Abstract: Epitaxial laser deposited YBa2Cu3O7−δ films of ∼50 nm thickness were patterned into detectors consisting of ten parallel 1 μm wide strips in order to study nonequilibrium and bolometric effects. Typically, the patterned samples had critical temperatures around 86 K, transition widths around 2 K and critical current densities above 1×106A/cm2 at 77 K. Pulsed laser measurements at 0.8 μm wavelength (17 ps full width at half maximum) showed a ∼30 ps response, attributed to electron heating, followed by a slower bolometric decay. Amplitude modulation in the band fmod=100 kHz–10 GHz of a laser with wavelength λ=0.8 μm showed two different thermal relaxations in the photoresponse. Phonon escape from the film (∼3 ns) is the limiting process, followed by heat diffusion in the substrate. Similar relaxations were also seen for λ=10.6 μm. The photoresponse measurements were made with the film in the resistive state and extended into the normal state. These states were created by supercritical bias currents. Measurements between 75 and 95 K (i.e., from below to above Tc) showed that the photoresponse was proportional to dR/dT for fmod=1 MHz and 4 GHz. The fast response is limited by the electron‐phonon scattering time, estimated to 1.8 ps from experimental data. The responsivity both at 0.8 and 10.6 μm wavelength was ∼1.2 V/W at fmod=1 GHz and the noise equivalent power was calculated to 1.5×10−9 WHz−1/2 for the fast response.

Abstract: The time of electron-phonon interaction tau(eph) in YBaCuO films at low temperatures is studied. This is measured as the time of resistance relaxation in the resistive state of the superconducter, and is also determined from the increase in resistance under the action of radiation. Consistent results of these methods show that resistance relaxation in the resistive state is caused by cooling of the electron subsystem with respect to the phonon subsystem. The time tau(eph) is found to be inversely proportional to the temperature and comes to 80 ps when T = 1.6 K and 5 ps when T = 30 K. 6 refs.

Abstract: The authors have investigated the photoinduced voltage response of a current-carrying structured YBa₂Cu₃O_7-δ thin film to ultrashort far-infrared (FIR) laser pulses in the frequency range from 0.7 THz to 7 THz. The detector has shown an almost constant sensitivity of 1 mV/W and a noise equivalent power of less than 5*10/sup -7/ W/ square root Hz. The temperature dependence of the decay time of the detector signal was studied for temperatures around the transition temperature of the film ( approximately 80 K). For a detector temperature where dR/dT had its maximum, the authors observed bolometric signals with decay times of about 2 ns, and for lower temperatures they observed nonbolometric signals with decay times of approximately 120 ps; the duration of the nonbolometric signals was limited by the time resolution of the electronic registration equipment.

Abstract: Direct measurements of the thermal boundary resistance were performed by means of the stationary method. In this approach the temperature of an electrically heated film is controlled by its dc resistance while an additional film on the same substrate is used as a thermometer monitoring substrate temperature. The temperature field in the substrate is then calculated to deduce the Kapitza temperature step at the interface between the heated strip and the substrate. The main statement of all afore-said papers is that experimental values of the thermal boundary resistance are too large to be explained by the acoustic mismatch model. In this paper we investigate transparency of YBaCuO film/substrate interfaces for thermal phonons by means of photoresponse measurements. We show that our data are in reasonable agreement with the acoustic mismatch theory.