only, in particular, by δU = Up – Uar value at contant stabilized discharge current is described. Technique to select optimal condition for deposition of niobium nitride films when the films have composition meeting chemical formula, is suggested. Thin films of niobium nitride with up to 7 nm thickness and with rather high temperature of transition into superconducting state Tk > 10 K) and with low width of transition (δ < 0.6 K), are obtained. It is determined, that substrate material and dielectric sublayer do not affect. Tk value, while difference in coefficients of thermal expansion of substrate and of film affects δTk value.
|
Averkin, A. S., Shishkin, A. G., Chichkov, V. I., Voronov, B. M., Goltsman, G. N., Karpov, A., et al. (2014). Tunable frequency-selective surface based on superconducting split-ring resonators. In 8th Metamaterials.
Abstract: We study a possibility to use the 2D superconducting metamaterial as a tunable frequency-selective surface (FSS). The proposed FSS is made of sub-wavelength size (l/14) metamaterial unit cells, where a split-ring resonator is embedded in a small iris aperture in a metal plane. The split-ring resonator is made of NbN film, and its resonance frequency is tuned by the temperature of the sample, changing the kinetic inductance of NbN film. The Ansoft HFSS simulation predicts the FSS tuning range of about 10-20 %. The developed superconducting FSS may be used as a tunable band-pass filter or modulator.
|
Hübers, H. - W., Semenov, A., Richter, H., Birk, M., Krocka, M., Mair, U., et al. (2002). Terahertz heterodyne receiver with a hot-electron bolometer mixer. In J. Wold, & J. Davidson (Eds.), Proc. Far-IR, Sub-mm, and mm Detector Technology Workshop.
Abstract: During the past decade major advances have been made regarding low noise mixers for terahertz (THz) heterodyne receivers. State of the art hot-electron-bolometer (HEB) mixers have noise temperatures close to the quantum limit and require less than a µW power from the local oscillator (LO). The technology is now at a point where the performance of a practical receiver employing such mixer, rather than the figures of merit of the mixer itself, are of major concern. We have incorporated a phonon-cooled NbN HEB mixer in a 2.5 THz heterodyne receiver and investigated the performance of the receiver. This yields important information for the development of heterodyne receivers such as GREAT (German receiver for astronomy at THz frequencies aboard SOFIA)[1] and TELIS (Terahertz limb sounder), a balloon borne heterodyne receiver for atmospheric research [2]. Both are currently under development at DLR.
|
Fedorov, G., Gayduchenko, I., Titova, N., Gazaliev, A., Moskotin, M., Kaurova, N., et al. (2018). Carbon nanotube based schottky diodes as uncooled terahertz radiation detectors. Phys. Status Solidi B, 255(1), 1700227 (1 to 6).
Abstract: Despite the intensive development of the terahertz technologies in the last decade, there is still a shortage of efficient room‐temperature radiation detectors. Carbon nanotubes (CNTs) are considered as a very promising material possessing many of the features peculiar for graphene (suppression of backscattering, high mobility, etc.) combined with a bandgap in the carrier spectrum. In this paper, we investigate the possibility to incorporate individual CNTs into devices that are similar to Schottky diodes. The latter is currently used to detect radiation with a frequency up to 50 GHz. We report results obtained with semiconducting (bandgap of about 0.5 eV) and quasi‐metallic (bandgap of few meV) single‐walled carbon nanotubes (SWNTs). Semiconducting CNTs show better performance up to 300 GHz with responsivity up to 100 V W−1, while quasi‐metallic CNTs are shown to operate up to 2.5 THz.
|