Yagoubov, P., Gol'tsman, G., Voronov, B., Svechnikov, S., Cherednichenko, S., Gershenzon, E., et al. (1996). Quasioptical phonon-cooled NbN hot-electron bolometer mixer at THz frequencies. In Proc. 7th Int. Symp. Space Terahertz Technol. (pp. 303–317).
Abstract: In our experiments we tested phonon-cooled hot-electron bolometer (HEB) quasioptical mixer based on spiral antenna designed for 0.5-1.2 THz frequency band and fabricated on sapphire, Si-coated sapphire and high resistivity silicon substrates. HEB devices were produced from thin superconducting NbN film 3.5-6 nm thick with the critical temperature of about 11-12 K. For these devices we achieved the receiver noise temperature T R (DSB) = 3000 K in the 500-700 GHz frequency range and an IF bandwidth of 3-4 GHz. Prelimanary measurements at frequencies 1-1.2 THz resulted the receiver noise temperature about 9000 K (DSB).
|
Gerecht, E., Musante, C. F., Wang, Z., Yngvesson, K. S., Mueller, E. R., Waldman, J., et al. (1996). Optimization of hot eleciron bolometer mixing efficiency in NbN at 119 micrometer wavelength. In Proc. 7th Int. Symp. Space Terahertz Technol. (pp. 584–600).
Abstract: We describe an investigation of a NbN HEB mixer for 2.5 THz. An intrinsic conversion loss of 23 dB has been measured with a two-laser measurement technique. The conversion loss was limited by the LO power available and is expected to decrease to 10 dB or less when sufficient LO power is available. For this initial experiment we used a prototype device which is directly coupled to the laser beams. We present results for a back-short technique that improves the optical coupling to the device and describe our progress for an antenna-coupled device with a smaller dimension. Based on our measured data for conversion loss and device output noise level, we predict that NbN HEB mixers will be capable of achieving DSB receiver noise temperatures of ten times the quantum noise limit in the THz range.
|
Karasik, B. S., Gol'tsman, G. N., Voronov, B. M., Svechnikov, S. I., Gershenzon, E. M., Ekstrom, H., et al. (1995). Hot electron quasioptical NbN superconducting mixer. IEEE Trans. Appl. Supercond., 5(2), 2232–2235.
Abstract: Hot electron superconductor mixer devices made of thin NbN films on SiO/sub 2/-Si/sub 3/N/sub 4/-Si membrane have been fabricated for 300-350 GHz operation. The device consists of 5-10 parallel strips each 5 /spl mu/m long by 1 /spl mu/m wide which are coupled to a tapered slot-line antenna. The I-V characteristics and position of optimum bias point were studied in the temperature range 4.5-8 K. The performance of the mixer at higher temperatures is closer to that predicted by theory for uniform electron heating. The intermediate frequency bandwidth versus bias has also been investigated. At the operating temperature 4.2 K a bandwidth as wide as 0.8 GHz has been measured for a mixer made of 6 nm thick film. The bandwidth tends to increase with operating temperature. The performance of the NbN mixer is expected to be better for higher frequencies where the absorption of radiation should be more uniform.
|
Okunev, 0., Dzardranov, A., Gol'tsman, G., & Gershenzon, E. (1995). Performances of hot—electron superconducting mixer for frequencies less than the gap energy: NbN mixer for 100 GHz operation. In Proc. 6th Int. Symp. Space Terahertz Technol. (pp. 247–253).
Abstract: The possibilities to improve the parameters of the 100 GHz NbN HEB superconducting waveguide mixers have been studied. The device consists of a signal strip 1 gm wide by 2 Am long made of 40 A thick NbN film. The best operation point was found at 5 K, where the mixer bandwidth made up 1.5-2 GHz and the total loss diminished down to 8 dB. The critical current density has been increased up to " 40 6 A/cm 2 , the noise temperature of the receiver (DSB) has reduced down to 450 K and the local oscillator power has decreased down to -.4).1 mcV.
|
Kawamura, J., Blundell, R., Tong, C. - Y. E., Gol'tsman, G., Gershenzon, E., & Voronov, B. (1995). NbN hot-electron mixer measurements at 200 GHz. In Proc. 6th Int. Symp. Space Terahertz Technol. (pp. 254–261).
