Akhmadishina, K. F., Bobrinetskiy, I. I., Komarov, I. A., Malovichko, A. M., Nevolin, V. K., Fedorov, G. E., et al. (2015). Fast-response biological sensors based on single-layer carbon nanotubes modified with specific aptamers. Semicond., 49(13), 1749–1753.
Abstract: The possibility of the fabrication of a fast-response biological sensor based on a composite of single-layer carbon nanotubes and aptamers for the specific detection of proteins is shown. The effect of modification of the surface of the carbon nanotubes on the selectivity and sensitivity of the sensors is investigated. It is shown that carboxylated nanotubes have a better selectivity for detecting thrombin.
|
|
|
|
Il'in, K. S., Lindgren, M., Currie, M. A., Semenov, D., Gol'tsman, G. N., Sobolewski, R., et al. (2000). Picosecond hot-electron energy relaxation in NbN superconducting photodetectors. Appl. Phys. Lett., 76(19), 2752–2754.
Abstract: We report time-resolved characterization of superconducting NbN hot-electron photodetectors using an electro-optic sampling method. Our samples were patterned into micron-size microbridges from 3.5-nm-thick NbN films deposited on sapphire substrates. The devices were illuminated with 100 fs optical pulses, and the photoresponse was measured in the ambient temperature range between 2.15 and 10.6 K (superconducting temperature transition TC). The experimental data agreed very well with the nonequilibrium hot-electron, two-temperature model. The quasiparticle thermalization time was ambient temperature independent and was measured to be 6.5 ps. The inelastic electron–phonon scattering time Ï„e–ph tended to decrease with the temperature increase, although its change remained within the experimental error, while the phonon escape time Ï„es decreased almost by a factor of two when the sample was put in direct contact with superfluid helium. Specifically, Ï„e–ph and Ï„es, fitted by the two-temperature model, were equal to 11.6 and 21 ps at 2.15 K, and 10(±2) and 38 ps at 10.5 K, respectively. The obtained value of Ï„e–ph shows that the maximum intermediate frequency bandwidth of NbN hot-electron phonon-cooled mixers operating at TC can reach 16(+4/–3) GHz if one eliminates the bolometric phonon-heating effect.
|
|
|
|
Gayduchenko, I., Kardakova, A., Fedorov, G., Voronov, B., Finkel, M., Jiménez, D., et al. (2015). Response of asymmetric carbon nanotube network devices to sub-terahertz and terahertz radiation. J. Appl. Phys., 118(19), 194303.
Abstract: Demand for efficient terahertz radiation detectors resulted in intensive study of the asymmetric carbon nanostructures as a possible solution for that problem. It was maintained that photothermoelectric effect under certain conditions results in strong response of such devices to terahertz radiation even at room temperature. In this work, we investigate different mechanisms underlying the response of asymmetric carbon nanotube (CNT) based devices to sub-terahertz and terahertz radiation. Our structures are formed with CNT networks instead of individual CNTs so that effects probed are more generic and not caused by peculiarities of an individual nanoscale object. We conclude that the DC voltage response observed in our structures is not only thermal in origin. So called diode-type response caused by asymmetry of the device IV characteristic turns out to be dominant at room temperature. Quantitative analysis provides further routes for the optimization of the device configuration, which may result in appearance of novel terahertz radiation detectors.
|
|
|
|
Gershenzon, E. M., Gershenzon, M. E., Goltsman, G. N., Semenov, A. D., & Sergeev, A. V. (1991). Wide-band highspeed Nb and YBaCuO detectors. IEEE Trans. Magn., 27(2), 2836–2839.
