Gol'tsman, G. N., Vachtomin, Y. B., Antipov, S. V., Finkel, M. I., Maslennikov, S. N., Smirnov, K. V., et al. (2005). NbN phonon-cooled hot-electron bolometer mixer for terahertz heterodyne receivers. In Proc. SPIE (Vol. 5727, pp. 95–106).
Abstract: We present the results of our studies of NbN phonon-cooled HEB mixers at terahertz frequencies. The mixers were fabricated from NbN film deposited on a high-resistivity Si substrate with an MgO buffer layer. The mixer element was integrated with a log-periodic spiral antenna. The noise temperature measurements were performed at 2.5 THz and at 3.8 THz local oscillator frequencies for the 3 x 0.2 μm2 active area devices. The best uncorrected receiver noise temperatures found for these frequencies are 1300 K and 3100 K, respectively. A water vapour discharge laser was used as the LO source. The largest gain bandwidth of 5.2 GHz was achieved for a mixer based on 2 nm thick NbN film deposited on MgO layer over Si substrate. The gain bandwidth of the mixer based on 3.5 nm NbN film deposited on Si with MgO is 4.2 GHz and the noise bandwidth for the same device amounts to 5 GHz. We also present the results of our research into decrease of the direct detection contribution to the measured Y-factor and a possible error of noise temperature calculation. The use of a square nickel cell mesh as an IR-filter enabled us to avoid the effect of direct detection and measure apparent value of the noise temperature which was 16% less than that obtained using conventional black polyethylene IR-filter.
|
Sobolewski, R., Xu, Y., Zheng, X., Williams, C., Zhang, J., Verevkin, A., et al. (2002). Spectral sensitivity of the NbN single-photon superconducting detector. IEICE Trans. Electron., E85-C(3), 797–802.
Abstract: We report our studies on the spectral sensitivity of superconducting NbN thin-film single-photon detectors (SPD's) capable of GHz counting rates of visible and near-infrared photons. In particular, it has been shown that a NbN SPD is sensitive to 1.55-µm wavelength radiation and can be used for quantum communication. Our SPD's exhibit experimentally measured intrinsic quantum efficiencies from 20% at 800 nm up to 1% at 1.55-µm wavelength. The devices demonstrate picosecond response time (<100 ps, limited by our readout system) and negligibly low dark counts. Spectral dependencies of photon counting of continuous-wave, 0.4-µm to 3.5-µm radiation, and 0.63-µm, 1.33-µm, and 1.55-µm laser-pulsed radiations are presented for the single-stripe-type and meander-type devices.
|
Korneev, A., Minaeva, O., Rubtsova, I., Milostnaya, I., Chulkova, G., Voronov, B., et al. (2005). Superconducting single-photon ultrathin NbN film detector. Quantum Electronics, 35(8), 698–700.
Abstract: Superconducting single-photon ultrathin NbN film detectors are studied. The development of manufacturing technology of detectors and the reduction of their operating temperature down to 2 K resulted in a considerable increase in their quantum efficiency, which reached in the visible region (at 0.56 μm) 30%—40%, i.e., achieved the limit determined by the absorption coefficient of the film. The quantum efficiency exponentially decreases with increasing wavelength, being equal to ~20% at 1.55 μm and ~0.02% at 5 μm. For the dark count rate of ~10-4s-1, the experimental equivalent noise power was 1.5×10-20 W Hz-1/2; it can be decreased in the future down to the record low value of 5×10-21 W Hz-1/2. The time resolution of the detector is 30 ps.
|
Smirnov, K., Korneev, A., Minaeva, O., Divochiy, A., Tarkhov, M., Ryabchun, S., et al. (2007). Ultrathin NbN film superconducting single-photon detector array. In J. Phys.: Conf. Ser. (Vol. 61, pp. 1081–1085).
Abstract: We report on the fabrication process of the 2 × 2 superconducting single-photon detector (SSPD) array. The SSPD array is made from ultrathin NbN film and is operated at liquid helium temperatures. Each detector is a nanowire-based structure patterned by electron beam lithography process. The advances in fabrication technology allowed us to produce highly uniform strips and preserve superconducting properties of the unpatterned film. SSPD exhibit up to 30% quantum efficiency in near infrared and up to 1% at 5-μm wavelength. Due to 120 MHz counting rate and 18 ps jitter, the time-domain multiplexing read-out is proposed for large scale SSPD arrays. Single-pixel SSPD has already found a practical application in non-invasive testing of semiconductor very-large scale integrated circuits. The SSPD significantly outperformed traditional single-photon counting avalanche diodes.
|
Semenov, A., Richter, H., Smirnov, K., Voronov, B., Gol'tsman, G., & Hübers, H. - W. (2004). The development of terahertz superconducting hot-electron bolometric mixers. Supercond. Sci. Technol., 17(5), 436–439.
