Romanov, N. R., Zolotov, P. I., Vakhtomin, Y. B., Divochiy, A. V., & Smirnov, K. V. (2018). Electron diffusivity measurements of VN superconducting single-photon detectors. In J. Phys.: Conf. Ser. (Vol. 1124, 051032).
Abstract: The research of ultrathin vanadium nitride (VN) films as a promising candidate for superconducting single-photon detectors (SSPD) is presented. The electron diffusivity measurements are performed for such devices. Devices that were fabricated out from 9.9 nm films had diffusivity coefficient of 0.41 cm2/s and from 5.4 nm – 0.54 cm2/s. Obtained values are similar to other typical SSPD materials. The diffusivity that increases along with decreasing of the film thickness is expected to allow fabrication of the devices with improved characteristics. Fabricated VN SSPDs showed prominent single-photon response in the range 0.9-1.55 µm.
|
|
|
|
Zolotov, P. I., Divochiy, A. V., Vakhtomin, Y. B., Morozov, P. V., Seleznev, V. A., & Smirnov, K. V. (2017). Development of high-effective superconducting single-photon detectors aimed for mid-IR spectrum range. In J. Phys.: Conf. Ser. (Vol. 917, 062037).
Abstract: We report on development of superconducting single-photon detectors (SSPD) with high intrinsic quantum efficiency in the wavelength range 1.31 – 3.3 μm. By optimization of the NbN film thickness and its compound, we managed to improve detection efficiency of the detectors in the range up to 3.3 μm. Optimized devices showed intrinsic quantum efficiencies as high as 10% at mid-IR range.
|
|
|
|
Zolotov, P. I., Semenov, A. V., Divochiy, A. V., Goltsman, G. N., Romanov, N. R., & Klapwijk, T. M. (2021). Dependence of photon detection efficiency on normal-state sheet resistance in marginally superconducting films of NbN. IEEE Trans. Appl. Supercond., 31(5), 1–5.
Abstract: We present an extensive set of data on nanowire-type superconducting single-photon detectors based on niobium-nitride (NbN) to establish the empirical correlation between performance and the normal-state resistance per square. We focus, in particular, on the bias current, compared to the expected depairing current, needed to achieve a near-unity detection efficiency for photon detection. The data are discussed within the context of a model in which the photon energy triggers the movement of vortices i.e. superconducting dissipation, followed by thermal runaway. Since the model is based on the non-equilibrium theory for conventional superconductors deviations may occur, because the efficient regime is found when NbN acts as a marginal superconductor in which long-range phase coherence is frustrated.
|
|
|
|
Zolotov, P., Semenov, A., Divochiy, A., & Goltsman, G. (2021). A comparison of VN and NbN thin films towards optimal SNSPD efficiency. IEEE Trans. Appl. Supercond., 31(5), 1–4.
Abstract: Based on early phenomenological ideas about the operation of superconducting single-photon detectors (SSPD or SNSPD), it was expected that materials with a lower superconducting gap should perform better in the IR range. The plausibility of this concept could be checked using two popular SSPD materials – NbN and WSi films. However, these materials differ strongly in crystallographic structure (polycrystalline B1 versus amorphous), which makes their dependence on disorder different. In our work we present a study of the single-photon response of SSPDs made from two disordered B1 structure superconductors – vanadium nitride and niobium nitride thin films. We compare the intrinsic efficiency of devices made from films with different sheet resistance values. While both materials have a polycrystalline structure and comparable diffusion coefficient values, VN films show metallic behavior over a wide range of sheet resistance, in contrast to NbN films with an insulator-like temperature dependence of resistivity, which may be partially due to enhanced Coulomb interaction, leading to different starting points for the normal electron density of states. The results show that even though VN devices are more promising in terms of theoretical predictions, their optimal performance was not reached due to lower values of sheet resistance.
|
|
|
|
Samsonova, A. S., Zolotov, P. I., Baeva, E. M., Lomakin, A. I., Titova, N. A., Kardakova, A. I., et al. (2021). Signatures of surface magnetic disorder in niobium films. IEEE Trans. Appl. Supercond., 31(5), 1–5.
Abstract: We present our studies on the evolution of the normal and superconducting properties with thickness of thin Nb films with a low level of non-magnetic disorder ( kFl≈150 for the thickest film in the set). The analysis of the superconducting behavior points to the presence of magnetic moments, hidden in the native oxide on the surface of Nb films. Using the Abrikosov-Gorkov theory, we obtain the density of surface magnetic moments of 1013 cm −2 , which is in agreement with the previously reported data for Nb films.
|
|