Semenov, A. D., Gousev, Y. P., Nebosis, R. S., Renk, K. F., Yagoubov, P., Voronov, B. M., et al. (1996). Heterodyne detection of THz radiation with a superconducting hot‐electron bolometer mixer. Appl. Phys. Lett., 69(2), 260–262.
Abstract: We report on the use of a superconducting hot‐electron bolometer mixer for heterodyne detection of terahertz radiation. Radiation with a wavelength of 119 μm was coupled to the mixer, a NbN microbridge, by a hybrid quasioptical antenna consisting of an extended hyperhemispherical lens and a planar logarithmic spiral antenna. We found, at an intermediate frequency of 1.5 GHz, a system double side band noise temperature of ≊40 000 K and conversion losses of 25 dB. We also discuss the possibilities of further improvement of the mixer performance.
|
Yagoubov, P., Gol'tsman, G., Voronov, B., Svechnikov, S., Cherednichenko, S., Gershenzon, E., et al. (1996). Quasioptical phonon-cooled NbN hot-electron bolometer mixer at THz frequencies. In Proc. 7th Int. Symp. Space Terahertz Technol. (pp. 303–317).
Abstract: In our experiments we tested phonon-cooled hot-electron bolometer (HEB) quasioptical mixer based on spiral antenna designed for 0.5-1.2 THz frequency band and fabricated on sapphire, Si-coated sapphire and high resistivity silicon substrates. HEB devices were produced from thin superconducting NbN film 3.5-6 nm thick with the critical temperature of about 11-12 K. For these devices we achieved the receiver noise temperature T R (DSB) = 3000 K in the 500-700 GHz frequency range and an IF bandwidth of 3-4 GHz. Prelimanary measurements at frequencies 1-1.2 THz resulted the receiver noise temperature about 9000 K (DSB).
|
Gerecht, E., Musante, C. F., Wang, Z., Yngvesson, K. S., Mueller, E. R., Waldman, J., et al. (1996). Optimization of hot eleciron bolometer mixing efficiency in NbN at 119 micrometer wavelength. In Proc. 7th Int. Symp. Space Terahertz Technol. (pp. 584–600).
Abstract: We describe an investigation of a NbN HEB mixer for 2.5 THz. An intrinsic conversion loss of 23 dB has been measured with a two-laser measurement technique. The conversion loss was limited by the LO power available and is expected to decrease to 10 dB or less when sufficient LO power is available. For this initial experiment we used a prototype device which is directly coupled to the laser beams. We present results for a back-short technique that improves the optical coupling to the device and describe our progress for an antenna-coupled device with a smaller dimension. Based on our measured data for conversion loss and device output noise level, we predict that NbN HEB mixers will be capable of achieving DSB receiver noise temperatures of ten times the quantum noise limit in the THz range.
|
Karasik, B. S., Gol'tsman, G. N., Voronov, B. M., Svechnikov, S. I., Gershenzon, E. M., Ekstrom, H., et al. (1995). Hot electron quasioptical NbN superconducting mixer. IEEE Trans. Appl. Supercond., 5(2), 2232–2235.
Abstract: Hot electron superconductor mixer devices made of thin NbN films on SiO/sub 2/-Si/sub 3/N/sub 4/-Si membrane have been fabricated for 300-350 GHz operation. The device consists of 5-10 parallel strips each 5 /spl mu/m long by 1 /spl mu/m wide which are coupled to a tapered slot-line antenna. The I-V characteristics and position of optimum bias point were studied in the temperature range 4.5-8 K. The performance of the mixer at higher temperatures is closer to that predicted by theory for uniform electron heating. The intermediate frequency bandwidth versus bias has also been investigated. At the operating temperature 4.2 K a bandwidth as wide as 0.8 GHz has been measured for a mixer made of 6 nm thick film. The bandwidth tends to increase with operating temperature. The performance of the NbN mixer is expected to be better for higher frequencies where the absorption of radiation should be more uniform.
|
Okunev, 0., Dzardranov, A., Gol'tsman, G., & Gershenzon, E. (1995). Performances of hot—electron superconducting mixer for frequencies less than the gap energy: NbN mixer for 100 GHz operation. In Proc. 6th Int. Symp. Space Terahertz Technol. (pp. 247–253).
Abstract: The possibilities to improve the parameters of the 100 GHz NbN HEB superconducting waveguide mixers have been studied. The device consists of a signal strip 1 gm wide by 2 Am long made of 40 A thick NbN film. The best operation point was found at 5 K, where the mixer bandwidth made up 1.5-2 GHz and the total loss diminished down to 8 dB. The critical current density has been increased up to " 40 6 A/cm 2 , the noise temperature of the receiver (DSB) has reduced down to 450 K and the local oscillator power has decreased down to -.4).1 mcV.
|
Kawamura, J., Blundell, R., Tong, C. - Y. E., Gol'tsman, G., Gershenzon, E., & Voronov, B. (1995). NbN hot-electron mixer measurements at 200 GHz. In Proc. 6th Int. Symp. Space Terahertz Technol. (pp. 254–261).