Abstract: We present recent advances in the development of NbN hot-electron bolometric (HEB) mixers for flying terahertz heterodyne receivers. Three important issues have been addressed: the quality of the source NbN films, the effect of the bolometer size on the spectral properties of different planar feed antennas, and the local oscillator (LO) power required for optimal operation of the mixer. Studies of the NbN films with an atomic force microscope indicated a surface structure that may affect the performance of the smallest mixers. Measured spectral gain and noise temperature suggest that at frequencies above 2.5 THz the spiral feed provides better overall performance than the double-slot feed. Direct measurements of the optimal LO power support earlier estimates made in the framework of the uniform mixer model.
|
Verevkin, A., Zhang, J., Sobolewski, R., Lipatov, A., Okunev, O., Chulkova, G., et al. (2002). Detection efficiency of large-active-area NbN single-photon superconducting detectors in the ultraviolet to near-infrared range. Appl. Phys. Lett., 80(25), 4687–4689.
Abstract: We report our studies on spectral sensitivity of meander-type, superconducting NbN thin-film single-photon detectors (SPDs), characterized by GHz counting rates of visible and near-infrared photons and negligible dark counts. Our SPDs exhibit experimentally determined quantum efficiencies ranging from ∼0.2% at the 1.55 μm wavelength to ∼70% at 0.4 μm. Spectral dependences of the detection efficiency (DE) at the 0.4 to 3.0-μm-wavelength range are presented. The exponential character of the DE dependence on wavelength, as well as its dependence versus bias current, is qualitatively explained in terms of superconducting fluctuations in our ultrathin, submicron-width superconducting stripes. The DE values of large-active-area NbN SPDs in the visible range are high enough for modern quantum communications.
|
Meledin, D., Tong, C. Y. - E., Blundell, R., Kaurova, N., Smirnov, K., Voronov, B., et al. (2003). Study of the IF bandwidth of NbN HEB mixers based on crystalline quartz substrate with an MgO buffer layer. IEEE Trans. Appl. Supercond., 13(2), 164–167.
Abstract: In this paper, we present the results of IF bandwidth measurements on 3-4 nm thick NbN hot electron bolometer waveguide mixers, which have been fabricated on a 200-nm thick MgO buffer layer deposited on a crystalline quartz substrate. The 3-dB IF bandwidth, measured at an LO frequency of 0.81 THz, is 3.7 GHz at the optimal bias point for low noise receiver operation. We have also made measurements of the IF dynamic impedance, which allow us to evaluate the intrinsic electron temperature relaxation time and self-heating parameters at different bias conditions.
|
Semenov, A. D., Hübers, H. - W., Richter, H., Birk, M., Krocka, M., Mair, U., et al. (2003). Superconducting hot-electron bolometer mixer for terahertz heterodyne receivers. IEEE Trans. Appl. Supercond., 13(2), 168–171.
Abstract: We present recent results showing the development of superconducting NbN hot-electron bolometer mixer for German receiver for astronomy at terahertz frequencies and terahertz limb sounder. The mixer is incorporated into a planar feed antenna, which has either logarithmic spiral or double-slot configuration, and backed on a silicon lens. The hybrid antenna had almost frequency independent and symmetric radiation pattern slightly broader than expected for a diffraction limited antenna. At 2.5 THz the best 2200 K double side-band receiver noise temperature was achieved across a 1 GHz intermediate frequency bandwidth centred at 1.5 GHz. For this operation regime, a receiver conversion efficiency of -17 dB was directly measured and the loss budget was evaluated. The mixer response was linear at load temperatures smaller than 400 K. Implementation of the MgO buffer layer on Si resulted in an increased 5.2 GHz gain bandwidth. The receiver was tested in the laboratory environment by measuring a methanol emission line at 2.5 THz.
|
Korneev, A., Vachtomin, Y., Minaeva, O., Divochiy, A., Smirnov, K., Okunev, O., et al. (2007). Single-photon detection system for quantum optics applications. IEEE J. Select. Topics Quantum Electron., 13(4), 944–951.
Abstract: We describe the design and characterization of a fiber-coupled double-channel single-photon detection system based on superconducting single-photon detectors (SSPD), and its application for quantum optics experiments on semiconductor nanostructures. When operated at 2-K temperature, the system shows 10% quantum efficiency at 1.3-¿m wavelength with dark count rate below 10 counts per second and timing resolution <100 ps. The short recovery time and absence of afterpulsing leads to counting frequencies as high as 40 MHz. Moreover, the low dark count rate allows operation in continuous mode (without gating). These characteristics are very attractive-as compared to InGaAs avalanche photodiodes-for quantum optics experiments at telecommunication wavelengths. We demonstrate the use of the system in time-correlated fluorescence spectroscopy of quantum wells and in the measurement of the intensity correlation function of light emitted by semiconductor quantum dots at 1300 nm.
|
Ozhegov, R. V., Gorshkov, K. N., Smirnov, K. V., Gol’tsman, G. N., Filippenko, L. V., & Koshelets, V. P. (2010). Terahertz imaging system based on superconducting integrated receiver. In Proc. 2-nd Int. Conf. Terahertz and Microwave radiation: Generation, Detection and Applications (pp. 20–22).