Abstract: We present noise and gain measurements of resistively driven NbN hot-electron mixers near 200 GHz. The device geometry is chosen so that the dominant cooling process of the hot-electrons is their interaction with the lattice. Except for a single batch, the intermediate frequency cut-off of these mixer elements is – 3 700 MHz, and has shown little variation among other batches of devices. At 100 MHz we measured intrinsic mixer losses as low as —3 dB. We measured the noise temperatures at several intermediate frequencies, and for the best de- vice at 137 MHz with 20 MHz bandwidth, we measured 2000 K; using a low-noise first- stage amplifier at 1.5 GHz with 200 MHz bandwidth, the receiver noise temperature measured 2800 K. We estimate that the noise contribution from the mixer is 500 K and the total losses are —15 dB at 137 MHz.
|
Ekström, H., Karasik, B., Kollberg, E., Gol'tsman, G., & Gershenzon, E. (1995). 350 GHz NbN hot electron bolometer mixer. In Proc. 6th Int. Symp. Space Terahertz Technol. (pp. 269–283).
Abstract: Superconducting NbN hot-electron bolometer (HEB) mixer devices have been fabricated and measured at 350 GHz. The HEB is integrated with a double dipole antenna on an extended crystalline quartz hyper hemispherical substrate lens. Heterodyne measurement gave a -3 dB bandwidth, mainly determined by the electron- phonon interaction time, of about 680 and 1000 MHz for two different films with Tc = 8.5 and 11 K respectively. The measured DSB receiver noise temperature is around 3000 K at 800 MHz IF frequency. The main contribution to the output noise from the device is due to electron temperature fluctuations with the equivalent output noise temperature TFL-100 K. TH, has the same frequency dependence as the IF response. The contribution from Johnson noise is of the order of T. The RF coupling loss is estimated to be = 6 dB. The film with lower Tc, had an estimated intrinsic low-frequency conversion loss = 7 dB, while the other film had a conversion loss as high as 14 dB. The difference in intrinsic conversion loss is explained by less uniform absorption of radiation. Measurements of the small signal impedance shows a transition of the output impedance from the DC differential resistance Rd=dV/dI in the low frequency limit to the DC resistance R 0 =Uoff 0 in the bias point for frequencies above 3 GHz. We judge that the optimum shape of the IV-characteristic is more easily obtained at THz frequencies where the main restriction in performance should come from problems with the RF coupling.
|
Gol'tsman, G., Jacobsson, S., Ekstrom, H., Karasik, B., Kollberg, E., & Gershenzon, E. (1994). Slot-line tapered antenna with NbN hot electron mixer for 300-360 GHz operation. In Proc. 5th Int. Symp. Space Terahertz Technol. (pp. 209–213a).
Abstract: NbN hot-electron mixers combined with slot-line tapered antennas on Si wdnitride membranes had been fabricated. Several strips of 1 gm wide and 5 tan long made from 100 A NbN film are inserted into the slot antenna. IV-curves under local oscillator power in 300-350 GHz frequency range and conversion gain dependencies on intermediate fre- quency in the 0.1-1 GHz range are measured and compared with that for 100 GHz frequency band. Our results show that pumped IV-curves and intermediate frequency bands are different for 100 GHz and 300 GHz frequency ranges. The interpretation exploits the fact that for the lowest radiation frequency the superconducting energy gap is larger than the radiation quantum energy while they are comparable at the higher frequency. Tha results show that such mixers have good perspectives for terahertz receiving technology.
|
Huebers, H. - W., Semenov, A., Schubert, J., Gol’tsman, G. N., Voronov, B. M., Gershenzon, E. M., et al. (2000). NbN hot-electron bolometer as THz mixer for SOFIA. In R. K. Melugin, & H. - P. Roeser (Eds.), Proc. SPIE (Vol. 4014, pp. 195–202). SPIE.
