Huebers, H. - W., Semenov, A., Richter, H., Birk, M., Krocka, M., Mair, U., et al. (2003). Superconducting hot electron bolometer as mixer for far-infrared heterodyne receivers. In T. G. Phillips, & J. Zmuidzinas (Eds.), Proc. SPIE (Vol. 4855, pp. 395–401). Presented at the Society of Photo-Optical Instrumentation Engineers (SPIE) Conference, 4855. Tucson, USA: SPIE.
Abstract: Heterodyne receivers for applications in astronomy need quantum limited sensitivity. In instruments which are currently under development for SOFIA or Herschel superconducting hot electron bolometers (HEB) will be used to achieve this goal at frequencies above 1.4 THz. We present results of the development of a phonon-cooled NbN HEB mixer for GREAT, the German Receiver for Astronomy at Terahertz Frequencies, which will be flown aboard SOFIA. The mixer is a small superconducting bridge incorporated in a planar feed antenna and a hyperhemispherical lens. Mixers with logarithmic-spiral and double-slot feed antennas have been investigated with respect to their noise temperature, conversion loss, linearity and beam pattern. At 2.5 THz a double sideband noise temperature of 2200 K was achieved. The conversion loss was 17 dB. The response of the mixer was linear up to 400 K load temperature. The performance was verified by measuring an emission line of methanol at 2.5 THz. The measured linewidth is in good agreement with the linewidth deduced from pressure broadening measurements at millimeter wavelength. The results demonstrate that the NbN HEB is very well suited as a mixer for far-infrared heterodyne receivers.
|
|
|
|
Semenov, A. D., Hübers, H. - W., Richter, H., Birk, M., Krocka, M., Mair, U., et al. (2003). Superconducting hot-electron bolometer mixer for terahertz heterodyne receivers. IEEE Trans. Appl. Supercond., 13(2), 168–171.
Abstract: We present recent results showing the development of superconducting NbN hot-electron bolometer mixer for German receiver for astronomy at terahertz frequencies and terahertz limb sounder. The mixer is incorporated into a planar feed antenna, which has either logarithmic spiral or double-slot configuration, and backed on a silicon lens. The hybrid antenna had almost frequency independent and symmetric radiation pattern slightly broader than expected for a diffraction limited antenna. At 2.5 THz the best 2200 K double side-band receiver noise temperature was achieved across a 1 GHz intermediate frequency bandwidth centred at 1.5 GHz. For this operation regime, a receiver conversion efficiency of -17 dB was directly measured and the loss budget was evaluated. The mixer response was linear at load temperatures smaller than 400 K. Implementation of the MgO buffer layer on Si resulted in an increased 5.2 GHz gain bandwidth. The receiver was tested in the laboratory environment by measuring a methanol emission line at 2.5 THz.
|
|
|
|
Cherednichenko, S., Drakinskiy, V., Baubert, J., Lecomte, B., Dauplay, F., Krieg, J. M., et al. (2006). 2.5 THz multipixel heterodyne receiver based on NbN HEB mixers. In Proc. SPIE (Vol. 6275, 62750I (1 to 11)).
Abstract: A 16 pixel heterodyne receiver for 2.5 THz has been developed based on NbN superconducting hot-electron bolometer (HEB) mixers. The receiver uses a quasioptical RF coupling approach where HEB mixers are integrated into double dipole antennas on 1.5 µm thick Si3N4/SiO2 membranes. Spherical mirrors (one per pixel) and backshort distance from the antenna have been used to design the output mixer beam profile. The camera design allows all 16 pixel IF readout in parallel. The gain bandwidth of the HEB mixers on Si3N4/SiO2 membranes was found to be 0.7÷0.9 GHz, which is much smaller than for similar devices on silicon. Application of buffer layers and use of alternative types of membranes (e.g. silicon-on-insulator) is under investigation.
|
|
|
|
Nebosis, R. S., Semenov, A. D., Gousev, Y. P., & Renk, K. F. (1996). Rigorous analysis of a superconducting hot-electron bolometer mixer: theory and comparision with experiment. In Proc. 7th Int. Symp. Space Terahertz Technol. (pp. 601–613). Charlottesville, Virginia, USA.
|
|
|
|
Huebers, H. - W., Pavlov, S., Semenov, A., Köhler, R., Mahler, L., Tredicucci, A., et al. (2005). Terahertz quantum cascade laser as local oscillator in a heterodyne receiver. Optics Express, 13(15), 5890–5896.
Abstract: Terahertz quantum cascade lasers have been investigated with respect to their performance as a local oscillator in a heterodyne receiver. The beam profile has been measured and transformed in to a close to Gaussian profile resulting in a good matching between the field patterns of the quantum cascade laser and the antenna of a superconducting hot electron bolometric mixer. Noise temperature measurements with the hot electron bolometer and a 2.5 THz quantum cascade laser yielded the same result as with a gas laser as local oscillator.
|
|
|
|
Korneeva, Y., Florya, I., Semenov, A., Korneev, A., & Goltsman, G. (2011). New generation of nanowire NbN superconducting single-photon detector for mid-infrared. IEEE Trans. Appl. Supercond., 21(3), 323–326.
Abstract: We present a break-through approach to mid-infrared single-photon detection based on nanowire NbN superconducting single-photon detectors (SSPD). Although SSPD became a mature technology for telecom wavelengths (1.3-1.55 μm) its further expansion to mid-infrared wavelength was hampered by low sensitivity above 2 μm. We managed to overcome this limit by reducing the nanowire width to 50 nm, while retaining high superconducting properties and connecting the wires in parallel to produce a voltage response of sufficient magnitude. The new device exhibits 10 times better quantum efficiency at 3.5 μm wavelength than the “standard” SSPD.
|
|
|
|
Henrich, D., Dorner, S., Hofherr, M., Il'in, K., Semenov, A., Heintze, E., et al. (2012). Broadening of hot-spot response spectrum of superconducting NbN nanowire single-photon detector with reduced nitrogen content. J. Appl. Phys., 112.
