Lindgren, M., Trifonov, V., Zorin, M., Danerud, M., Winkler, D., Karasik, B. S., et al. (1994). Transient resistive photoresponse of YBa2Cu3O7−δ films using low power 0.8 and 10.6 μm laser radiation. Appl. Phys. Lett., 64(22), 3036–3038.
Abstract: Thin YBa2Cu3O7−δ laser deposited films were patterned into devices consisting of ten parallel 1 μm wide strips. Nonequilibrium picosecond and bolometric photoresponses were studied by the use of 17 ps full width at half‐maximum laser pulses and amplitude modulated radiation from an AlGaAs laser up to 10 GHz and from a CO2 laser up to 1 GHz. The time and frequency domain measurements were in agreement. The fast response can be explained by electron heating. The use of low optical power and a sensitive measurement system excluded any nonlinear transient processes and kinetic inductance changes in the superconducting state. At 1 GHz modulation frequency, the responsivity was ∼1.2 V/W both for 0.8 and 10.6 μm wavelengths. The sensitivity of a fast and spectrally broadband infrared detector is discussed.
|
|
|
Sergeev, A. V., Semenov, A. D., Kouminov, P., Trifonov, V., Goghidze, I. G., Karasik, B. S., et al. (1994). Transparency of a YBa2Cu3O7-film/substrate interface for thermal phonons measured by means of voltage response to radiation. Phys. Rev. B Condens. Matter., 49(13), 9091–9096.
Abstract: The transparency of a film/substrate interface for thermal phonons was investigated for YBa2Cu3O7 thin films deposited on MgO, Al2O3, LaAlO3, NdGaO3, and ZrO2 substrates. Both voltage response to pulsed-visible and to continuously modulated far-infrared radiation show two regimes of heat escape from the film to the substrate. That one dominated by the thermal boundary resistance at the film/substrate interface provides an initial exponential decay of the response. The other one prevailing at longer times or smaller modulation frequencies causes much slower decay and is governed by phonon diffusion in the substrate. The transparency of the boundary for phonons incident from the film on the substrate and also from the substrate on the film was determined separately from the characteristic time of the exponential decay and from the time at which one regime was changed to the other. Taking into account the specific heat of optical phonons and the temperature dependence of the group velocity of acoustic phonons, we show that the body of experimental data agrees with acoustic mismatch theory rather than with the model that assumes strong diffusive scattering of phonons at the interface.
|
|
|
Semenov, A. D., Goghidze, I. G., Gol’tsman, G. N., Sergeev, A. V., & Gershenzon, E. M. (1993). Evidence for the spectral dependence of nonequilibrium picosecond photoresponse of YBaCuO thin films. Appl. Phys. Lett., 63(5), 681–683.
Abstract: The transient voltage photoresponse of current biased YBaCuO thin films to 20 ps laser pulses of 0.63 and 1.54 μm wavelengths is measured for temperatures around the superconducting transition region. The fast picosecond decay of the response is followed by a slow nanosecond relaxation which is associated with the bolometric effect. The magnitude of the fast component of the response varies in proportion to the square root of wavelength that plausibly reflects multiplication processes of photoexcited electrons via electron–electron scattering and interaction with high energy phonons.
|
|
|
Nebosis, R. S., Heusinger, M. A., Schatz, W., Renk, K. F., Gol’tsman, G. N., Karasik, B. S., et al. (1993). Ultrafast photoresponse of a structured YBa2Cu3O7-δ thin film to ultrashort FIR laser pulses. IEEE Trans. Appl. Supercond., 3(1), 2160–2162.
Abstract: The authors have investigated the photoinduced voltage response of a current-carrying structured YBa2Cu3O7-δ thin film to ultrashort far-infrared (FIR) laser pulses in the frequency range from 0.7 THz to 7 THz. The detector has shown an almost constant sensitivity of 1 mV/W and a noise equivalent power of less than 5*10/sup -7/ W/ square root Hz. The temperature dependence of the decay time of the detector signal was studied for temperatures around the transition temperature of the film ( approximately 80 K). For a detector temperature where dR/dT had its maximum, the authors observed bolometric signals with decay times of about 2 ns, and for lower temperatures they observed nonbolometric signals with decay times of approximately 120 ps; the duration of the nonbolometric signals was limited by the time resolution of the electronic registration equipment.
|
|
|
Semenov, A. D., Goghidze, I. G., Gol’tsman, G. N., Sergeev, A. V., Aksaev, E. E., & Gershenzon, E. M. (1993). Non-equilibrium quasiparticle response to radiation and bolometric effect in YBaCuO films. IEEE Trans. Appl. Supercond., 3(1), 2132–2135.
