Kawamura, J., Blundell, R., Tong, C. -yu E., Gol’tsman, G., Gershenzon, E., Voronov, B., et al. (1997). Low noise NbN lattice-cooled superconducting hot-electron bolometric mixers at submillimeter wavelengths. Appl. Phys. Lett., 70(12), 1619–1621.
Abstract: Lattice-cooled superconducting hot-electron bolometric mixers are used in a submillimeter-wave waveguide heterodyne receiver. The mixer elements are niobium nitride film with 3.5 nm thickness and ∼10 μm2 area. The local oscillator power for optimal performance is estimated to be 0.5 μW, and the instantaneous bandwidth is 2.2 GHz. At an intermediate frequency centered at 1.4 GHz with 200 MHz bandwidth, the double sideband receiver noise temperature is 410 K at 430 GHz. The receiver has been used to detect molecular line emission in a laboratory gas cell.
|
|
|
|
Cherednichenko, S., Kollberg, E., Angelov, I., Drakinskiy, V., Berg, T., & Merkel, H. (2005). Effect of the direct detection effect on the HEB receiver sensitivity calibration. In Proc. 16th Int. Symp. Space Terahertz Technol. (pp. 235–239). Göteborg, Sweden.
Abstract: We analyze the scale of the HEB receiver sensitivity calibration error caused by the so called “direct detection effect”. The effect comes from changing of the HEB parameters when whey face the calibration loads of different temperatures. We found that for HIFI Band 6 mixers (Herschel Space Observatory) the noise temperature error is of the order of 8% for 300K/77K loads (lab receiver) and 2.5% for 100K/10K loads (in HIFI). Using different approach we also predict that with an isolator between the mixer and the low noise amplifiers the error can be much smaller.
|
|
|
|
Meledin, D., Pantaleev, M., Pavolotsky, A., Risacher, C., Belitsky, V., Drakinskiy, V., et al. (2005). Balanced waveguide HEB mixer for APEX 1.3 THz receiver. In Proc. 16th Int. Symp. Space Terahertz Technol.. Göteborg, Sweden.
|
|
|
|
Yagubov, P., Gol'tsman, G., Voronov, B., Seidman, L., Siomash, V., Cherednichenko, S., et al. (1996). The bandwidth of HEB mixers employing ultrathin NbN films on sapphire substrate. In Proc. 7th Int. Symp. Space Terahertz Technol. (pp. 290–302). Charlottesville, Virginia, USA.
Abstract: We report on some unusual features observed during fabrication of ultrathin NbN films with high Tc. The films were used to fabricate HEB mixers, which were evaluated for IF bandwidth measurements at 140 GHz. Ultrathin films were fabricated using reactive dc magnetron sputtering with a discharge current source. Reproducible parameters of the films are assured keeping constant the difference between the discharge voltage in pure argon, and in a gas mixture, for the same current. A maximum bandwidth of 4 GHz at optimal LO and dc bias was obtained for mixer chip based on NbN film 35 A thick with Tc = 11 K.
|
|
|
|
Cherednichenko, S., Yagoubov, P., Il'In, K., Gol'tsman, G., & Gershenzon, E. (1997). Large bandwidth of NbN phonon-cooled hot-electron bolometer mixers on sapphire substrates. In Proc. 8th Int. Symp. Space Terahertz Technol. (pp. 245–257).
Abstract: The bandwidth of NbN phonon-cooled hot electron bolometer mixers has been systematically investigated with respect to the film thickness and film quality variation. The films, 2.5 to 10 mm thick, were fabricated on sapphire substrates using DC reactive magnetron sputtering. All devices consisted of several parallel strips, each 1 1.1 wide and 211 long, placed between Ti-Au contact pads. To measure the gain bandwidth we used two identical BWOs operating in the 120-140 GHz frequency range, one functioning as a local oscillator and the other as a signal source. The majority of the measurements were made at an ambient temperature of 4.5 K with optimal LO and DC bias. The maximum 3 dB bandwidth (about 4 GHz) was achieved for the devices made of films which were 2.5-3.5 nm thick, had a high critical temperature, and high critical current density. A theoretical analysis of bandwidth for these mixers based on the two-temperature model gives a good description of the experimental results if one assumes that the electron temperature is equal to the critical temperature.
|
|