Abstract: The bandwidth of NbN phonon-cooled hot electron bolometer mixers has been systematically investigated with respect to the film thickness and film quality variation. The films, 2.5 to 10 nm thick, were fabricated on sapphire substrates using DC reactive magnetron sputtering. All devices consisted of several parallel strips, each 1 um wide and 2 um long, placed between Ti-Au contact pads. To measure the gain bandwidth we used two identical BWOs operating in the 120-140 GHz frequency range, one functioning as a local oscillator and the other as a signal source. The majority of the measurements were made at an ambient temperature of 4.2 K with optimal LO and DC bias. The maximum 3 dB bandwidth (about 4 GHz) was achieved for the devices made of films which were 2.5-3.5 nm thick, had a high critical temperature, and high critical current density. A theoretical analysis of bandwidth for these mixers based on the two-temperature model gives a good description of the experimental results if one assumes that the electron temperature is equal to the critical temperature.

Abstract: The thesis reports the development of Hot Electron Bolometer (HEB) mixers for radio astronomy heterodyne receivers in THz frequency range. Part of this work is the fabrication of HEB devices, which are based on NbN or NbTiN superconducting thin films (â‰<a4>5 nm). They are integrated with wideband spiral or double-slot planar antennas. The mixer chips are incorporated into a quasi-optical receiver. The experimental part of this work focuses on the characterization of the receiver as a whole, and the HEB mixers as a part. Double side band receiver noise temperature and the IF bandwidth are reported for frequencies from 0.7 THz up to 2.6 THz. The spectrum of the direct response of HEB integrated with dierent antennas are measured using Fourier Transform Spectrometer (FTS). The effect of the bolometer size on total receiver performance and the LO power requirements is also discussed. A high-yield and reliable process for fabrication of NbN HEB mixers have been achieved. Over 100 devices with different bolometer geometry, film property and also different antennas have been fabricated and measured. The measured data enables us to discuss the impact of different parameters to the receiver overall performance.
This work has provided NbN HEB mixers to the following receivers:
TREND (Terahertz REceiver with NbN HEB Device) operating at 1.25-1.5 THz, installed in AST/RO Submillimeter Wave Telescope, Amundsen/Scott South Pole Station, in 2002-2003.
Band 6-low (1.410-1.700 THz) and 6-high (1.700-1.920 THz) of the HIFI (Heterodyne Instrument for Far Infra-red) in the Herschel Space Observatory, due to launch in 2007 by ESA (European Space Agency).
Besides, there has been continuous efforts to develop better models to explain the mixer performance more accurately. They are based on two temperature model for electrons and phonons and solving one-dimensional heat balance equations along the bolometer. The principles of these models are illustrated and the calculated results are compared with measured data.

Abstract: Разработан и исследован смеситель на горячих электронах, изготовленный из двуслойной плёнки NbN-Au, осаждённой на кремневую подложку in situ. Двухполосная шумовая температура устройства составила 750 К на частоте 2.5 ТГц. Измерения эффективности преобразования для смесителя длиной 0.112 мкм вблизи температуры сверхпроводящего перехода показали полосу промежуточных частот около 6.5 ГГц. Эти результаты являются рекордными и были получены за счёт улучшения контактов между чувствительным элементом и спиральной антенной при замене технологического маршрута с нанесением слоёв NbN и Au в отдельных процессах на технологический процесс, в котором данные слои наносятся in situ без нарушения вакуума.