Abstract: The development of terahertz imaging instruments for security systems is on the cutting edge of terahertz technology. We are developing a THz imaging system based on a superconducting integrated receiver (SIR). An SIR is a new type of heterodyne receiver based on an SIS mixer integrated with a flux-flow oscillator (FFO) and a harmonic mixer which is used for phase-locking the FFO. Developing an array of SIRs would allow obtaining amplitude and phase characteristics of incident radiation in the plane of the receiver. Employing an SIR in an imaging system means building an entirely new instrument with many advantages compare to traditional systems: i) high temperature resolution, comparable to the best results for incoherent receivers; ii) high spectral resolution allowing spectral analysis of various substances; iii) the local oscillator frequency can be varied to obtain images at different frequencies, effectively providing “color” images; iv) since a heterodyne receiver preserves the phase of the radiation, it is possible to construct 3D images. The paper presents a prototype THz imaging system using an 1 pixel SIR. We have studied the dependence of the noise equivalent temperature difference (NETD) on the integration time and also possible ways of achieving best possible sensitivity. An NETD of 13 mK was obtained with an integration time of 1 sec a detection bandwidth of 4 GHz at a local oscillator frequency of 520 GHz. An important advantage of an FFO is its wide operation range: 300-700 GHz.
|
Korneev, A., Kouminov, P., Matvienko, V., Chulkova, G., Smirnov, K., Voronov, B., et al. (2004). Sensitivity and gigahertz counting performance of NbN superconducting single-photon detectors. Appl. Phys. Lett., 84(26), 5338–5340.
Abstract: We have measured the quantum efficiencysQEd, GHz counting rate, jitter, and noise-equivalentpowersNEPdof nanostructured NbN superconducting single-photon detectorssSSPDsdin thevisible to infrared radiation range. Our 3.5-nm-thick and 100- to 200-nm-wide meander-typedevices(total area 10310mm2), operating at 4.2 K, exhibit an experimental QE of up to 20% inthe visible range and,10% at 1.3 to 1.55mm wavelength and are potentially sensitive up tomidinfrareds,10mmdradiation. The SSPD counting rate was measured to be above 2 GHz withjitter,18 ps, independent of the wavelength. The devices’ NEP varies from,10−17W/Hz1/2for1.55mm photons to,10−20W/Hz1/2for visible radiation. Lowering the SSPD operatingtemperature to 2.3 K significantly enhanced its performance, by increasing the QE to,20% andlowering the NEP level to,3310−22W/Hz1/2, both measured at 1.26mm wavelength.
|
Verevkin, A., Slysz, W., Pearlman, A., Zhang, J., Sobolewski, R., Okunev, O., et al. (2003). Real-time GHz-rate counting of infrared photons using nanostructured NbN superconducting detectors. In CLEO/QELS (CThM8). Optical Society of America.
Abstract: We demonstrate that our ultrathin, nanometer-width NbN superconducting single-photon detectors are capable of above 1-GHz-frequency, real-time counting of near-infrared photons. The measured system jitter of the detector is below 15 ps.
|
Goltsman, G., Korneev, A., Divochiy, A., Minaeva, O., Tarkhov, M., Kaurova, N., et al. (2009). Ultrafast superconducting single-photon detector. J. Modern Opt., 56(15), 1670–1680.
Abstract: The state-of-the-art of the NbN nanowire superconducting single-photon detector technology (SSPD) is presented. The SSPDs exhibit excellent performance at 2 K temperature: 30% quantum efficiency from visible to infrared, negligible dark count rate, single-photon sensitivity up to 5.6 µm. The recent achievements in the development of GHz counting rate devices with photon-number resolving capability is presented.
|
Shangina, E. L., Smirnov, K. V., Morozov, D. V., Kovalyuk, V. V., Goltsman, G. N., Verevkin, A. A., et al. (2011). Concentration dependence of energy relaxation time in AlGaAs/GaAs heterojunctions: direct measurements. Semicond. Sci. Technol., 26(2), 025013.
Abstract: We present measurements of the energy relaxation time, τε, of electrons in a single heterojunction in a quasi-equilibrium state using microwave time-resolved spectroscopy at 4.2 K. We find the relaxation time has a power-law dependence on the carrier density of the two-dimensional electron gas, τε∝nγs with γ = 0.40 ± 0.02 for values of the carrier density, ns, from 1.6 × 1011 to 6.6 × 1011cm−2. The results are in good agreement with predictions taking into account the scattering of the carriers by both piezoelectric and deformation potential acoustic phonons. We compare these results with indirect measurements of the energy relaxation time from energy loss measurements involving Joule heating of the electron gas.
|
Glejm, A. V., Anisimov, A. A., Asnis, L. N., Vakhtomin, Y. B., Divochiy, A. V., Egorov, V. I., et al. (2014). Quantum key distribution in an optical fiber at distances of up to 200 km and a bit rate of 180 bit/s. Bulletin of the Russian Academy of Sciences. Physics, 78(3), 171–175.
Abstract: An experimental demonstration of a subcarrier-wave quantum cryptography system with superconducting single-photon detectors (SSPDs) that distributes a secure key in a single-mode fiber at distance of 25 km with a bit rate of 800 kbit/s, a distance of 100 km with a bit rate of 19 kbit/s, and a distance of 200 km with a bit rate of 0.18 kbit/s is described.
|