Abstract: We present noise and gain measurements of resistively driven NbN hot-electron mixers near 200 GHz. The device geometry is chosen so that the dominant cooling process of the hot-electrons is their interaction with the lattice. Except for a single batch, the intermediate frequency cut-off of these mixer elements is – 3 700 MHz, and has shown little variation among other batches of devices. At 100 MHz we measured intrinsic mixer losses as low as —3 dB. We measured the noise temperatures at several intermediate frequencies, and for the best de- vice at 137 MHz with 20 MHz bandwidth, we measured 2000 K; using a low-noise first- stage amplifier at 1.5 GHz with 200 MHz bandwidth, the receiver noise temperature measured 2800 K. We estimate that the noise contribution from the mixer is 500 K and the total losses are —15 dB at 137 MHz.
|
Ekström, H., Karasik, B., Kollberg, E., Gol'tsman, G., & Gershenzon, E. (1995). 350 GHz NbN hot electron bolometer mixer. In Proc. 6th Int. Symp. Space Terahertz Technol. (pp. 269–283).
Abstract: Superconducting NbN hot-electron bolometer (HEB) mixer devices have been fabricated and measured at 350 GHz. The HEB is integrated with a double dipole antenna on an extended crystalline quartz hyper hemispherical substrate lens. Heterodyne measurement gave a -3 dB bandwidth, mainly determined by the electron- phonon interaction time, of about 680 and 1000 MHz for two different films with Tc = 8.5 and 11 K respectively. The measured DSB receiver noise temperature is around 3000 K at 800 MHz IF frequency. The main contribution to the output noise from the device is due to electron temperature fluctuations with the equivalent output noise temperature TFL-100 K. TH, has the same frequency dependence as the IF response. The contribution from Johnson noise is of the order of T. The RF coupling loss is estimated to be = 6 dB. The film with lower Tc, had an estimated intrinsic low-frequency conversion loss = 7 dB, while the other film had a conversion loss as high as 14 dB. The difference in intrinsic conversion loss is explained by less uniform absorption of radiation. Measurements of the small signal impedance shows a transition of the output impedance from the DC differential resistance Rd=dV/dI in the low frequency limit to the DC resistance R 0 =Uoff 0 in the bias point for frequencies above 3 GHz. We judge that the optimum shape of the IV-characteristic is more easily obtained at THz frequencies where the main restriction in performance should come from problems with the RF coupling.
|
Gol'tsman, G., Jacobsson, S., Ekstrom, H., Karasik, B., Kollberg, E., & Gershenzon, E. (1994). Slot-line tapered antenna with NbN hot electron mixer for 300-360 GHz operation. In Proc. 5th Int. Symp. Space Terahertz Technol. (pp. 209–213a).
Abstract: NbN hot-electron mixers combined with slot-line tapered antennas on Si wdnitride membranes had been fabricated. Several strips of 1 gm wide and 5 tan long made from 100 A NbN film are inserted into the slot antenna. IV-curves under local oscillator power in 300-350 GHz frequency range and conversion gain dependencies on intermediate fre- quency in the 0.1-1 GHz range are measured and compared with that for 100 GHz frequency band. Our results show that pumped IV-curves and intermediate frequency bands are different for 100 GHz and 300 GHz frequency ranges. The interpretation exploits the fact that for the lowest radiation frequency the superconducting energy gap is larger than the radiation quantum energy while they are comparable at the higher frequency. Tha results show that such mixers have good perspectives for terahertz receiving technology.
|
Il'in, K. S., Lindgren, M., Currie, M. A., Semenov, D., Gol'tsman, G. N., Sobolewski, R., et al. (2000). Picosecond hot-electron energy relaxation in NbN superconducting photodetectors. Appl. Phys. Lett., 76(19), 2752–2754.
Abstract: We report time-resolved characterization of superconducting NbN hot-electron photodetectors using an electro-optic sampling method. Our samples were patterned into micron-size microbridges from 3.5-nm-thick NbN films deposited on sapphire substrates. The devices were illuminated with 100 fs optical pulses, and the photoresponse was measured in the ambient temperature range between 2.15 and 10.6 K (superconducting temperature transition TC). The experimental data agreed very well with the nonequilibrium hot-electron, two-temperature model. The quasiparticle thermalization time was ambient temperature independent and was measured to be 6.5 ps. The inelastic electron–phonon scattering time Ï„e–ph tended to decrease with the temperature increase, although its change remained within the experimental error, while the phonon escape time Ï„es decreased almost by a factor of two when the sample was put in direct contact with superfluid helium. Specifically, Ï„e–ph and Ï„es, fitted by the two-temperature model, were equal to 11.6 and 21 ps at 2.15 K, and 10(±2) and 38 ps at 10.5 K, respectively. The obtained value of Ï„e–ph shows that the maximum intermediate frequency bandwidth of NbN hot-electron phonon-cooled mixers operating at TC can reach 16(+4/–3) GHz if one eliminates the bolometric phonon-heating effect.
|
Gol'tsman, G. N., Semenov, A. D., Gousev, Y. P., Zorin, M. A., Gogidze, I. G., Gershenzon, E. M., et al. (1991). Sensitive picosecond NbN detector for radiation from millimetre wavelengths to visible light. Supercond. Sci. Technol., 4(9), 453–456.
