Lobanov, Y., Tong, E., Blundell, R., Hedden, A., Voronov, B., & Gol'tsman, G. (2011). Large-signal frequency response of an HEB mixer: from 300 MHz to terahertz. IEEE Trans. Appl. Supercond., 21(3), 628–631.
Abstract: We present a study of the large signal frequency response of an HEB mixer over a wide frequency range. In our experiments, we have subjected the HEB mixer to incident electromagnetic radiation from 0.3 GHz to 1 THz. The mixer element is an NbN film deposited on crystalline quartz. The mixer chip is mounted in a waveguide cavity, coupled to free space with a diagonal horn. At microwave frequencies, electromagnetic radiation is applied through the coaxial bias port of the mixer block. At higher frequencies the input signal passes via the diagonal horn feed. At each frequency, the incident power is varied and a family of I-V curves is recorded. From the curves we identify 3 distinct regimes of operation of the mixer separated by the phonon relaxation frequency and the superconducting energy gap frequency observed at about 3 GHz and 660 GHz respectively. In this paper, we will present observed curves and discuss the results of our experiment.
|
Lobanov, Y. V., Tong, C. - Y. E., Hedden, A. S., Blundell, R., Voronov, B. M., & Gol'tsman, G. N. (2011). Direct measurement of the gain and noise bandwidths of HEB mixers. IEEE Trans. Appl. Supercond., 21(3), 645–648.
Abstract: The intermediate frequency (IF) bandwidth of a hot electron bolometer (HEB) mixer is an important parameter of the mixer, in that it helps to determine its suitability for a given application. With the availability of wideband low noise amplifiers, it is simple to measure the performance of an HEB mixer over a wide range of IF at a fixed LO frequency using the standard Y-factor method. This in-situ method allows us to measure both the gain and noise bandwidths simultaneously. We have also measured mixer output impedance with a vector network analyser. Intrinsic time constant has been extracted from the impedance data and compared to the mixer's bandwidths determined from receiver Y-factor measurement.
|
Kawakami, A., Saito, S., & Hyodo, M. (2011). Fabrication of nano-antennas for superconducting Infrared detectors. IEEE Trans. Appl. Supercond., 21(3), 632–635.
Abstract: To improve the response performance of superconducting infrared detectors, we have developed a fabrication process for nano-antennas. A nano-antenna consists of a dipole antenna, and a superconducting thin film strip placed in the antenna's center. By measuring the transition temperature of the superconducting strips, we confirmed that their superconductivity maintained a good condition after the nano-antenna fabrication process. We also evaluated nano-antenna characteristics using Fourier transform infrared spectroscopy. The evaluated antenna length and width were respectively set at around 2400 nm and 400 nm, and the antennas were placed at intervals of several micrometers around the area of 1 mm2 . In an evaluation of spectral transmission characteristics, clear absorption caused by antenna effects was observed at around 1400 cm-1. High polarization dependencies were also observed.
|
Il'in, K. S., Lindgren, M., Currie, M. A., Semenov, D., Gol'tsman, G. N., Sobolewski, R., et al. (2000). Picosecond hot-electron energy relaxation in NbN superconducting photodetectors. Appl. Phys. Lett., 76(19), 2752–2754.
Abstract: We report time-resolved characterization of superconducting NbN hot-electron photodetectors using an electro-optic sampling method. Our samples were patterned into micron-size microbridges from 3.5-nm-thick NbN films deposited on sapphire substrates. The devices were illuminated with 100 fs optical pulses, and the photoresponse was measured in the ambient temperature range between 2.15 and 10.6 K (superconducting temperature transition TC). The experimental data agreed very well with the nonequilibrium hot-electron, two-temperature model. The quasiparticle thermalization time was ambient temperature independent and was measured to be 6.5 ps. The inelastic electron–phonon scattering time Ï„e–ph tended to decrease with the temperature increase, although its change remained within the experimental error, while the phonon escape time Ï„es decreased almost by a factor of two when the sample was put in direct contact with superfluid helium. Specifically, Ï„e–ph and Ï„es, fitted by the two-temperature model, were equal to 11.6 and 21 ps at 2.15 K, and 10(±2) and 38 ps at 10.5 K, respectively. The obtained value of Ï„e–ph shows that the maximum intermediate frequency bandwidth of NbN hot-electron phonon-cooled mixers operating at TC can reach 16(+4/–3) GHz if one eliminates the bolometric phonon-heating effect.
|
Henrich, D., Dorner, S., Hofherr, M., Il'in, K., Semenov, A., Heintze, E., et al. (2012). Broadening of hot-spot response spectrum of superconducting NbN nanowire single-photon detector with reduced nitrogen content. J. Appl. Phys., 112.
Abstract: The spectral detection efficiency and the dark count rate of superconducting nanowire
single-photon detectors (SNSPD) have been studied systematically on detectors made from thin
NbN films with different chemical compositions. Reduction of the nitrogen content in the 4 nm
thick NbN films results in a decrease of the dark count rates more than two orders of magnitude
and in a red shift of the cut-off wavelength of the hot-spot SNSPD response. The observed
phenomena are explained by an improvement of uniformity of NbN films that has been confirmed
by a decrease of resistivity and an increase of the ratio of the measured critical current to the
depairing current. The latter factor is considered as the most crucial for both the cut-off
wavelength and the dark count rates of SNSPD. Based on our results we propose a set of criteria
for material properties to optimize SNSPD in the infrared spectral region. VC 2012 American
Institute of Physics. [http://dx.doi.org/10.1063/1.4757625]
|