Gousev, Y. P., Semenov, A. D., Gol'tsman, G. N., Sergeev, A. V., & Gershenzon, E. M. (1994). Electron-phonon interaction in disordered NbN films. Phys. B Condens. Mat., 194-196, 1355–1356.
Abstract: Electron-phonon interaction time has been investigated in disordered films of NbN. A temperatures below 5.5 K tau_eph ~ T -1"6 which is attributed to the renormalisation of phonon spectrum in thin films.
|
Semenov, A. D., Hübers, H. - W., Richter, H., Birk, M., Krocka, M., Mair, U., et al. (2002). 2.5 THz heterodyne receiver with NbN hot-electron-bolometer mixer. Phys. C: Supercond., 372-376, 448–453.
Abstract: We describe a 2.5 THz heterodyne receiver for applications in astronomy and atmospheric research. The receiver employs a superconducting NbN phonon-cooled hot-electron-bolometer mixer and an optically pumped far-infrared gas laser as local oscillator. 2200 K double sideband mixer noise temperature was measured at 2.5 THz across a 1 GHz intermediate frequency bandwidth centred at 1.5 GHz. The total conversion losses were 17 dB. The mixer response was linear at load temperatures smaller than 400 K. The receiver was tested in the laboratory environment by measuring the methanol line in emission. Observed pressure broadening confirms the true heterodyne detection regime of the mixer.
|
Cherednichenko, S., Kroug, M., Merkel, H., Khosropanah, P., Adam, A., Kollberg, E., et al. (2002). 1.6 THz heterodyne receiver for the far infrared space telescope. Phys. C: Supercond., 372-376, 427–431.
Abstract: A low noise heterodyne receiver is being developed for the terahertz range using a phonon-cooled hot-electron bolometric mixer based on 3.5 nm thick superconducting NbN film. In the 1–2 GHz intermediate frequency band the double-sideband receiver noise temperature was 450 K at 0.6 THz, 700 K at 1.6 THz and 1100 K at 2.5 THz. In the 3–8 GHz IF band the lowest receiver noise temperature was 700 K at 0.6 THz, 1500 K at 1.6 THz and 3000 K at 2.5 THz while it increased by a factor of 3 towards 8 GHz.
|
Marsili, F., Bitauld, D., Fiore, A., Gaggero, A., Leoni, R., Mattioli, F., et al. (2009). Superconducting parallel nanowire detector with photon number resolving functionality. J. Modern Opt., 56(2-3), 334–344.
Abstract: We present a new photon number resolving detector (PNR), the Parallel Nanowire Detector (PND), which uses spatial multiplexing on a subwavelength scale to provide a single electrical output proportional to the photon number. The basic structure of the PND is the parallel connection of several NbN superconducting nanowires (100 nm-wide, few nm-thick), folded in a meander pattern. Electrical and optical equivalents of the device were developed in order to gain insight on its working principle. PNDs were fabricated on 3-4 nm thick NbN films grown on sapphire (substrate temperature TS=900C) or MgO (TS=400C) substrates by reactive magnetron sputtering in an Ar/N2 gas mixture. The device performance was characterized in terms of speed and sensitivity. The photoresponse shows a full width at half maximum (FWHM) as low as 660ps. PNDs showed counting performance at 80 MHz repetition rate. Building the histograms of the photoresponse peak, no multiplication noise buildup is observable and a one photon quantum efficiency can be estimated to be QE=3% (at 700 nm wavelength and 4.2 K temperature). The PND significantly outperforms existing PNR detectors in terms of simplicity, sensitivity, speed, and multiplication noise.
|
Słysz, W., Wegrzecki, M., Bar, J., Grabiec, P., Górska, M., Zwiller, V., et al. (2007). Fibre-coupled, single photon detector based on NbN superconducting nanostructures for quantum communications. J. Modern Opt., 54(2-3), 315–326.
Abstract: We present a novel, two-channel, single photon receiver based on two fibre-coupled, NbN, superconducting, single photon detectors (SSPDs). The SSPDs are nanostructured superconducting meanders and are known for ultrafast and efficient detection of visible-to-infrared photons. Coupling between the NbN detector and optical fibre was achieved using a micromechanical photoresist ring placed directly over the SSPD, holding the fibre in place. With this arrangement, we obtained coupling efficiencies up to ∼30%. Our experimental results showed that the best receiver had a near-infrared system quantum efficiency of 0.33% at 4.2 K. The quantum efficiency increased exponentially with the photon energy increase, reaching a few percent level for visible-light photons. The photoresponse pulses of our devices were limited by the meander high kinetic inductance and had the rise and fall times of approximately 250 ps and 5 ns, respectively. The receiver's timing jitter was in the 37 to 58 ps range, approximately 2 to 3 times larger than in our older free-space-coupled SSPDs. We stipulate that this timing jitter is in part due to optical fibre properties. Besides quantum communications, the two-detector arrangement should also find applications in quantum correlation experiments.
|