Svechnikov, S., Gol'tsman, G., Voronov, B., Yagoubov, P., Cherednichenko, S., Gershenzon, E., et al. (1997). Spiral antenna NbN hot-electron bolometer mixer at submm frequencies. IEEE Trans. Appl. Supercond., 7(2), 3395–3398.
Abstract: We have studied the phonon-cooled hot-electron bolometer (HEB) as a quasioptical mixer based on a spiral antenna designed for the 0.3-1 THz frequency band and fabricated on sapphire and high resistivity silicon substrates. HEB devices were produced from superconducting 3.5-5 nm thick NbN films with a critical temperature 10-12 K and a critical current density of approximately 10/sup 7/ A/cm/sup 2/ at 4.2 K. For these devices we reached a DSB receiver noise temperature below 1500 K, a total conversion loss of L/sub t/=16 dB in the 500-700 GHz frequency range, an IF bandwidth of 3-4 GHz and an optimal LO absorbed power of /spl sime/4 /spl mu/W. We experimentally analyzed various contributions to the conversion loss and obtained an RF coupling factor of about 5 dB, internal mixer loss of 10 dB and IF mismatch of 1 dB.
|
|
|
|
Semenov, A. D., Heusinger, M. A., Renk, K. F., Menschikov, E., Sergeev, A. V., Elant'ev, A. I., et al. (1997). Influence of phonon trapping on the performance of NbN kinetic inductance detectors. IEEE Trans. Appl. Supercond., 7(2), 3083–3086.
Abstract: Voltage and microwave photoresponse of NbN thin films to modulated and pulsed optical radiation reveals, far below the superconducting transition, a response time consistent with the lifetime of nonequilibrium quasiparticles. We show that even in 5 nm thick films at 4.2 K the phonon trapping is significant resulting in a quasiparticle lifetime of a few nanoseconds that is an order of magnitude larger than the recombination time. Values and temperature dependence of the quasiparticle lifetime obey the Bardeen-Cooper-Schrieffer theory and are in quantitative agreement with the electron-phonon relaxation rate determined from the resistive response near the superconducting transition. We discuss a positive effect of the phonon trapping on the performance of kinetic inductance detectors.
|
|
|
|
Kawamura, J., Blundell, R., Tong, C. -yu E., Gol’tsman, G., Gershenzon, E., Voronov, B., et al. (1997). Low noise NbN lattice-cooled superconducting hot-electron bolometric mixers at submillimeter wavelengths. Appl. Phys. Lett., 70(12), 1619–1621.
Abstract: Lattice-cooled superconducting hot-electron bolometric mixers are used in a submillimeter-wave waveguide heterodyne receiver. The mixer elements are niobium nitride film with 3.5 nm thickness and ∼10 μm2 area. The local oscillator power for optimal performance is estimated to be 0.5 μW, and the instantaneous bandwidth is 2.2 GHz. At an intermediate frequency centered at 1.4 GHz with 200 MHz bandwidth, the double sideband receiver noise temperature is 410 K at 430 GHz. The receiver has been used to detect molecular line emission in a laboratory gas cell.
|
|
|
|
Kawamura, J., Blundell, R., Tong, C. ‐yu E., Gol’tsman, G., Gershenzon, E., & Voronov, B. (1996). Performance of NbN lattice‐cooled hot‐electron bolometric mixers. J. Appl. Phys., 80(7), 4232–4234.
Abstract: The heterodyne performance of lattice‐cooled hot‐electron bolometric mixers is measured at 200 GHz. Superconducting thin‐film niobium nitride strips with ∼5 nm thickness are used as waveguide mixer elements. A double‐sideband receiver noise temperature of 750 K at 244 GHz is measured at an intermediate frequency centered at 1.5 GHz with 500 MHz bandwidth and with 4.2 K device temperature. The instantaneous bandwidth for this mixer is 1.6 GHz. The local oscillator power required by the mixer is about 0.5 μW. The mixer is linear to within 1 dB up to an input power level 6 dB below the local oscillator power. A receiver incorporating a hot‐electron bolometric mixer was used to detect molecular line emission in a laboratory gascell. This experiment unambiguously confirms that the receiver noise temperature determined from Y‐factor measurements reflects the true heterodyne sensitivity.
|
|
|
|
Verevkin, A. A., Ptitsina, N. G., Chulcova, G. M., Gol'tsman, G. N., Gershenzon, E. M., & Yngvesson, K. S. (1996). Direct measurements of energy relaxation time of electrons in AlGaAs/GaAs heterostructures under quasi-equilibrium conditions. Surface Science, 361-362, 569–573.
Abstract: For the first time, results are presented of a direct measurement of the energy relaxation time τε of 2D electrons in an AlGaAs/GaAs heterojunction at T = 1 and 5–20 K. A weak temperature dependence of τε for the T > 4K range and a linear temperature dependence of the reciprocal of τε for T < 4K have been observed. The linear dependence τε−1 ≈ T in the Bloch-Gruneisen regime is direct evidence of the predominance of the piezo-electric mechanism of electron-phonon interaction in non-elastic electron scattering processes. The values of τε in this regime are in very good agreement with the results of the Karpus theory. At higher temperatures, where the deformation-potential scattering becomes noticeable, a substantial disagreement between the experimental data and the theoretical results is observed.
|
|
|
|
Semenov, A. D., Gousev, Y. P., Nebosis, R. S., Renk, K. F., Yagoubov, P., Voronov, B. M., et al. (1996). Heterodyne detection of THz radiation with a superconducting hot‐electron bolometer mixer. Appl. Phys. Lett., 69(2), 260–262.