Abstract: The voltage photoresponse of structured current biased YBCO films on different substrates to 20-ps laser pulses of 0.63- mu m and 1.54- mu m wavelengths and to continuously modulated radiation of 2-mm wavelength is measured to temperatures around Tc. Fast picosecond decay of the response to pulsed radiation is followed by slow exponential relaxation with a nanosecond characteristic time depending on the substrate material and film dimensions. The slow component does not depend on wavelength and is attributed to the bolometric effect, while the magnitude of the fast component associated with nonequilibrium response rises with wavelength. More than an order-of-magnitude increase of the nonequilibrium response is seen from near-infrared to millimeter-wave range. This dependence plausibly reflects the low efficiency of multiplication of photoexcited electrons in YBaCuO compared to conventional superconductors.
|
|
|
Nebosis, R. S., Steinke, R., Lang, P. T., Schatz, W., Heusinger, M. A., Renk, K. F., et al. (1992). Picosecond YBa2Cu3O7−δdetector for far‐infrared radiation. J. Appl. Phys., 72(11), 5496–5499.
Abstract: We report on a picosecond YBa2Cu3O7−δ detector for far‐infrared radiation. The detector, consisting of a current carrying structure cooled to liquid‐nitrogen temperature, was studied by use of ultrashort laser pulses from an optically pumped far‐infrared laser in the frequency range from 25 to 215 cm−1. We found that the sensitivity (1 mV/W) was almost constant in this frequency range. We estimated a noise equivalent power of less than 5×10−7 W Hz−1/2. Taking into account the results of a mixing experiment (in the frequency range from 4 to 30 cm−1) we suggest that the response time of the detector was few picoseconds.
|
|
|
Semenov, A. D., Gol’tsman, G. N., Gogidze, I. G., Sergeev, A. V., Gershenzon, E. M., Lang, P. T., et al. (1992). Subnanosecond photoresponse of a YBaCuO thin film to infrared and visible radiation by quasiparticle induced suppression of superconductivity. Appl. Phys. Lett., 60(7), 903–905.
Abstract: We observed subnanosecond photoresponse of a structured superconducting YBa2Cu3O7−δ thin film to infrared and visible radiation. We measured the voltage response of a current biased film (thickness 700 Å) in a resistive state to radiation pulses. From our results we conclude a response time of about 90 ps and a responsivity of about 4×1010 Ω/J. We attribute the response to Cooper pair breaking and suppression of the superconducting energy gap induced by nonequilibrium quasiparticles.
|
|
|
Gershenzon, E. M., Gol’tsman, G. N., Semenov, A. D., & Sergeev, A. V. (1991). Mechanism of picosecond response of granular YBaCuO films to electromagnetic radiation. IEEE Trans. Magn., 27(2), 1321–1324.
Abstract: Ultrafast mechanisms of radiation detection in granular YBaCuO films are studied in the wide wavelength range from millimeter waves to near infrared. With an increase in radiation frequency, the Josephson detection at the grain-boundary weak links is replaced by electron heating into the grains. This change occurs in the submillimeter wavelength range. The electron-phonon relaxation time tau /sub eph/ is determined from direct measurements, quasi-stationary electron heating measurements, and the frequency dependence of the current at which maximum voltage shift is observed. The temperature dependence of tau /sub eph/ at T<or=40 K was found to be tau /sub eph/ approximately T/sup -1/. The results show that detectors with a response time of a few picoseconds at nitrogen temperature are attainable.
|
|
|
Gershenzon, E. M., Gol’tsman, G. N., Dzardanov, A. L., & Zorin, M. A. (1991). Ultrafast superconductive switch. IEEE Trans. Magn., 27(2), 2844–2846.
Abstract: The transition from superconductive to resistive state caused by infrared radiation and bias current pulses was investigated in order to minimize switching time tau and driving power W. Experimental results for Nb microstrips confirm the correctness of calculations based on the model of electron heating. For Nb switches, tau measured directly is 0.3-0.8 ns for radiation pulses and 1-3 ns for bias current pulses at T=4.2 K, while for YBaCuO switches at T=77 K it is expected to be several picoseconds. For an YBaCuO sample with the dimensions of 5*2*0.15 mu m/sup 2/, W was 10 mW, and it can be further reduced to the order of several microwatts by decreasing the volume of the sample.
|
|
|
Blagosklonskaya, L. E., Gershenzon, E. M., Gol’tsman, G. N., & Elant’ev, A. I. (1978). Effect of a strong magnetic field on the spectrum of donors in InSb. Sov. Phys. Semicond., 11(12), 1395–1397.
|
|
|
Zhang, J., Verevkin, A., Slysz, W., Chulkova, G., Korneev, A., Lipatov, A., et al. (2017). Time-resolved characterization of NbN superconducting single-photon optical detectors. In J. C. Armitage (Ed.), Proc. SPIE (Vol. 10313, 103130F (1 to 3)). SPIE.