Abstract: The physical limitations on the response time and the nature of nonequilibrium detection of radiation were investigated for Nb and YBCO film in a wide spectral range from millimeter to near-infrared wavelengths. In the case of ideal heat removal from the film, the detection mechanism is connected with an electron heating effect which is not selective over a wide spectral interval. For Nb, the dependence of the response time on the electron mean free path l and temperature T is tau varies as T/sup -2/l/sup -1/. The values of detectivity D* and tau are 3*10/sup 11/ W/sup -1/ Hz/sup 1/2/ cm and 5*10/sup -9/ s at T=1.6 K, respectively. For YBCO film the tau value of 1-2 ps at T=77 K was obtained; the NEP value of 3*10/sup -11/ W-Hz/sup -1/2/ can be obtained at T=77 K in the case of the optimal film matching to the radiation.
|
|
|
|
Dauler, E., Kerman, A., Robinson, B., Yang, J., Voronov, B., Goltsman, G., et al. (2009). Photon-number-resolution with sub-30-ps timing using multi-element superconducting nanowire single photon detectors. J. Modern Opt., 56(2), 364–373.
Abstract: A photon-number-resolving detector based on a four-element superconducting nanowire single photon detector is demonstrated to have sub-30-ps resolution in measuring the arrival time of individual photons. This detector can be used to characterize the photon statistics of non-pulsed light sources and to mitigate dead-time effects in high-speed photon counting applications. Furthermore, a 25% system detection efficiency at 1550 nm was demonstrated, making the detector useful for both low-flux source characterization and high-speed photon-counting and quantum communication applications. The design, fabrication and testing of this detector are described, and a comparison between the measured and theoretical performance is presented.
|
|
|
|
Nebosis, R. S., Heusinger, M. A., Semenov, A. D., Lang, P. T., Schatz, W., Steinke, R., et al. (1993). Ultrafast photoresponse of an YBa2Cu3O7-δ film to far-infrared radiation pulses. Opt. Lett., 18(2), 96–97.
Abstract: We report the observation of an ultrafast photoresponse of a high-T(c), film to far-infrared radiation pulses. The response of a sample, consisting of a current-carrying structured YBa(2)Cu(3)O(7-delta) film cooled to liquid-nitrogen temperature, was studied by use of ultrashort laser pulses from an optically pumped far-infrared laser in the frequency range from 0.7 to 7 THz. We found that the response time was limited by the time resolution, 120 ps, of our electronic registration equipment.
|
|
|
|
Gershenzon, E. M., Gol’tsman, G. N., Semenov, A. D., & Sergeev, A. V. (1991). Mechanism of picosecond response of granular YBaCuO films to electromagnetic radiation. IEEE Trans. Magn., 27(2), 1321–1324.
Abstract: Ultrafast mechanisms of radiation detection in granular YBaCuO films are studied in the wide wavelength range from millimeter waves to near infrared. With an increase in radiation frequency, the Josephson detection at the grain-boundary weak links is replaced by electron heating into the grains. This change occurs in the submillimeter wavelength range. The electron-phonon relaxation time tau /sub eph/ is determined from direct measurements, quasi-stationary electron heating measurements, and the frequency dependence of the current at which maximum voltage shift is observed. The temperature dependence of tau /sub eph/ at T<or=40 K was found to be tau /sub eph/ approximately T/sup -1/. The results show that detectors with a response time of a few picoseconds at nitrogen temperature are attainable.
|
|
|
|
Marsili, F., Bitauld, D., Fiore, A., Gaggero, A., Leoni, R., Mattioli, F., et al. (2009). Superconducting parallel nanowire detector with photon number resolving functionality. J. Modern Opt., 56(2-3), 334–344.
Abstract: We present a new photon number resolving detector (PNR), the Parallel Nanowire Detector (PND), which uses spatial multiplexing on a subwavelength scale to provide a single electrical output proportional to the photon number. The basic structure of the PND is the parallel connection of several NbN superconducting nanowires (100 nm-wide, few nm-thick), folded in a meander pattern. Electrical and optical equivalents of the device were developed in order to gain insight on its working principle. PNDs were fabricated on 3-4 nm thick NbN films grown on sapphire (substrate temperature TS=900C) or MgO (TS=400C) substrates by reactive magnetron sputtering in an Ar/N2 gas mixture. The device performance was characterized in terms of speed and sensitivity. The photoresponse shows a full width at half maximum (FWHM) as low as 660ps. PNDs showed counting performance at 80 MHz repetition rate. Building the histograms of the photoresponse peak, no multiplication noise buildup is observable and a one photon quantum efficiency can be estimated to be QE=3% (at 700 nm wavelength and 4.2 K temperature). The PND significantly outperforms existing PNR detectors in terms of simplicity, sensitivity, speed, and multiplication noise.
