Danerud, M., Winkler, D., Lindgren, M., Zorin, M., Trifonov, V., Karasik, B., et al. (1994). A fast infrared detector based on patterned YBCO thin film. Supercond. Sci. Technol., 7(5), 321–323.
Abstract: Detectors for infrared radiation ( lambda =0.85 mu m) were made of 50 nm thick YBa2Cu3O7- delta films on LaAlO3 and MgO or 60 nm thick films on NdGaO3. Parallel strips (1 mu m wide by 20 mu m long) were patterned in the films and formed the active device. These devices were designed to detect short infrared laser pulses by electron heating. The detectors were current biased into the resistive and the normal states. The response was studied in direct pulse measurements as well as by amplitude modulation of a laser. The pulse measurements showed a fast picosecond response followed by a slower decay related to phonon escape through the film-substrate interface and heat diffusion in the substrate. The frequency spectra up to 10 GHz showed two slopes with a knee corresponding to the phonon escape time.
|
Zorin, M., Milostnaya, I., Gol'tsman, G. N., & Gershenzon, E. M. (1997). Fast NbN superconducting switch controlled by optical radiation. IEEE Trans. Appl. Supercond., 7(2), 3734–3737.
Abstract: The switching time and the optical control power of the NbN superconducting switch have been measured. The device is based on the ultrathin film 5-8 nm thick patterned as a structure of several narrow parallel strips (/spl sim/1 /spl mu/m wide) connected to wide current leads. The current-voltage characteristic of the switch at temperature 4.2 K demonstrated a hysteresis due to DC current self-heating. We studied the superconducting-to-resistive state transition induced by both optical and bias-current excitations. The optical pulse duration was /spl sim/20 ps and the rise time of the current step was determined to be less than 50 ps. The optical pulse was delivered to the switch by the semiconductor laser through an optical fiber. We found that the measured switching time is less than the duration of the optical excitation. The threshold optical power density does not exceed 3/spl middot/10/sup 3/ W/cm/sup 2/. The proposed device can be used in the fiber input of LTS rapid single flux quantum circuits.
|
Zorin, M., Gol'tsman, G. N., Karasik, B. S., Elantev, A. I., Gershenzon, E. M., Lindgren, M., et al. (1995). Optical mixing in thin YBa2Cu3O7-x films. IEEE Trans. Appl. Supercond., 5(2), 2431–2434.
Abstract: High quality, j/sub c/ (77 K)>10/sup 6/ A/cm/sup 2/, epitaxial YBa2Cu3O7-x films of 50 nm thickness were patterned into ten parallel 1 /spl mu/m wide strips. The film structure was coupled to a single-mode fiber. Mixer response was obtained at 0.78 /spl mu/m using laser frequency modulation and an optical delay line. Using two semiconductor lasers at 1.55 /spl mu/m wavelength the beating signal was used to measure the photoresponse up to 18 GHz. Nonequilibrium photoresponse in the resistive state of the superconductor was observed. Bolometric response dominates up to 3 GHz, after which the nonequilibrium response is constant up to the frequency limit of our registration system. Using an electron heating model the influence of different thermal processes on the conversion loss has been analyzed. Ways of increasing the sensitivity are also discussed.
|
Karasik, B. S., Milostnaya, I. I., Zorin, M. A., Elantev, A. I., Gol'tsman, G. N., & Gershenzon, E. M. (1995). High speed current switching of homogeneous YBaCuO film between superconducting and resistive states. IEEE Trans. Appl. Supercond., 5(2), 3042–3045.
Abstract: Transitions of thin structured YBaCuO films from superconducting (S) to normal (N) state and back induced by a supercritical current pulse has been studied. A subnanosecond stage in the film resistance dynamic has been observed. A more gradual (nanosecond) ramp in the time dependence of the resistance follows the fast stage. The fraction of the film resistance which is attained during the fast S-N stage rises with the current amplitude. Subnanosecond N-S switching is more pronounced for smaller amplitudes of driving current and for shorter pulses. The phenomena observed are viewed within the framework of an electron heating model. The expected switching time and repetition rate of an optimized current controlling device are estimated to be 1-2 ps and 80 GHz respectively.
|
Gershenzon, E. M., Gol’tsman, G. N., Dzardanov, A. L., & Zorin, M. A. (1991). Ultrafast superconductive switch. IEEE Trans. Magn., 27(2), 2844–2846.
Abstract: The transition from superconductive to resistive state caused by infrared radiation and bias current pulses was investigated in order to minimize switching time tau and driving power W. Experimental results for Nb microstrips confirm the correctness of calculations based on the model of electron heating. For Nb switches, tau measured directly is 0.3-0.8 ns for radiation pulses and 1-3 ns for bias current pulses at T=4.2 K, while for YBaCuO switches at T=77 K it is expected to be several picoseconds. For an YBaCuO sample with the dimensions of 5*2*0.15 mu m/sup 2/, W was 10 mW, and it can be further reduced to the order of several microwatts by decreasing the volume of the sample.
|