Abstract: NbN superconducting single-photon detectors (SSPDs) are very promising devices for their picosecond response time, high intrinsic quantum efficiency, and high signal-to-noise ratio within the radiation wavelength from ultraviolet to near infrared (0.4 gm to 3 gm) [1-3]. The single photon counting property of NbN SSPDs have been investigated thoroughly and a model of hotspot formation has been introduced to explain the physics of the photon- counting mechanism [4-6]. At high incident flux density (many-photon pulses), there are, of course, a large number of hotspots simultaneously formed in the superconducting stripe. If these hotspots overlap with each other across the width w of the stripe, a resistive barrier is formed instantly and a voltage signal can be generated. We assume here that the stripe thickness d is less than the electron diffusion length, so the hotspot region can be considered uniform. On the other hand, when the photon flux is so low that on average only one hotspot is formed across w at a given time, the formation of the resistive barrier will be realized only when the supercurrent at sidewalks surpasses the critical current (jr) of the superconducting stripe [1]. In the latter situation, the formation of the resistive barrier is associated with the phase-slip center (PSC) development. The effect of PSCs on the suppression of superconductivity in nanowires has been discussed very recently [8, 9] and is the subject of great interest.
|
|
|
Gol’tsman, G. N., & Gershenzon, E. M. (1993). High speed hot-electron superconducting bolometer. In J. R. Birch, & T. J. Parker (Eds.), Proc. SPIE (Vol. 2104, pp. 181–182). SPIE.
Abstract: Physical limitation of response time of a superconducting bolometer as well as the nature of non-equilibrium detection of radiation have been investigated for Al, Nb and NbN thin films in spectral range from submillimeter to near-infraredwavelengths [1,2]. In the case of ideal heat removal from the film with the f_‘. 100A thickness the detection mechanism is an electron heating effect that is not selective to radiation wavelength in a very broad range. The response time ofan electron heating bolometer is determined by an electron-phonon interaction time. This time is of about 10 ns, 0.5 ns and 20 ps for Al, Nb, and NbN correspondingly near the critical temperature of the superconducting film. Thesensitive area of the bolometer consists of a number of narrow strips (with awidth of 1µm) connected in parallel to contact pads; these pads together witha sapphire substrate and a ground plate represent the microstrip transmissionline with an impedance of 50 Q.
|
|
|
Karasik, B. S., Zorin, M. A., Milostnaya, I. I., Elantev, A. I., Gol’tsman, G. N., & Gershenzon, E. M. (1994). Evidence of subnanosecond transition stage in S-N current switching of YBaCuO films. In R. A. Buhrman, J. T. Clarke, K. Daly, R. H. Koch, J. A. Luine, & R. W. Simon (Eds.), Proc. SPIE (Vol. 2160, pp. 74–82). SPIE.
Abstract: We report on a study of S-N and N-S current switching in high quality YBaCuO films deposited onto ZrO2 and NdGaO3 substrates. The films 60-120 nm thick prepared by laser ablation were structured into single strips and were provided with gold contacts. We monitored the time dependence of the resistance upon application of the voltage step on the film. Experiment performed within certain ranges of voltage amplitudes and temperatures showed the occurrence of the fast stage both in S-N (shorter than 300 ps) and N-S transition. We discuss the mechanism of switching taking into account the hot electron phenomena in YBaCuO. The contributions of various thermal processes in the subsequent stage of the resistance dynamic are also discussed. The basic limiting characteristics (average dissipated power, minimum work done for switching, maximum repetition rate) of a picosecond switch which is proposed to be developed are estimated.
|
|
|
Huebers, H. - W., Schubert, J., Semenov, A., Gol’tsman, G. N., Voronov, B. M., Gershenzon, E. M., et al. (1999). NbN phonon-cooled hot-electron bolometer as a mixer for THz heterodyne receivers. In J. M. Chamberlain (Ed.), Proc. SPIE (Vol. 3828, pp. 410–416). Spie.
Abstract: We have investigated a phonon-cooled NbN hot electron bolometric (HEB) mixer in the frequency range from 0.7 THz to 5.2 THz. The device was a 3.5 nm thin film with an in- plane dimension of 1.7 X 0.2 micrometers 2 integrated in a complementary logarithmic spiral antenna. The measured DSB receiver noise temperatures are 1500 K, 2200 K, 2600 K, 2900 K, 4000 K, 5600 K and 8800 K. The sensitivity fluctuation, the long term stability, and the antenna pattern were measured and the suitability of the mixer for a practical heterodyne receiver is discussed.
|
|
|
Gershenzon, E. M., Gol’tsman, G. N., Sergeev, A., & Semenov, A. D. (1990). Picosecond response of YBaCuO films to electromagnetic radiation. In W. Gorzkowski, M. Gutowski, A. Reich, & H. Szymczak (Eds.), Proc. European Conf. High-Tc Thin Films and Single Crystals (pp. 457–462).
Abstract: Radiation-induced change of the resistance was studied in the resistive state of YBaCuO films. Electron-phonon relaxation time T h was determmed from direct ep measurements and analysis of quasistationary electron heating. Temperature dependence of That TS 40 K was found to – ep be T h.. T'. The resul ts show that ep detectors with the response time of few picosecond at nitrogen temperature can be realized.
|
|