Smirnov, K., Divochiy, A., Vakhtomin, Y., Morozov, P., Zolotov, P., Antipov, A., et al. (2018). NbN single-photon detectors with saturated dependence of quantum efficiency. Supercond. Sci. Technol., 31(3), 035011 (1 to 8).
Abstract: The possibility of creating NbN superconducting single-photon detectors with saturated dependence of quantum efficiency (QE) versus normalized bias current was investigated. It was shown that the saturation increases for the detectors based on finer films with a lower value of Rs300/Rs20. The decreasing of Rs300/Rs20 was related to the increasing influence of quantum corrections to conductivity of superconductors and, in turn, to the decrease of the electron diffusion coefficient. The best samples have a constant value of system QE 94% at Ib/Ic ~ 0.8 and wavelength 1310 nm.
|
Yang, Z. Q., Hajenius, M., Baselmans, J. J. A., Gao, J. R., Voronov, B., & Gol’tsman, G. N. (2006). Reduced noise in NbN hot-electron bolometer mixers by annealing. Supercond. Sci. Technol., 19(4), L (9 to 12).
Abstract: We find that the sensitivity of heterodyne receivers based on superconducting hot-electron bolometers (HEBs) increases by 25–30% after annealing at 85 °C in vacuum. The devices studied are twin-slot antenna coupled mixers with a small NbN bridge of 1 × 0.15 µm2. We show that annealing changes the device properties as reflected in sharper resistive transitions of the complete device, apparently reducing the device-related noise. The lowest receiver noise temperature of 700 K is measured at a local oscillator frequency of 1.63 THz and a bath temperature of 4.3 K.
|
Lipatov, A., Okunev, O., Smirnov, K., Chulkova, G., Korneev, A., Kouminov, P., et al. (2002). An ultrafast NbN hot-electron single-photon detector for electronic applications. Supercond. Sci. Technol., 15(12), 1689–1692.
Abstract: We present the latest generation of our superconducting single-photon detector (SPD), which can work from ultraviolet to mid-infrared optical radiation wavelengths. The detector combines a high speed of operation and low jitter with high quantum efficiency (QE) and very low dark count level. The technology enhancement allows us to produce ultrathin (3.5 nm thick) structures that demonstrate QE hundreds of times better, at 1.55 μm, than previous 10 nm thick SPDs. The best, 10 × 10 μm2, SPDs demonstrate QE up to 5% at 1.55 μm and up to 11% at 0.86 μm. The intrinsic detector QE, normalized to the film absorption coefficient, reaches 100% at bias currents above 0.9 Ic for photons with wavelengths shorter than 1.3 μm.
|
Il'in, K. S., Verevkin, A. A., Gol'tsman, G. N., & Sobolewski, R. (1999). Infrared hot-electron NbN superconducting photodetectors for imaging applications. Supercond. Sci. Technol., 12(11), 755–758.
Abstract: We report an effective quantum efficiency of 340, responsivity >200 A W-1 (>104 V W-1) and response time of 27±5 ps at temperatures close to the superconducting transition for NbN superconducting hot-electron photodetectors (HEPs) in the near-infrared and optical ranges. Our studies were performed on a few nm thick NbN films deposited on sapphire substrates and patterned into µm-size multibridge detector structures, incorporated into a coplanar transmission line. The time-resolved photoresponse was studied by means of subpicosecond electro-optic sampling with 100 fs wide laser pulses. The quantum efficiency and responsivity studies of our photodetectors were conducted using an amplitude-modulated infrared beam, fibre-optically coupled to the device. The observed picosecond response time and the very high efficiency and sensitivity of the NbN HEPs make them an excellent choice for infrared imaging photodetectors and input optical-to-electrical transducers for superconducting digital circuits.
|
Rönnung, F., Cherednichenko, S., Winkler, D., & Gol'tsman, G. N. (1999). A nanoscale YBCO mixer optically coupled with a bow tie antenna. Supercond. Sci. Technol., 12(11), 853–855.
Abstract: The bolometric response of YBa2Cu3O7-δ(YBCO) hot-electron bolometers (HEBs) to near-infrared radiation was studied. Devices were fabricated from a 50 nm thick film and had in-plane areas of 10 × 10 µm2, 2 × 0.2 µm2, 1 × 0.2µm2 and 0.5 × 0.2 µm2. We found that nonequilibrium phonons cool down more effectively for the bolometers with smaller area. For the smallest bolometer the bolometric component in the response is 10 dB less than for the largest one.
|