|
|
|
|
Zhang, Z., Zhang, J., Wu, L., Zhang, Y., Zhao, Y., & Su, J. (2013). Photon-counting chirped amplitude modulation lidar using a smart premixing method. Opt. Lett., 38(21), 4389–4392.
Abstract: We proposed a new premixing method for photon-counting chirped amplitude modulation lidar (PCCAML). Earlier studies used the counting results of the returned signal detected by a Geiger mode avalanche photodiode detector (Gm-APD) to mix with the reference signal, called the postmixing method. We use an alternative method known as the premixing method, in which the reference signal is used to directly modulate the sampling gate width of the Gm-APD, and the mixing of the returned signal and the reference signal is completed before the Gm-APD. This premixing method is more flexible and may perform better than the postmixing method in terms of signal-to-noise ratio by cutting down a separated mixer commonly used in the postmixing lidar system. Furthermore, this premixing method lowers the demand for the sampling frequency of the Gm-APD. It allows the use of a much wider modulation bandwidth to improve the range accuracy and resolution. To the best of our knowledge, this is the first report to use the premixing method in the PCCAML system, which will benefit future lidar applications.
|
|
|
|
Gershenzon, E. M., Gogidze, I. G., Goltsman, G. N., Semenov, A. D., & Sergeev, A. V. (1991). Picosecond response on optical-range emission in thin YBaCuO films. Pisma v Zhurnal Tekhnicheskoi Fiziki, 17(22), 6–10.
Abstract: Целью настоящей работы является целенаправленный поиск пико-секундного отклика на оптическое излучение выяснение оптимальных условий его наблюдения, а также сравнение характеристик неравновесных эффектов в оптическом и субмиллиметровом диапазонах.
|
|
|
|
Seliverstov, S., Maslennikov, S., Ryabchun, S., Finkel, M., Klapwijk, T. M., Kaurova, N., et al. (2015). Fast and sensitive terahertz direct detector based on superconducting antenna-coupled hot electron bolometer. IEEE Trans. Appl. Supercond., 25(3), 2300304.
Abstract: We characterize superconducting antenna-coupled hot-electron bolometers for direct detection of terahertz radiation operating at a temperature of 9.0 K. The estimated value of responsivity obtained from lumped-element theory is strongly different from the measured one. A numerical calculation of the detector responsivity is developed, using the Euler method, applied to the system of heat balance equations written in recurrent form. This distributed element model takes into account the effect of nonuniform heating of the detector along its length and provides results that are in better agreement with the experiment. At a signal frequency of 2.5 THz, the measured value of the optical detector noise equivalent power is 2.0 × 10-13 W · Hz-0.5. The value of the bolometer time constant is 35 ps. The corresponding energy resolution is about 3 aJ. This detector has a sensitivity similar to that of the state-of-the-art sub-millimeter detectors operating at accessible cryogenic temperatures, but with a response time several orders of magnitude shorter.
|
|
|
|
Zhang, W., Miao, W., Li, S. L., Zhou, K. M., Shi, S. C., Gao, J. R., et al. (2013). Measurement of the spectral response of spiral-antenna coupled superconducting hot electron bolometers. IEEE Trans. Appl. Supercond., 23(3), 2300804.
