Danerud, M., Winkler, D., Lindgren, M., Zorin, M., Trifonov, V., Karasik, B., et al. (1994). A fast infrared detector based on patterned YBCO thin film. Supercond. Sci. Technol., 7(5), 321–323.
Abstract: Detectors for infrared radiation ( lambda =0.85 mu m) were made of 50 nm thick YBa2Cu3O7- delta films on LaAlO3 and MgO or 60 nm thick films on NdGaO3. Parallel strips (1 mu m wide by 20 mu m long) were patterned in the films and formed the active device. These devices were designed to detect short infrared laser pulses by electron heating. The detectors were current biased into the resistive and the normal states. The response was studied in direct pulse measurements as well as by amplitude modulation of a laser. The pulse measurements showed a fast picosecond response followed by a slower decay related to phonon escape through the film-substrate interface and heat diffusion in the substrate. The frequency spectra up to 10 GHz showed two slopes with a knee corresponding to the phonon escape time.
|
Gol'tsman, G. N., Semenov, A. D., Gousev, Y. P., Zorin, M. A., Gogidze, I. G., Gershenzon, E. M., et al. (1991). Sensitive picosecond NbN detector for radiation from millimetre wavelengths to visible light. Supercond. Sci. Technol., 4(9), 453–456.
Abstract: The authors report on the application of a broad-band NbN film detector which has high sensitivity and picosecond response time for detection of radiation from millimetre wavelengths to visible light. From a study of amplitude modulated radiation of backward-wave tubes and picosecond pulses from gas and solid state lasers at wavelengths between 2 mm and 0.53 mu m, they found a detectivity of 1010 W-1 cm Hz-1/2 and a response time of less than 50 ps at T=10 K. The characteristics were provided by using a 150 AA thick NbN film patterned into a structure of micron strips. According to the proposed detection mechanism, namely electron heating, they expect an intrinsic response time of approximately 20 ps at the same temperature.
|
Schubert, J., Semenov, A., Gol'tsman, G., Hübers, H. - W., Schwaab, G., Voronov, B., et al. (1999). Noise temperature of an NbN hot-electron bolometric mixer at frequencies from 0.7 THz to 5.2 THz. Supercond. Sci. Technol., 12(11), 748–750.
Abstract: We report on noise temperature measurements of an NbN phonon-cooled hot-electron bolometric mixer in the terahertz frequency range. The devices were 3 nm thick films with in-plane dimensions 1.7 × 0.2 µm2 and 0.9 × 0.2 µm2 integrated in a complementary logarithmic-spiral antenna. Measurements were performed at seven frequencies ranging from 0.7 THz to 5.2 THz. The measured DSB noise temperatures are 1500 K (0.7 THz), 2200 K (1.4 THz), 2600 K (1.6 THz), 2900 K (2.5 THz), 4000 K (3.1 THz), 5600 K (4.3 THz) and 8800 K (5.2 THz).
|
Kawamura, J., Blundell, R., Tong, C. ‐yu E., Gol’tsman, G., Gershenzon, E., & Voronov, B. (1996). Performance of NbN lattice‐cooled hot‐electron bolometric mixers. J. Appl. Phys., 80(7), 4232–4234.
Abstract: The heterodyne performance of lattice‐cooled hot‐electron bolometric mixers is measured at 200 GHz. Superconducting thin‐film niobium nitride strips with ∼5 nm thickness are used as waveguide mixer elements. A double‐sideband receiver noise temperature of 750 K at 244 GHz is measured at an intermediate frequency centered at 1.5 GHz with 500 MHz bandwidth and with 4.2 K device temperature. The instantaneous bandwidth for this mixer is 1.6 GHz. The local oscillator power required by the mixer is about 0.5 μW. The mixer is linear to within 1 dB up to an input power level 6 dB below the local oscillator power. A receiver incorporating a hot‐electron bolometric mixer was used to detect molecular line emission in a laboratory gascell. This experiment unambiguously confirms that the receiver noise temperature determined from Y‐factor measurements reflects the true heterodyne sensitivity.
|
Karasik, B. S., Zorin, M. A., Milostnaya, I. I., Elantev, A. I., Gol’tsman, G. N., & Gershenzon, E. M. (1995). Subnanosecond switching of YBaCuO films between superconducting and normal states induced by current pulse. J. Appl. Phys., 77(8), 4064–4070.
Abstract: A study is reported of the current switching in high‐quality YBaCuO films deposited onto NdGaO3 and ZrO2 substrates between superconducting (S) and normal (N) states. The films 60–120 nm thick prepared by laser ablation were structured into single strips between gold contacts. The time dependence of the resistance after application of the voltage step to the film was monitored. Experiment performed within certain ranges of voltage amplitudes and temperatures has shown the occurrence of the fast stage (shorter than 400 ps) both in S‐N and N‐S transitions. A fraction of the film resistance changing within this stage in the S‐N transition increases with the current amplitude. A subnanosecond N‐S stage becomes more pronounced for shorter pulses. The fast switching is followed by the much slower change of resistance. The mechanism of switching is discussed in terms of the hot‐electron phenomena in YBaCuO. The contributions of other thermal processes (e.g., a phonon escape from the film, a heat diffusion in the film and substrate, a resistive domain formation) in the subsequent stage of the resistance dynamic have been also discussed. The basic limiting characteristics (average dissipated power, energy needed for switching, maximum repetition rate) of a picosecond switch which is proposed to be developed are estimated.
|