Ryabchun, S. A., Tretyakov, I. V., Finkel, M. I., Maslennikov, S. N., Kaurova, N. S., Seleznev, V. A., et al. (2008). Fabrication and characterisation of NbN HEB mixers with in situ gold contacts. In Proc. 19th Int. Symp. Space Terahertz Technol. (pp. 62–67). Groningen, Netherlands.
Abstract: We present our recent results of the fabrication and testing of NbN hot-electron bolometer mixers with in situ gold contacts. An intermediate frequency bandwidth of about 6 GHz has been measured for the mixers made of a 3.5-nm NbN film on a plane Si substrate with in situ gold contacts, compared to 3.5 GHz for devices made of the same film with ex situ gold contacts. The increase in the intermediate frequency bandwidth is attributed to additional diffusion cooling through the improved contacts, which is further supported by the its dependence on the bridge length: intermediate frequency bandwidths of 3.5 GHz and 6 GHz have been measured for devices with lengths of 0.35 μm and 0.16 μm respectively at a local oscillator frequency of 300 GHz near the superconducting transition. At a local oscillator frequency of 2.5 THz the receiver has offered a DSB noise temperature of 950 K. When compared to the previous result of 1300 K obtained at the same local oscillator frequency for devices fabricated with an ex situ route, such a low value of the noise temperature may also be attributed to the improved gold contacts.
|
|
|
Tarkhov, M., Claudon, J., Poizat, J. P., Korneev, A., Divochiy, A., Minaeva, O., et al. (2008). Ultrafast reset time of superconducting single photon detectors. Appl. Phys. Lett., 92(24), 241112 (1 to 3).
|
|
|
Finkel, M. I., Maslennikov, S. N., Vachtomin, Y. B., Svechnikov, S. I., Smirnov, K. V., Seleznev, V. A., et al. (2005). Hot electron bolometer mixer for 20 – 40 THz frequency range. In Proc. 16th Int. Symp. Space Terahertz Technol. (pp. 393–397). Göteborg, Sweden.
Abstract: The developed HEB mixer was based on a 5 nm thick NbN film deposited on a GaAs substrate. The active area of the film was patterned as a 30×20 μm 2 strip and coupled with a 50 Ohm coplanar line deposited in situ. An extended hemispherical germanium lens was used to focus the LO radiation on the mixer. The responsivity of the mixer was measured in a direct detection mode in the 25÷64 THz frequency range. The noise performance of the mixer and the directivity of the receiver were investigated in a heterodyne mode. A 10.6 μm wavelength CW CO 2 laser was utilized as a local oscillator.
|
|
|
Korneev, A., Minaeva, O., Rubtsova, I., Milostnaya, I., Chulkova, G., Voronov, B., et al. (2005). Superconducting single-photon ultrathin NbN film detector. Quantum Electronics, 35(8), 698–700.
Abstract: Superconducting single-photon ultrathin NbN film detectors are studied. The development of manufacturing technology of detectors and the reduction of their operating temperature down to 2 K resulted in a considerable increase in their quantum efficiency, which reached in the visible region (at 0.56 μm) 30%—40%, i.e., achieved the limit determined by the absorption coefficient of the film. The quantum efficiency exponentially decreases with increasing wavelength, being equal to ~20% at 1.55 μm and ~0.02% at 5 μm. For the dark count rate of ~10-4s-1, the experimental equivalent noise power was 1.5×10-20 W Hz-1/2; it can be decreased in the future down to the record low value of 5×10-21 W Hz-1/2. The time resolution of the detector is 30 ps.
|
|
|
Smirnov, K., Korneev, A., Minaeva, O., Divochiy, A., Tarkhov, M., Ryabchun, S., et al. (2007). Ultrathin NbN film superconducting single-photon detector array. In J. Phys.: Conf. Ser. (Vol. 61, pp. 1081–1085).
Abstract: We report on the fabrication process of the 2 × 2 superconducting single-photon detector (SSPD) array. The SSPD array is made from ultrathin NbN film and is operated at liquid helium temperatures. Each detector is a nanowire-based structure patterned by electron beam lithography process. The advances in fabrication technology allowed us to produce highly uniform strips and preserve superconducting properties of the unpatterned film. SSPD exhibit up to 30% quantum efficiency in near infrared and up to 1% at 5-μm wavelength. Due to 120 MHz counting rate and 18 ps jitter, the time-domain multiplexing read-out is proposed for large scale SSPD arrays. Single-pixel SSPD has already found a practical application in non-invasive testing of semiconductor very-large scale integrated circuits. The SSPD significantly outperformed traditional single-photon counting avalanche diodes.
|
|