Zolotov, P. I., Divochiy, A. V., Vakhtomin, Y. B., Lubenchenko, A. V., Morozov, P. V., Shurkaeva, I. V., et al. (2018). Influence of sputtering parameters on the main characteristics of ultra-thin vanadium nitride films. In J. Phys.: Conf. Ser. (Vol. 1124, 051030).
Abstract: We researched the relation between deposition and ultra-thin VN films parameters. To conduct the experimental study we varied substrate temperature, Ar and N2 partial pressures and deposition rate. The study allowed us to obtain the films with close to the bulk values transition temperatures and implement such samples in order to fabricate superconducting single-photon detectors.
|
Romanov, N. R., Zolotov, P. I., Vakhtomin, Y. B., Divochiy, A. V., & Smirnov, K. V. (2018). Electron diffusivity measurements of VN superconducting single-photon detectors. In J. Phys.: Conf. Ser. (Vol. 1124, 051032).
Abstract: The research of ultrathin vanadium nitride (VN) films as a promising candidate for superconducting single-photon detectors (SSPD) is presented. The electron diffusivity measurements are performed for such devices. Devices that were fabricated out from 9.9 nm films had diffusivity coefficient of 0.41 cm2/s and from 5.4 nm – 0.54 cm2/s. Obtained values are similar to other typical SSPD materials. The diffusivity that increases along with decreasing of the film thickness is expected to allow fabrication of the devices with improved characteristics. Fabricated VN SSPDs showed prominent single-photon response in the range 0.9-1.55 µm.
|
Shcheslavskiy, V., Morozov, P., Divochiy, A., Vakhtomin, Y., Smirnov, K., & Becker, W. (2016). Ultrafast time measurements by time-correlated single photon counting coupled with superconducting single photon detector. Rev. Sci. Instrum., 87, 053117 (1 to 5).
Abstract: Time resolution is one of the main characteristics of the single photon detectors besides quantum efficiency and dark count rate. We demonstrate here an ultrafast time-correlated single photon counting (TCSPC) setup consisting of a newly developed single photon counting board SPC-150NX and a superconducting NbN single photon detector with a sensitive area of 7 × 7 μm. The combination delivers a record instrument response function with a full width at half maximum of 17.8 ps and system quantum efficiency ~5% at wavelength of 1560 nm. A calculation of the root mean square value of the timing jitter for channels with counts more than 1% of the peak value yielded about 7.6 ps. The setup has also good timing stability of the detector–TCSPC board.
|
Shcheslavskiy, V., Morozov, P., Divochiy, A., Vakhtomin, Y., Smirnov, K., & Becker, W. (2016). Erratum: “Ultrafast time measurements by time-correlated single photon counting coupled with superconducting single photon detector” [Rev. Sci. Instrum. 87, 053117 (2016)] (Vol. 87).
Abstract: In the original paper1the Ref. 10 should be M. Sanzaro, N. Calandri, A. Ruggeri, C. Scarcella, G. Boso, M. Buttafava, and A. Tosi, Proc. SPIE9370, 93701T (2015).
|
Smirnov, K. V., Vachtomin, Y. B., Ozhegov, R. V., Pentin, I. V., Slivinskaya, E. V., Korneev, A. A., et al. (2008). Fiber coupled single photon receivers based on superconducting detectors for quantum communications and quantum cryptography. In P. Tománek, D. Senderáková, & M. Hrabovský (Eds.), Proc. SPIE (Vol. 7138, 713827 (1 to 6)). Spie.
Abstract: At present superconducting detectors become increasingly attractive for various practical applications. In this paper we present results on the depelopment of fiber coupled receiver systems for the registration of IR single photons, optimized for telecommunication and quantum-cryptography. These receiver systems were developed on the basis of superconducting single photon detectors (SSPD) of VIS and IR wavelength ranges. The core of the SSPD is a narrow ( 100 nm) and long ( 0,5 mm) strip in the form of a meander which is patterned from a 4-nm-thick NbN film (TC=10-11 K, jC= 5-7•106 A/cm2); the sensitive area dimensions are 10×10 μm2. The main problem to be solved while the receiver system development was optical coupling of a single-mode fiber (9 microns in diameter) with the SSPD sensitive area. Characteristics of the developed system at the optical input are as follows: quantum efficiency >10 % (at 1.3 μm), >4 % (at 1.55 μm); dark counts rate ≤1 s-1; duration of voltage pulse ≤5 ns; jitter ≤40 ps. The receiver systems have either one or two identical channels (for the case of carrying out correlation measurements) and are made as an insert in a helium storage Dewar.
|