Abstract: Traditionally, hot-electron-bolometer (HEB) mixers are employed for THz and “super-THz” heterodyne detection. To explore the near-IR spectral range, we propose a fiber-coupled NbN film based HEB mixer. To enhance the incident-light absorption, a quasi-antenna consisting of a set of parallel stripes of gold is used. To study the antenna effect on the mixer performance, we have experimentally studied a set of devices with different size of the Au stripe and spacing between the neighboring stripes. With use of the well-known isotherm technique we have estimated the absorption efficiency of the mixer, and the maximum efficiency has been observed for devices with the smallest pitch of the alternating NbN and NbN-Au stripes. Also, a proper alignment of the incident Eâƒ<2014>-field with respect to the stripes allows us to improve the coupling further. Studying IV-characteristics of the mixer under differently-aligned Eâƒ<2014>-field of the incident radiation, we have noticed a difference in their shape. This observation suggests that a difference exists in the way the two waves with orthogonal polarizations parallel and perpendicular Eâƒ<2014>-field to the stripes heat the electrons in the HEB mixer. The latter results in a variation in the electron temperature distribution over the HEB device irradiated by the two waves.

Abstract: We present the results of noise temperature measurements of NbN phonon-cooled HEB mixers based on a 3.5 nm NbN film deposited on a high-resistivity Si substrate with a 200 nm – thick MgO buffer layer. The mixer element was integrated with a log-periodic spiral antenna. The noise temperature measurements were performed at 2.5 THz and at 3.8 THz local oscillator frequencies for the 3 µm x 0.2 µm active area devices. The best uncorrected receiver noise temperatures found for these frequencies are 1300 K and 3100 K, respectively. A water vapour discharge laser was used as the LO source. We also present the results of direct detection contribution to the measured Y-factor and of a possible error of noise temperature calculation. This error was more than 8% for the mixer with in-plane dimensions of 2.4 x 0.16 µm 2 at the optimal noise temperature point. The use of a mesh filter enabled us to avoid the effect of direct detection and decrease optical losses by 0.5 dB. The paper is concluded by the investigation results of the mixer polarization response. It was shown that the polarization can differ from the circular one at 3.8 THz by more than 2 dB.

Abstract: A systematic study of the intermediate frequency noise bandwidth of Nb thin-film superconducting hot-electron bolometers is presented. We have measured the spectrum of the output noise as well as the conversion efficiency over a very broad intermediate frequency range (from 0.1 to 7.5 GHz) for devices varying in length from 0.08 μm to 3 μm. Local oscillator and rf signals from 8 to 40 GHz were used. For a device of a given length, the spectrum of the output noise and the conversion efficiency behave similarly for intermediate frequencies less than the gain bandwidth, in accordance with a simple thermal model for both the mixing and thermal fluctuation noise. For higher intermediate frequencies the conversion efficiency decreases; in contrast, the noise decreases but has a second contribution which dominates at higher frequency. The noise bandwidth is larger than the gain bandwidth, and the mixer noise is low, between 120 and 530 K (double side band).

Abstract: A theoretical analysis for the noise temperature of hot–electron superconducting mixer has been presented. Thecontributions of both Johnson noise and electron temperature fluctuations have been evaluated. A set of criteriaensuring low noise performance of the mixer has been stated and a simple analytic expression for the noisetemperature of the mixer device has been suggested. It has been shown that an improvement of the mixer sensitivitydoes not necessarily follow by a decrease of the bandwidth. An SSB noise temperature limit due to the intrinsic noisemechanisms has been estimated to be as low as 40–90 K for a mixer device made from Nb or NbN thin film.Furthermore, the conversion gain bandwidth can be as wide as is allowed by the intrinsic electron temperaturerelaxation time if an appropriate choice of the mixer resistance has been made. The intrinsic mixer noise bandwidthis of 3 GHz for Nb device and of 5 GHz for NbN device. An additional improvement of the theory has been madewhen a distinction between the impedance measured at high intermediate frequency (larger than the mixerbandwidth) and the mixer ohmic resistance has been taken into account.Recently obtained experimental data on Nb and NbNbolometer mixer devices are viewed in connection with thetheoretical predictions.The noise temperature limit has also been specified for the mixer device where an outdiffusion coolingmechanism rather than the electron–phonon energy relaxation determines the mixer bandwidth. A consideration ofthe noise performance of a bolometer mixer made from YBaCuO film utilizing a hot–electron effect has been done.