Abstract: Measured spectral response of spiral-antenna coupled superconducting hot electron bolometers (HEBs) often drops dramatically at frequencies that are still within the frequency range of interest (e.g., ~ 5 THz). This is inconsistent with the implied low receiver noise temperatures from the same measurements. To understand this discrepancy, we exhaustively test and calibrate the thermal sources used in Fourier transform spectrometer measurements. We first investigate the absolute emission spectrum of high-pressure Hg arc lamp, then measure the spectral response of two spiral-antenna coupled NbN HEBs with a Martin-Puplett interferometer as spectrometer and 77 K blackbody as broadband signal source. The measured absolute emission spectrum of Hg arc lamp is proportional to frequency, corresponding to an equivalent blackbody temperature of 4000 K at 1 THz, 1500 K at 3 THz, and 800 K at 5 THz, respectively. Measured spectral response of spiral-antenna coupled NbN HEBs, corrected for air absorption, is nearly flat in the frequency range of 0.5-4 THz, consistent with simulated coupling efficiency between HEB and spiral-antenna. These results explain the discrepancy, and prove that spiral-antenna coupled superconducting NbN HEBs work well in a wide frequency range. In addition, this calibration method and these results are broadly applicable to other quasi-optical THz receivers.
|
|
|
|
Danerud, M., Winkler, D., Lindgren, M., Zorin, M., Trifonov, V., Karasik, B. S., et al. (1994). Nonequilibrium and bolometric photoresponse in patterned YBa2Cu3O7−δ thin films. J. Appl. Phys., 76(3), 1902–1909.
Abstract: Epitaxial laser deposited YBa2Cu3O7−δ films of ∼50 nm thickness were patterned into detectors consisting of ten parallel 1 μm wide strips in order to study nonequilibrium and bolometric effects. Typically, the patterned samples had critical temperatures around 86 K, transition widths around 2 K and critical current densities above 1×106A/cm2 at 77 K. Pulsed laser measurements at 0.8 μm wavelength (17 ps full width at half maximum) showed a ∼30 ps response, attributed to electron heating, followed by a slower bolometric decay. Amplitude modulation in the band fmod=100 kHz–10 GHz of a laser with wavelength λ=0.8 μm showed two different thermal relaxations in the photoresponse. Phonon escape from the film (∼3 ns) is the limiting process, followed by heat diffusion in the substrate. Similar relaxations were also seen for λ=10.6 μm. The photoresponse measurements were made with the film in the resistive state and extended into the normal state. These states were created by supercritical bias currents. Measurements between 75 and 95 K (i.e., from below to above Tc) showed that the photoresponse was proportional to dR/dT for fmod=1 MHz and 4 GHz. The fast response is limited by the electron‐phonon scattering time, estimated to 1.8 ps from experimental data. The responsivity both at 0.8 and 10.6 μm wavelength was ∼1.2 V/W at fmod=1 GHz and the noise equivalent power was calculated to 1.5×10−9 WHz−1/2 for the fast response.
|
|
|
|
Arams, F., Allen, C., Peyton, B., & Sard, E. (1966). Millimeter mixing and detection in bulk InSb. In Proc. IEEE (Vol. 54, pp. 612–622).
|
|
|
|
Korneeva, Y., Florya, I., Vdovichev, S., Moshkova, M., Simonov, N., Kaurova, N., et al. (2017). Comparison of hot-spot formation in NbN and MoN thin superconducting films after photon absorption. In IEEE Transactions on Applied Superconductivity (Vol. 27, 5).
Abstract: In superconducting single-photon detectors SSPD
the efficiency of local suppression of superconductivity and hotspot
formation is controlled by diffusivity and electron-phonon
interaction time. Here we selected a material, 3.6-nm-thick MoNx
film, which features diffusivity close to those of NbN traditionally
used for SSPD fabrication, but with electron-phonon interaction
time an order of magnitude larger. In MoNx detectors we study
the dependence of detection efficiency on bias current, photon
energy, and strip width and compare it with NbN SSPD. We
observe non-linear current-energy dependence in MoNx SSPD
and more pronounced plateaus in dependences of detection
efficiency on bias current which we attribute to longer electronphonon
interaction time.
|
|