Abstract: Heterodyne receivers for applications in astronomy need quantum limited sensitivity. We have investigated phonon- cooled NbN hot electron bolometric mixers in the frequency range from 0.7 THz to 5.2 THz. The devices were 3.5 nm thin films with an in-plane dimension of 1.7 X 0.2 micrometers 2 integrated in a complementary logarithmic spiral antenna. The best measured DSB receiver noise temperatures are 1300 K (0.7 THz), 2000 K (1.4 THz), 2100 K (1.6 THz), 2600 K (2.5 THz), 4000 K (3.1 THz), 5600 K (4.3 THz), and 8800 K (5.2 THz). The sensitivity fluctuation, the long term stability, and the antenna pattern were measured. The results demonstrate that this mixer is very well suited for GREAT, the German heterodyne receiver for SOFIA.
|
Hübers, H. - W., Schubert, J., Krabbe, A., Birk, M., Wagner, G., Semenov, A., et al. (2001). Parylene anti-reflection coating of a quasi-optical hot-electron-bolometric mixer at terahertz frequencies. Infrared Physics & Technology, 42(1), 41–47.
Abstract: Parylene C was investigated as anti-reflection coating for silicon at terahertz frequencies. Measurements with a Fourier-transform spectrometer show that the transmittance of pure silicon can be improved by about 30% when applying a layer of Parylene C with a quarter wavelength optical thickness. The 10% bandwidth of this coating extends from 1.5 to 3 THz for a center frequency of 2.3–2.5 THz, where the transmittance is constant. Heterodyne measurements demonstrate that the noise temperature of a hot-electron-bolometric mixer can be reduced significantly by coating the silicon lens of the hybrid antenna with a quarter wavelength Parylene C layer. Compared to the same mixer with an uncoated lens the improvement is about 30% at a frequency of 2.5 THz.
|
Ekstörm, H., Kollberg, E., Yagoubov, P., Gol'tsman, G., Gershenzon, E., & Yngvesson, S. (1997). Gain and noise bandwidth of NbN hot-electron bolometric mixers. Appl. Phys. Lett., 70(24), 3296–3298.
Abstract: We have measured the noise performance and gain bandwidth of 35 Å thin NbN hot-electron mixers integrated with spiral antennas on silicon substrate lenses at 620 GHz. The best double-sideband receiver noise temperature is less than 1300 K with a 3 dB bandwidth of ≈5 GHz. The gain bandwidth is 3.2 GHz. The mixer output noise dominated by thermal fluctuations is 50 K, and the intrinsic conversion gain is about −12 dB. Without mismatch losses and excluding the loss from the beamsplitter, we expect to achieve a receiver noise temperature of less than 700 K.
|
Gerecht, E., Musante, C. F., Schuch, R., Lutz, C. R., Jr., Yngvesson, K. S., et al. (1995). Hot electron detection and mixing experiments in NbN at 119 micrometer wavelength. In Proc. 6th Int. Symp. Space Terahertz Technol. (pp. 284–293).
Abstract: We have performed preliminary experiments with the goal of demonstrating a Hot Electron Bolometric (HEB) mixer for a 119 micrometer wavelength (2.5 THz). We have chosen a NbN device of size 700 x 350 micrometers. This device can easily be coupled to a laser LO source, which is advantageous for performing a prototype experiment. The relatively large size of the device means that the LO power required is in the mW range; this power can be easily obtained from a THz laser source. We have measured the amount of laser power actually absorbed in the device, and from this have estimated the best optical coupling loss to be about 10 di . We are developing methods for improving the optical coupling further. Preliminary measurements of the response of the device to a chopped black-body have not yet resulted in a measured receiver noise temperature. We expect to be able to complete this measurement in the near future.
|
Yagubov, P., Gol'tsman, G., Voronov, B., Seidman, L., Siomash, V., Cherednichenko, S., et al. (1996). The bandwidth of HEB mixers employing ultrathin NbN films on sapphire substrate. In Proc. 7th Int. Symp. Space Terahertz Technol. (pp. 290–302). Charlottesville, Virginia, USA.
