Il’in, K. S., Milostnaya, I. I., Verevkin, A. A., Gol’tsman, G. N., Gershenzon, E. M., & Sobolewski, R. (1998). Ultimate quantum efficiency of a superconducting hot-electron photodetector. Appl. Phys. Lett., 73(26), 3938–3940.
Abstract: The quantum efficiency and current and voltage responsivities of fast hot-electron photodetectors, fabricated from superconducting NbN thin films and biased in the resistive state, have been shown to reach values of 340, 220 A/W, and 4×104 V/W,
respectively, for infrared radiation with a wavelength of 0.79 μm. The characteristics of the photodetectors are presented within the general model, based on relaxation processes in the nonequilibrium electron heating of a superconducting thin film. The observed, very high efficiency and sensitivity of the superconductor absorbing the photon are explained by the high multiplication rate of quasiparticles during the avalanche breaking of Cooper pairs.
|
|
|
Elvira, D., Michon, A., Fain, B., Patriarche, G., Beaudoin, G., Robert-Philip, I., et al. (2010). Time-resolved spectroscopy of InAsP/InP(001) quantum dots emitting near 2 μm. Appl. Phys. Lett., 97(13), 131907 (1 to 3).
Abstract: By using superconducting single photon detectors, we perform time-resolved characterization of a small ensemble of InAsP/InP quantum dots grown by metal organic vapor phase epitaxy, emitting at wavelengths between 1.6 and 2.2 μm. We demonstrate that alloying phosphorus with InAs allows to shift the emission wavelength toward higher wavelengths, while keeping the high optical quality of these quantum dots at room temperature, with no decrease in their radiative lifetime. This work was partially supported by Russian Ministry of Science and Education: Federal State Program “Scientific and Educational Cadres of Innovative” state Contract Nos. 02.740.0228, 14.740.11.0343, 14.740.11.0269, and P931, and RFBR Project No. 09-02-12364.
|
|
|
Rasulova, G. K., Brunkov, P. N., Pentin, I. V., Egorov, A. Y., Knyazev, D. A., Andrianov, A. V., et al. (2012). A weakly coupled semiconductor superlattice as a potential for a radio frequency modulated terahertz light emitter. Appl. Phys. Lett., 100(13), 131104 (1 to 4).
Abstract: The bolometer response to THz radiation from a weakly coupled GaAs/AlGaAs superlattice biased in the self-oscillations regime has been observed. The bolometer signal is modulated with the frequency equal to the fundamental frequency of superlattice self-oscillations. The frequency spectrum of the bolometer signal contains higher harmonics whose frequency is a multiple of fundamental frequency of self-oscillations.
This work was supported by State Contracts Nos. 16.740.11.0044 and 16.552.11.7002 of Ministry of Education and Science of the Russian Federation. Structural characterization was made on the equipment of the Joint Research Centre «Material science and characterization in advanced technology» (Ioffe Institute, St. Petersburg, Russia).
|
|
|
Zinoni, C., Alloing, B., Li, L. H., Marsili, F., Fiore, A., Lunghi, L., et al. (2010). Erratum: “Single photon experiments at telecom wavelengths using nanowire superconducting detectors” [Appl. Phys. Lett. 91, 031106 (2007)]. Appl. Phys. Lett., 96(8), 089901.
Abstract: A calculation error was made in the original publication of this letter. The error was in the calculation of the noise equivalent power (NEP) values for the avalanche photodiode detector (APD) and the superconducting single photon detector (SSPD), the incorrect values were plotted on the right axis in Fig. 1(b). The correct NEP values were calculated with the same equation reported in the original letter and the revised Fig. 1(b) is shown below. The other conclusions of the paper remain unaltered.
|
|
|
Zinoni, C., Alloing, B., Li, L. H., Marsili, F., Fiore, A., Lunghi, L., et al. (2007). Single-photon experiments at telecommunication wavelengths using nanowire superconducting detectors. Appl. Phys. Lett., 91(3), 031106 (1 to 3).
Abstract: The authors report fiber-coupled superconducting single-photon detectors with specifications that exceed those of avalanche photodiodes, operating at telecommunication wavelength, in sensitivity, temporal resolution, and repetition frequency. The improved performance is demonstrated by measuring the intensity correlation function g(2)(τ) of single-photon states at 1300nm produced by single semiconductor quantum dots.
This work was supported by Swiss National Foundation through the “Professeur borsier” and NCCR Quantum Photonics program, FP6 STREP “SINPHONIA” (Contract No. NMP4-CT-2005-16433), IP “QAP” (Contract No. 15848), NOE “ePIXnet,” and the Italian MIUR-FIRB program.
|
|
|
Ejrnaes, M., Cristiano, R., Quaranta, O., Pagano, S., Gaggero, A., Mattioli, F., et al. (2007). A cascade switching superconducting single photon detector. Appl. Phys. Lett., 91(26), 262509 (1 to 3).
Abstract: We have realized superconducting single photon detectors with reduced inductance and increased signal pulse amplitude. The detectors are based on a parallel connection of ultrathin NbN nanowires with a common bias inductance. When properly biased, an absorbed photon induces a cascade switch of all the parallel wires generating a signal pulse amplitude of 2mV. The parallel wire configuration lowers the detector inductance and reduces the response time well below 1ns.
