Cherednichenko, S., Kroug, M., Merkel, H., Kollberg, E., Loudkov, D., Smirnov, K., et al. (2001). Local oscillator power requirement and saturation effects in NbN HEB mixers. In C. Iit.u.t.e of T. Jet Propulsion Laboratory (Ed.), Proc. 12th Int. Symp. Space Terahertz Technol. (pp. 273–285). San Diego, CA, USA.
Abstract: The local oscillator power required for NbN hot-electron bolometric mixers (P LO ) was investigated with respect to mixer size, critical temperature and ambient temperature. P LO can be decreased by a factor of 10 as the mixer size decreases from 4×0.4 µm 2 to 0.6×0.13 µm 2 . For the smallest volume mixer the optimal local oscillator power was found to be 15 nW. We found that for such mixer no signal compression was observed up to an input signal of 2 nW which corresponds to an equivalent input load of 20,000 K. For a constant mixer volume, reduction of T c can decrease optimal local oscillator power at least by a factor of 2 without a deterioration of the receiver noise temperature. Bath temperature was found to have minor effect on the receiver characteristics.
|
Hübers, H. - W., Semenov, A. D., Richter, H., Schubert, J., Hadjiloucas, S., Bowen, J. W., et al. (2001). Antenna pattern of the quasi-optical hot-electron bolometric mixer at terahertz frequencies. In Proc. 12th Int. Symp. Space Terahertz Technol. (pp. 286–296). San Diego, CA, USA.
|
Semenov, A. D., Sergeev, A. V., Kouminov, P., Goghidze, I. G., Heusinger, M. A., Nebosis, R. S., et al. (1993). Transparency of YBCO film/substrate interfaces for thermal phonons determined by photoresponse measurements. In H. C. Freyhardt (Ed.), Proc. 1st European Conf. on Appl. Supercond. (Vol. 2, pp. 1443–1446).
Abstract: Direct measurements of the thermal boundary resistance were performed by means of the stationary method. In this approach the temperature of an electrically heated film is controlled by its dc resistance while an additional film on the same substrate is used as a thermometer monitoring substrate temperature. The temperature field in the substrate is then calculated to deduce the Kapitza temperature step at the interface between the heated strip and the substrate. The main statement of all afore-said papers is that experimental values of the thermal boundary resistance are too large to be explained by the acoustic mismatch model. In this paper we investigate transparency of YBaCuO film/substrate interfaces for thermal phonons by means of photoresponse measurements. We show that our data are in reasonable agreement with the acoustic mismatch theory.
|
Cherednichenko, S., Yagoubov, P., Il'in, K., Gol'tsman, G., & Gershenzon, E. (1997). Large bandwidth of NbN phonon-cooled hot-electron bolometer mixers. In Proc. 27th Eur. Microwave Conf. (Vol. 2, pp. 972–977). IEEE.
Abstract: The bandwidth of NbN phonon-cooled hot electron bolometer mixers has been systematically investigated with respect to the film thickness and film quality variation. The films, 2.5 to 10 nm thick, were fabricated on sapphire substrates using DC reactive magnetron sputtering. All devices consisted of several parallel strips, each 1 um wide and 2 um long, placed between Ti-Au contact pads. To measure the gain bandwidth we used two identical BWOs operating in the 120-140 GHz frequency range, one functioning as a local oscillator and the other as a signal source. The majority of the measurements were made at an ambient temperature of 4.2 K with optimal LO and DC bias. The maximum 3 dB bandwidth (about 4 GHz) was achieved for the devices made of films which were 2.5-3.5 nm thick, had a high critical temperature, and high critical current density. A theoretical analysis of bandwidth for these mixers based on the two-temperature model gives a good description of the experimental results if one assumes that the electron temperature is equal to the critical temperature.
|
Merkel, H. F., Yagoubov, P. A., Kroug, M., Khosropanah, P., Kollberg, E. L., Gol’tsman, G. N., et al. (1998). Noise temperature and absorbed LO power measurement methods for NbN phonon-cooled hot electron bolometric mixers at terahertz frequencies. In Proc. 28th European Microwave Conf. (Vol. 1, pp. 294–299).
Abstract: In this paper the absorbed LO power requirements and the noise performance of NbN based phonon-cooled hot electron bolometric (HEB) quasioptical mixers are investigated for RF frequencies in the 0.55-1.1 range The minimal measured DSB noise temperatures are about 500 K at 640 GHz, 600 K at 750 GHz, 850 K at 910 GHz and 1250 K at 1.1 THz. The increase in noise temperature at 1.1THz is attributed to water absorption. The absorbed LO power is measured using a calorimetric approach. The results are subsequently corrected for lattice heating. These values are compared to results of a novel one dimensional hot spot mixer models and to a more traditional isotherm method which tends to underestimate the absorbed LO power for small bias powers. Typically a LO power between 50nW and 100nW is needed to pump the device to the optimal operating point.
|