Abstract: We report on the use of a superconducting hot‐electron bolometer mixer for heterodyne detection of terahertz radiation. Radiation with a wavelength of 119 μm was coupled to the mixer, a NbN microbridge, by a hybrid quasioptical antenna consisting of an extended hyperhemispherical lens and a planar logarithmic spiral antenna. We found, at an intermediate frequency of 1.5 GHz, a system double side band noise temperature of ≊40 000 K and conversion losses of 25 dB. We also discuss the possibilities of further improvement of the mixer performance.
|
|
|
|
Trifonov, V. A., Karasik, B. S., Zorin, M. A., Gol’tsman, G. N., Gershenzon, E. M., Lindgren, M., et al. (1996). 9.6 μm wavelength mixing in a patterned YBa2Cu3O7‐δ thin film. Appl. Phys. Lett., 68(10), 1418–1420.
Abstract: Hot‐electron bolometric (HEB) mixing of 9.6 μm infrared radiation from two lasers in high‐quality YBa2Cu3O7−δ (YBCO) patterned thin film has been demonstrated. A heterodyne measurement showed an intermediate frequency (IF) bandwidth of 18 GHz, limited by our measurement system. An intrinsic limit of 100 GHz is predicted. Between 0.1 and 1 GHz intermediate frequency, temperature fluctuations with an equivalent output noise temperature Tfl up to ∼150 K, contributed to the mixer noise while Johnson noise dominated above 1 GHz. The overall conversion loss at 77 K at low intermediate frequencies was measured to be ∼25 dB, of which 13 dB was due to the coupling loss. The HEB mixer is very promising for use in heterodyne receivers within the whole infrared range.
|
|
|
|
Gousev, Y. P., Gol'tsman, G. N., Karasik, B. S., Gershenzon, E. M., Semenov, A. D., Barowski, H. S., et al. (1996). Quasioptical superconducting hot electron bolometer for submillmeter waves. Int. J. of Infrared and Millimeter Waves, 17(2), 317–331.
Abstract: We report on a superconducting hot electron bolometer coupled to radiation via a broadband antenna. The bolometer, a structured NbN film, was patterned on a thin dielectric membrane between terminals of a gold slotline antenna. We investigated the response to submillimeter radiation (wave-lengths ∼ 0.1 mm to 0.7 mm) in the fundamental Gaussian mode. We found that the directivity of the antenna was constant within a factor of 2.5 through the whole experimental range. The noise equivalent power of the bolometer at 119 µm was ∼ 3 · 10−13 W/Hz1/2; a time constant of ∼ 160 ps was estimated.
|
|
|
|
Zorin, M., Gol'tsman, G. N., Karasik, B. S., Elantev, A. I., Gershenzon, E. M., Lindgren, M., et al. (1995). Optical mixing in thin YBa2Cu3O7-x films. IEEE Trans. Appl. Supercond., 5(2), 2431–2434.
Abstract: High quality, j/sub c/ (77 K)>10/sup 6/ A/cm/sup 2/, epitaxial YBa2Cu3O7-x films of 50 nm thickness were patterned into ten parallel 1 /spl mu/m wide strips. The film structure was coupled to a single-mode fiber. Mixer response was obtained at 0.78 /spl mu/m using laser frequency modulation and an optical delay line. Using two semiconductor lasers at 1.55 /spl mu/m wavelength the beating signal was used to measure the photoresponse up to 18 GHz. Nonequilibrium photoresponse in the resistive state of the superconductor was observed. Bolometric response dominates up to 3 GHz, after which the nonequilibrium response is constant up to the frequency limit of our registration system. Using an electron heating model the influence of different thermal processes on the conversion loss has been analyzed. Ways of increasing the sensitivity are also discussed.
|
|
|
|
Karasik, B. S., Milostnaya, I. I., Zorin, M. A., Elantev, A. I., Gol'tsman, G. N., & Gershenzon, E. M. (1995). High speed current switching of homogeneous YBaCuO film between superconducting and resistive states. IEEE Trans. Appl. Supercond., 5(2), 3042–3045.
Abstract: Transitions of thin structured YBaCuO films from superconducting (S) to normal (N) state and back induced by a supercritical current pulse has been studied. A subnanosecond stage in the film resistance dynamic has been observed. A more gradual (nanosecond) ramp in the time dependence of the resistance follows the fast stage. The fraction of the film resistance which is attained during the fast S-N stage rises with the current amplitude. Subnanosecond N-S switching is more pronounced for smaller amplitudes of driving current and for shorter pulses. The phenomena observed are viewed within the framework of an electron heating model. The expected switching time and repetition rate of an optimized current controlling device are estimated to be 1-2 ps and 80 GHz respectively.
|
|