Abstract: We report on some unusual features observed during fabrication of ultrathin NbN films with high Tc. The films were used to fabricate HEB mixers, which were evaluated for IF bandwidth measurements at 140 GHz. Ultrathin films were fabricated using reactive dc magnetron sputtering with a discharge current source. Reproducible parameters of the films are assured keeping constant the difference between the discharge voltage in pure argon, and in a gas mixture, for the same current. A maximum bandwidth of 4 GHz at optimal LO and dc bias was obtained for mixer chip based on NbN film 35 A thick with Tc = 11 K.
|
Cherednichenko, S., Yagoubov, P., Il'In, K., Gol'tsman, G., & Gershenzon, E. (1997). Large bandwidth of NbN phonon-cooled hot-electron bolometer mixers on sapphire substrates. In Proc. 8th Int. Symp. Space Terahertz Technol. (pp. 245–257).
Abstract: The bandwidth of NbN phonon-cooled hot electron bolometer mixers has been systematically investigated with respect to the film thickness and film quality variation. The films, 2.5 to 10 mm thick, were fabricated on sapphire substrates using DC reactive magnetron sputtering. All devices consisted of several parallel strips, each 1 1.1 wide and 211 long, placed between Ti-Au contact pads. To measure the gain bandwidth we used two identical BWOs operating in the 120-140 GHz frequency range, one functioning as a local oscillator and the other as a signal source. The majority of the measurements were made at an ambient temperature of 4.5 K with optimal LO and DC bias. The maximum 3 dB bandwidth (about 4 GHz) was achieved for the devices made of films which were 2.5-3.5 nm thick, had a high critical temperature, and high critical current density. A theoretical analysis of bandwidth for these mixers based on the two-temperature model gives a good description of the experimental results if one assumes that the electron temperature is equal to the critical temperature.
|
Cherednichenko, S., Kroug, M., Merkel, H., Kollberg, E., Loudkov, D., Smirnov, K., et al. (2001). Local oscillator power requirement and saturation effects in NbN HEB mixers. In C. Iit.u.t.e of T. Jet Propulsion Laboratory (Ed.), Proc. 12th Int. Symp. Space Terahertz Technol. (pp. 273–285). San Diego, CA, USA.
Abstract: The local oscillator power required for NbN hot-electron bolometric mixers (P LO ) was investigated with respect to mixer size, critical temperature and ambient temperature. P LO can be decreased by a factor of 10 as the mixer size decreases from 4×0.4 µm 2 to 0.6×0.13 µm 2 . For the smallest volume mixer the optimal local oscillator power was found to be 15 nW. We found that for such mixer no signal compression was observed up to an input signal of 2 nW which corresponds to an equivalent input load of 20,000 K. For a constant mixer volume, reduction of T c can decrease optimal local oscillator power at least by a factor of 2 without a deterioration of the receiver noise temperature. Bath temperature was found to have minor effect on the receiver characteristics.
|
Kawamura, J., Blundell, R., Tong, C. - Y. E., Papa, D. C., Hunter, T. R., Paine, S. N., et al. (2000). Superconductive hot-electron-bolometer mixer receiver for 800-GHz operation. IEEE Trans. Microw. Theory Techn., 48(4), 683–689.
Abstract: In this paper, we describe a superconductive hot-electron-bolometer mixer receiver designed to operate in the partially transmissive 350-μm atmospheric window. The receiver employs an NbN thin-film microbridge as the mixer element, in which the main cooling mechanism of the hot electrons is through electron-phonon interaction. At a local-oscillator frequency of 808 GHz, the measured double-sideband receiver noise temperature is TRX=970 K, across a 1-GHz intermediate-frequency bandwidth centered at 1.8 GHz. We have measured the linearity of the receiver and the amount of local-oscillator power incident on the mixer for optimal operation, which is PLO≈1 μW. This receiver was used in making observations as a facility instrument at the Heinrich Hertz Telescope, Mt. Graham, AZ, during the 1998-1999 winter observing season.
|