Abstract: The spectral detection efficiency and the dark count rate of superconducting nanowire
single-photon detectors (SNSPD) have been studied systematically on detectors made from thin
NbN films with different chemical compositions. Reduction of the nitrogen content in the 4 nm
thick NbN films results in a decrease of the dark count rates more than two orders of magnitude
and in a red shift of the cut-off wavelength of the hot-spot SNSPD response. The observed
phenomena are explained by an improvement of uniformity of NbN films that has been confirmed
by a decrease of resistivity and an increase of the ratio of the measured critical current to the
depairing current. The latter factor is considered as the most crucial for both the cut-off
wavelength and the dark count rates of SNSPD. Based on our results we propose a set of criteria
for material properties to optimize SNSPD in the infrared spectral region. VC 2012 American
Institute of Physics. [http://dx.doi.org/10.1063/1.4757625]
|
|
|
|
Semenov, A. D., Nebosis, R. S., Gousev, Y. P., Heusinger, M. A., & Renk, K. F. (1995). Analysis of the nonequilibrium photoresponse of superconducting films to pulsed radiation by use of a two-temperature model. Phys. Rev. B, 52(1), 581–590.
Abstract: Photoresponse of a superconducting film in the resistive state to pulsed radiation has been studied in the framework of a model assuming that two different effective temperatures can be assigned to the quasiparticle and phonon nonequilibrium distributions. The coupled electron-phonon-substrate system is described by a system of time-dependent energy-balance differential equations for effective temperatures. An analytical solution of the system is given and calculated voltage transients are compared with experimental photoresponse signals taking into account the radiation pulse shape and the time resolution of the readout electronics. It is supposed that a resistive state (vortices, fluxons, network of intergrain junctions, hot spots, phase slip centers) provides an ultrafast connection between electron temperature changes and changes of the film resistance and thus plays a minor role in the temporal evolution of the response. In accordance with experimental observations a two-component response was revealed from simulations. The slower component corresponds to a bolometric mechanism while the fast component is connected with the relaxation of the electron temperature. Calculated photoresponse transients are presented for different ratios of the electron and phonon specific heat, radiation pulse durations and fluences, and frequency band passes of registration electronics. From the amplitude of the bolometric component we determine the radiation energy absorbed in a film. This enables us to reveal an intrinsic electron-phonon scattering time even if it is much shorter than the time resolution of readout electronics. We analyze experimental voltage transients for NbN, YBa2Cu3O7, and TlBa2Ca2Cu3O9 superconducting films and find the electron-phonon interaction times at the transition temperatures of 17, 2.5, and 1.8 ps, respectively. The values are in reasonable agreement with data of other experiments.
|
|
|
|
Lobanov, Y., Shcherbatenko, M., Finkel, M., Maslennikov, S., Semenov, A., Voronov, B. M., et al. (2015). NbN hot-electron-bolometer mixer for operation in the near-IR frequency range. IEEE Trans. Appl. Supercond., 25(3), 2300704 (1 to 4).
Abstract: Traditionally, hot-electron-bolometer (HEB) mixers are employed for THz and “super-THz” heterodyne detection. To explore the near-IR spectral range, we propose a fiber-coupled NbN film based HEB mixer. To enhance the incident-light absorption, a quasi-antenna consisting of a set of parallel stripes of gold is used. To study the antenna effect on the mixer performance, we have experimentally studied a set of devices with different size of the Au stripe and spacing between the neighboring stripes. With use of the well-known isotherm technique we have estimated the absorption efficiency of the mixer, and the maximum efficiency has been observed for devices with the smallest pitch of the alternating NbN and NbN-Au stripes. Also, a proper alignment of the incident Eâƒ<2014>-field with respect to the stripes allows us to improve the coupling further. Studying IV-characteristics of the mixer under differently-aligned Eâƒ<2014>-field of the incident radiation, we have noticed a difference in their shape. This observation suggests that a difference exists in the way the two waves with orthogonal polarizations parallel and perpendicular Eâƒ<2014>-field to the stripes heat the electrons in the HEB mixer. The latter results in a variation in the electron temperature distribution over the HEB device irradiated by the two waves.
|
|
|
|
Gousev, Y. P., Semenov, A. D., Pechen, E. V., Varlashkin, A. V., Nebosis, R. S., & Renk K. F. (1996). Coupling of terahertz radiation to a high-Т(с) superconducting hot electron bolometer mixer. Appl. Phys. Lett.,, 69, 691–693.
Abstract: We report on efficient coupling of THz radiation to a high-T(c) superconducting hot electron bolometer that is suitable for heterodyne detection. Our quasioptical system consisted of a planar self-complementary spiral antenna on a dielectric substrate clamped to an extended hyperhemispherical lens. The antenna was integrated into a co-planar line for broadband intermediate frequency matching. Measurements in the homodyne regime at a frequency of 2.5 THz showed a radiation pattern with a beam width of 1° and a coupling efficiency of 0.1. We measured, at an intermediate frequency of 1.5 GHz, an output noise temperature of'160 K and estimated for the device, operated in the heterodyne regime, a system noise temperature of 30 000 K. We also discuss possibilities of significant improvement of the sensitivity.
|
|