Yagoubov, P., Kroug, M., Merkel, H., Kollberg, E., Hübers, H. - W., Schubert, J., et al. (1999). NbN hot electron bolometric mixers at frequencies between 0.7 and 3.1 THz. In Proc. 10th Int. Symp. Space Terahertz Technol. (pp. 238–246).
Abstract: The performance of NbN based phonon-cooled Hot Electron Bolometric (HEB) quasioptical mixers is investigated in the 0.7-3.1 THz frequency range. The devices are made from a 3.5-4 nm thick NbN film on high resistivity Si and integrated with a planar spiral antenna on the same substrate. The length of the bolometer microbridge is 0.1- 0.2 gm, the width is 1-2 gm. The best results of the DSB receiver noise temperature measured at 1.5 GHz intermediate frequency are: 800 K at 0.7 THz, 1100 K at 1.6 THz, 2000 K at 2.5 THz and 4200 K at 3.1 THz. The measurements were performed with a far infrared laser as the local oscillator (LO) source. The estimated LO power required is less than 500 nW at the receiver input. First results on the spiral antenna polarization measurements are reported.
|
|
|
Gershenzon, E. M., Gol'tsman, G. N., Emtsev, V. V., Mashovets, T. V., Ptitsyna, N. G., & Ryvkin, S. M. (1971). Role of impurities of groups III and V in the formation of defects following γ irradiation of germanium. JETP Lett., 14(6), 241.
|
|
|
Antipov, S. V., Svechnikov, S. I., Smirnov, K. V., Vakhtomin, Y. B., Finkel, M. I., Goltsman, G. N., et al. (2001). Noise temperature of quasioptical NbN hot electron bolometer mixers at 900 GHz. Physics of Vibrations, 9(4), 242–245.
|
|
|
Cherednichenko, S., Yagoubov, P., Il'In, K., Gol'tsman, G., & Gershenzon, E. (1997). Large bandwidth of NbN phonon-cooled hot-electron bolometer mixers on sapphire substrates. In Proc. 8th Int. Symp. Space Terahertz Technol. (pp. 245–257).
Abstract: The bandwidth of NbN phonon-cooled hot electron bolometer mixers has been systematically investigated with respect to the film thickness and film quality variation. The films, 2.5 to 10 mm thick, were fabricated on sapphire substrates using DC reactive magnetron sputtering. All devices consisted of several parallel strips, each 1 1.1 wide and 211 long, placed between Ti-Au contact pads. To measure the gain bandwidth we used two identical BWOs operating in the 120-140 GHz frequency range, one functioning as a local oscillator and the other as a signal source. The majority of the measurements were made at an ambient temperature of 4.5 K with optimal LO and DC bias. The maximum 3 dB bandwidth (about 4 GHz) was achieved for the devices made of films which were 2.5-3.5 nm thick, had a high critical temperature, and high critical current density. A theoretical analysis of bandwidth for these mixers based on the two-temperature model gives a good description of the experimental results if one assumes that the electron temperature is equal to the critical temperature.
|
|
|
Okunev, 0., Dzardranov, A., Gol'tsman, G., & Gershenzon, E. (1995). Performances of hot—electron superconducting mixer for frequencies less than the gap energy: NbN mixer for 100 GHz operation. In Proc. 6th Int. Symp. Space Terahertz Technol. (pp. 247–253).
Abstract: The possibilities to improve the parameters of the 100 GHz NbN HEB superconducting waveguide mixers have been studied. The device consists of a signal strip 1 gm wide by 2 Am long made of 40 A thick NbN film. The best operation point was found at 5 K, where the mixer bandwidth made up 1.5-2 GHz and the total loss diminished down to 8 dB. The critical current density has been increased up to " 40 6 A/cm 2 , the noise temperature of the receiver (DSB) has reduced down to 450 K and the local oscillator power has decreased down to -.4).1 mcV.
|
|