Abstract: The authors report on the application of a broad-band NbN film detector which has high sensitivity and picosecond response time for detection of radiation from millimetre wavelengths to visible light. From a study of amplitude modulated radiation of backward-wave tubes and picosecond pulses from gas and solid state lasers at wavelengths between 2 mm and 0.53 mu m, they found a detectivity of 1010 W-1 cm Hz-1/2 and a response time of less than 50 ps at T=10 K. The characteristics were provided by using a 150 AA thick NbN film patterned into a structure of micron strips. According to the proposed detection mechanism, namely electron heating, they expect an intrinsic response time of approximately 20 ps at the same temperature.
|
Voronov, B. M., Gershenzon, E. M., Gol'tsman, G. N., Gogidze, I. G., Gusev, Y. P., Zorin, M. A., et al. (1992). Picosecond range detector base on superconducting niobium nitride film sensitive to radiation in spectral range from millimeter waves up to visible light. Sverkhprovodimost': Fizika, Khimiya, Tekhnika, 5(5), 955–960.
Abstract: Fast-operating picosecond detector of electromagnetical radiation is developed on the basis of fine superconducting film of niobium nitride with high sensitivity within spectral range from millimetric waves up to visible light. Detector sensitive element represents structure covering narrow parallel strips with micron sizes included in the rupture of microstrip line. Detecting ability of the detector and time constant measured using amplitude-simulated radiation of reverse wave tubes and pulse radiation of picosecond gas and solid-body lasers, constitute D*≅1010 W-1·cm·Hz-1/2 and τ≤5 ps respectively, at 10 K temperature. The expected value of time constant of the detector at 10 K obtained via extrapolation of directly measured dependence that is, τ ∝ τ-1, constitutes 20 ps. Experimental data demonstrate that detection mechanism is linked with electron heating effect.
|
Gousev, Y. P., Gol'tsman, G. N., Semenov, A. D., Gershenzon, E. M., Nebosis, R. S., Heusinger, M. A., et al. (1994). Broadband ultrafast superconducting NbN detector for electromagnetic radiation. J. Appl. Phys., 75(7), 3695–3697.
Abstract: An ultrafast detector that is sensitive to radiation in a broad spectral range from submillimeter waves to visible light is reported. It consists of a structured NbN thin film cooled to a temperature below Tc (∼11 K). Using 20 ps pulses of a GaAs laser, we observed signal pulses with both rise and decay time of about 50 ps. From the analysis of a mixing experiment with submillimeter radiation we estimate an intrinsic response time of the detector of ∼12 ps. The sensitivity was found to be similar for the near‐infrared and submillimeter radiation. Broadband sensitivity and short response time are attributed to a quasiparticle heating effect.
|
Gousev, Y. P., Gol'tsman, G. N., Karasik, B. S., Gershenzon, E. M., Semenov, A. D., Barowski, H. S., et al. (1996). Quasioptical superconducting hot electron bolometer for submillmeter waves. Int. J. of Infrared and Millimeter Waves, 17(2), 317–331.
Abstract: We report on a superconducting hot electron bolometer coupled to radiation via a broadband antenna. The bolometer, a structured NbN film, was patterned on a thin dielectric membrane between terminals of a gold slotline antenna. We investigated the response to submillimeter radiation (wave-lengths ∼ 0.1 mm to 0.7 mm) in the fundamental Gaussian mode. We found that the directivity of the antenna was constant within a factor of 2.5 through the whole experimental range. The noise equivalent power of the bolometer at 119 µm was ∼ 3 · 10−13 W/Hz1/2; a time constant of ∼ 160 ps was estimated.
|
Voronov, B. M., Gershenzon, E. M., Gol'tsman, G. N., Gubkina, T. O., & Semash, V. D. (1994). Superconductive properties of ultrathin NbN films on different substrates. Sverkhprovodimost': Fizika, Khimiya, Tekhnika, 7(6), 1097–1102.
Abstract: A study was made on dependence of surface resistance, critical temperature and width of superconducting transition on application temperature and thickness of NbN films, which varied within the range of 3-10 nm. Plates of sapphire, fused and monocrystalline quartz, MgO, as well as Si and silicon oxide were used as substrates. NbN films with 160 μθ·cm specific resistance and 16.5 K (Tc) critical temperature were obtained on sapphire substrates. Intensive growth of ΔTc was noted for films, applied on fused quartz, with increase of precipitation temperature. This is explained by occurrence of high tensile stresses in NbN films, caused by sufficient difference of thermal coefficients of expansion of NbN and quartz.
|
Gousev, Y. P., Semenov, A. D., Gol'tsman, G. N., Sergeev, A. V., & Gershenzon, E. M. (1994). Electron-phonon interaction in disordered NbN films. Phys. B Condens. Mat., 194-196, 1355–1356.
Abstract: Electron-phonon interaction time has been investigated in disordered films of NbN. A temperatures below 5.5 K tau_eph ~ T -1"6 which is attributed to the renormalisation of phonon spectrum in thin films.
|