This work was performed in the framework of the EU project “SINPHONIA” NMP4-CT-2005-016433.
|
|
|
Gao, J. R., Hajenius, M., Tichelaar, F. D., Klapwijk, T. M., Voronov, B., Grishin, E., et al. (2007). Monocrystalline NbN nanofilms on a 3C-SiC∕Si substrate. Appl. Phys. Lett., 91(6), 062504 (1 to 3).
Abstract: The authors have realized NbN (100) nanofilms on a 3C-SiC (100)/Si(100) substrate by dc reactive magnetron sputtering at 800°C. High-resolution transmission electron microscopy (HRTEM) is used to characterize the films, showing a monocrystalline structure and confirming epitaxial growth on the 3C-SiC layer. A film ranging in thickness from 3.4to4.1nm shows a superconducting transition temperature of 11.8K, which is the highest reported for NbN films of comparable thickness. The NbN nano-films on 3C-SiC offer a promising alternative to improve terahertz detectors. For comparison, NbN nanofilms grown directly on Si substrates are also studied by HRTEM.
The authors acknowledge S. V. Svetchnikov at National Centre for HRTEM at Delft, who prepared the specimens for HRTEM inspections. This work was supported by the EU through RadioNet and INTAS.
|
|
|
Kerman, A. J., Dauler, E. A., Yang, J. K. W., Rosfjord, K. M., Anant, V., Berggren, K. K., et al. (2007). Constriction-limited detection efficiency of superconducting nanowire single-photon detectors. Appl. Phys. Lett., 90(10), 101110 (1 to 3).
Abstract: We investigate the source of the large variations in the observed detection efficiencies of superconducting nanowire single-photon detectors between many nominally identical devices. Through both electrical and optical measurements, we infer that these variations arise from “constrictions:” highly localized regions of the nanowires where the effective cross-sectional area for superconducting current is reduced. These constrictions limit the bias-current density to well below its critical value over the remainder of the wire, and thus prevent the detection efficiency from reaching the high values that occur in these devices when they are biased near the critical current density.
This work is sponsored by the United States Air Force under Contract No. FA8721-05-C-0002.
|
|
|
Słysz, W., Węgrzecki, M., Bar, J., Grabiec, P., Górska, M., Zwiller, V., et al. (2006). Fiber-coupled single-photon detectors based on NbN superconducting nanostructures for practical quantum cryptography and photon-correlation studies. Appl. Phys. Lett., 88(26), 261113 (1 to 3).
Abstract: We have fabricated and tested a two-channel single-photon detector system based on two fiber-coupled superconducting single-photon detectors (SSPDs). Our best device reached the system quantum efficiency of 0.3% in the 1540-nm telecommunication wavelength with a fiber-to-detector coupling factor of about 30%. The photoresponse consisted of 2.5-ns-wide voltage pulses with a rise time of 250ps and timing jitter below 40ps. The overall system response time, measured as a second-order, photon cross-correlation function, was below 400ps. Our SSPDs operate at 4.2K inside a liquid-helium Dewar, but their optical fiber inputs and electrical outputs are at room temperature. Our two-channel detector system should find applications in practical quantum cryptography and in antibunching-type quantum correlation measurements.
The authors would like to thank Dr. Marc Currie for his assistance in early time-resolved photoresponse measurements and Professor Atac Imamoglu for his support. This work was supported by the Polish Ministry of Science under Project No. 3 T11B 052 26 (Warsaw), RFBR 03-02-17697 and INTAS 03-51-4145 grants (Moscow), CRDF Grant No. RE2-2531-MO-03 (Moscow), RE2-2529-MO-03 (Moscow and Rochester), and US AFOSR FA9550-04-1-0123 (Rochester). Additional funding was provided by the grants from the MIT Lincoln Laboratory and BBN Technologies Corp.
|
|
|
Kerman, A. J., Dauler, E. A., Keicher, W. E., Yang, J. K. W., Berggren, K. K., Gol’tsman, G., et al. (2006). Kinetic-inductance-limited reset time of superconducting nanowire photon counters. Appl. Phys. Lett., 88(11), 111116 (1 to 3).
Abstract: We investigate the recovery of superconducting NbN-nanowire photon counters after detection of an optical pulse at a wavelength of 1550nm, and present a model that quantitatively accounts for our observations. The reset time is found to be limited by the large kinetic inductance of these nanowires, which forces a tradeoff between counting rate and either detection efficiency or active area. Devices of usable size and high detection efficiency are found to have reset times orders of magnitude longer than their intrinsic photoresponse time.
The authors acknowledge D. Oates and W. Oliver (MIT Lincoln Laboratory), S.W. Nam, A. Miller, and R. Hadfield (NIST) and R. Sobolewski, A. Pearlman, and A. Verevkin (University of Rochester) for helpful discussions and technical assistance. This work made use of MIT’s shared scanning-electron-beam-lithography facility in the Research Laboratory of Electronics. This work is sponsored by the United States Air Force under Air Force Contract No. FA8721-05-C-0002. Opinions, interpretations, recommendations and conclusions are those of the authors and are not necessarily endorsed by the United States Government.
|
|