Floet D. W., Gao J. R., Klapwijk T. M., & de Korte P. A. J. (2000). Bias Dependence of the Thermal Time Constant in Nb Superconducting Diffusion-Cooled HEB Mixers. Appl. Phys. Lett., 77, 1719.
Abstract: We present an experimental study of the intermediate frequency bandwidth of a Nb diffusion-cooled hot-electron bolometer mixer for different bias voltages. The measurements show that the bandwidth increases with increasing voltage. Analysis of the data reveals that this effect is mainly caused by a decrease of the intrinsic thermal time of the mixer and that the effect of electrothermal feedback through the intermediate frequency circuit is small. The results are understood using a qualitative model, which takes into account the different effective diffusion constants in the normal and superconducting domains.
|
|
|
|
Baselmans, J. J. A., Hajenius, M., Gao, J. R., Klapwijk, T. M., de Korte, P. A. J., Voronov, B., et al. (2004). Doubling of sensitivity and bandwidth in phonon cooled hot electron bolometer mixers. Appl. Phys. Lett., 84(11), 1958–1960.
Abstract: We demonstrate that the performance of NbN lattice cooled hot electron bolometer mixers depends strongly on the interface quality between the bolometer and the contact structure. We show experimentally that both the receiver noise temperature and the gain bandwidth can be improved by more than a factor of 2 by cleaning the interface and adding an additional superconducting interlayer to the contact pad. Using this we obtain a double sideband receiver noise temperature TN,DSB=950 K
at 2.5 THz and 4.3 K, uncorrected for losses in the optics. At the same bias point, we obtain an IF gain bandwidth of 6 GHz.
|
|
|
|
Gershenson, M. E., Gong, D., Sato, T., Karasik, B. S., & Sergeev, A. V. (2001). Millisecond electron-phonon relaxation in ultrathin disordered metal films at millikelvin temperatures. Appl. Phys. Lett., 79, 2049–2051.
|
|
|
|
Prober, D. E. (1993). Superconducting terahertz mixer using a transition-edge microbolometer. Appl. Phys. Lett., 62(17), 2119–2121.
|
|
|
|
Il'in, K. S., Lindgren, M., Currie, M. A., Semenov, D., Gol'tsman, G. N., Sobolewski, R., et al. (2000). Picosecond hot-electron energy relaxation in NbN superconducting photodetectors. Appl. Phys. Lett., 76(19), 2752–2754.
Abstract: We report time-resolved characterization of superconducting NbN hot-electron photodetectors using an electro-optic sampling method. Our samples were patterned into micron-size microbridges from 3.5-nm-thick NbN films deposited on sapphire substrates. The devices were illuminated with 100 fs optical pulses, and the photoresponse was measured in the ambient temperature range between 2.15 and 10.6 K (superconducting temperature transition TC). The experimental data agreed very well with the nonequilibrium hot-electron, two-temperature model. The quasiparticle thermalization time was ambient temperature independent and was measured to be 6.5 ps. The inelastic electron–phonon scattering time Ï„e–ph tended to decrease with the temperature increase, although its change remained within the experimental error, while the phonon escape time Ï„es decreased almost by a factor of two when the sample was put in direct contact with superfluid helium. Specifically, Ï„e–ph and Ï„es, fitted by the two-temperature model, were equal to 11.6 and 21 ps at 2.15 K, and 10(±2) and 38 ps at 10.5 K, respectively. The obtained value of Ï„e–ph shows that the maximum intermediate frequency bandwidth of NbN hot-electron phonon-cooled mixers operating at TC can reach 16(+4/–3) GHz if one eliminates the bolometric phonon-heating effect.
|
|