Karasik, B. S., Il'in, K. S., Pechen, E. V., & Krasnosvobodtsev, S. I. (1996). Diffusion cooling mechanism in a hot-electron NbC microbolometer mixer. Appl. Phys. Lett., 68(16), 2285–2287.
|
|
|
Il'in, K. S., Verevkin, A. A., Gol'tsman, G. N., & Sobolewski, R. (1999). Infrared hot-electron NbN superconducting photodetectors for imaging applications. Supercond. Sci. Technol., 12(11), 755–758.
Abstract: We report an effective quantum efficiency of 340, responsivity >200 A W-1 (>104 V W-1) and response time of 27±5 ps at temperatures close to the superconducting transition for NbN superconducting hot-electron photodetectors (HEPs) in the near-infrared and optical ranges. Our studies were performed on a few nm thick NbN films deposited on sapphire substrates and patterned into µm-size multibridge detector structures, incorporated into a coplanar transmission line. The time-resolved photoresponse was studied by means of subpicosecond electro-optic sampling with 100 fs wide laser pulses. The quantum efficiency and responsivity studies of our photodetectors were conducted using an amplitude-modulated infrared beam, fibre-optically coupled to the device. The observed picosecond response time and the very high efficiency and sensitivity of the NbN HEPs make them an excellent choice for infrared imaging photodetectors and input optical-to-electrical transducers for superconducting digital circuits.
|
|
|
Semenov, A. D., Il'in, K., Siegel, M., Smirnov, A., Pavlov, S., Richter, H., et al. (2006). Evidence of non-bolometric mixing in the bandwidth of a hot-electron bolometer. Supercond. Sci. Technol., 19(10), 1051–1056.
|
|
|
Cherednichenko, S., Yagoubov, P., Il'In, K., Gol'tsman, G., & Gershenzon, E. (1997). Large bandwidth of NbN phonon-cooled hot-electron bolometer mixers on sapphire substrates. In Proc. 8th Int. Symp. Space Terahertz Technol. (pp. 245–257).
Abstract: The bandwidth of NbN phonon-cooled hot electron bolometer mixers has been systematically investigated with respect to the film thickness and film quality variation. The films, 2.5 to 10 mm thick, were fabricated on sapphire substrates using DC reactive magnetron sputtering. All devices consisted of several parallel strips, each 1 1.1 wide and 211 long, placed between Ti-Au contact pads. To measure the gain bandwidth we used two identical BWOs operating in the 120-140 GHz frequency range, one functioning as a local oscillator and the other as a signal source. The majority of the measurements were made at an ambient temperature of 4.5 K with optimal LO and DC bias. The maximum 3 dB bandwidth (about 4 GHz) was achieved for the devices made of films which were 2.5-3.5 nm thick, had a high critical temperature, and high critical current density. A theoretical analysis of bandwidth for these mixers based on the two-temperature model gives a good description of the experimental results if one assumes that the electron temperature is equal to the critical temperature.
|
|
|
Henrich, D., Dorner, S., Hofherr, M., Il'in, K., Semenov, A., Heintze, E., et al. (2012). Broadening of hot-spot response spectrum of superconducting NbN nanowire single-photon detector with reduced nitrogen content. J. Appl. Phys., 112.
Abstract: The spectral detection efficiency and the dark count rate of superconducting nanowire
single-photon detectors (SNSPD) have been studied systematically on detectors made from thin
NbN films with different chemical compositions. Reduction of the nitrogen content in the 4 nm
thick NbN films results in a decrease of the dark count rates more than two orders of magnitude
and in a red shift of the cut-off wavelength of the hot-spot SNSPD response. The observed
phenomena are explained by an improvement of uniformity of NbN films that has been confirmed
by a decrease of resistivity and an increase of the ratio of the measured critical current to the
depairing current. The latter factor is considered as the most crucial for both the cut-off
wavelength and the dark count rates of SNSPD. Based on our results we propose a set of criteria
for material properties to optimize SNSPD in the infrared spectral region. VC 2012 American
Institute of Physics. [http://dx.doi.org/10.1063/1.4757625]
|
|