Romanov, N. R., Zolotov, P. I., Vakhtomin, Y. B., Divochiy, A. V., & Smirnov, K. V. (2018). Electron diffusivity measurements of VN superconducting single-photon detectors. In J. Phys.: Conf. Ser. (Vol. 1124, 051032).
Abstract: The research of ultrathin vanadium nitride (VN) films as a promising candidate for superconducting single-photon detectors (SSPD) is presented. The electron diffusivity measurements are performed for such devices. Devices that were fabricated out from 9.9 nm films had diffusivity coefficient of 0.41 cm2/s and from 5.4 nm – 0.54 cm2/s. Obtained values are similar to other typical SSPD materials. The diffusivity that increases along with decreasing of the film thickness is expected to allow fabrication of the devices with improved characteristics. Fabricated VN SSPDs showed prominent single-photon response in the range 0.9-1.55 µm.
|
Zolotov, P. I., Divochiy, A. V., Vakhtomin, Y. B., Morozov, P. V., Seleznev, V. A., & Smirnov, K. V. (2017). Development of high-effective superconducting single-photon detectors aimed for mid-IR spectrum range. In J. Phys.: Conf. Ser. (Vol. 917, 062037).
Abstract: We report on development of superconducting single-photon detectors (SSPD) with high intrinsic quantum efficiency in the wavelength range 1.31 – 3.3 μm. By optimization of the NbN film thickness and its compound, we managed to improve detection efficiency of the detectors in the range up to 3.3 μm. Optimized devices showed intrinsic quantum efficiencies as high as 10% at mid-IR range.
|
Gol’tsman, G. N., & Smirnov, K. V. (2001). Electron-phonon interaction in a two-dimensional electron gas of semiconductor heterostructures at low temperatures. Jetp Lett., 74(9), 474–479.
Abstract: Theoretical and experimental works devoted to studying electron-phonon interaction in the two-dimensional electron gas of semiconductor heterostructures at low temperatures in the case of strong heating in an electric field under quasi-equilibrium conditions and in a quantizing magnetic field perpendicular to the 2D layer are considered.
|
Smirnov, K. V., Ptitsina, N. G., Vakhtomin, Y. B., Verevkin, A. A., Gol’tsman, G. N., & Gershenzon, E. M. (2000). Energy relaxation of two-dimensional electrons in the quantum Hall effect regime. JETP Lett., 71(1), 31–34.
Abstract: The mm-wave spectroscopy with high temporal resolution is used to measure the energy relaxation times τe of 2D electrons in GaAs/AlGaAs heterostructures in magnetic fields B=0–4 T under quasi-equilibrium conditions at T=4.2 K. With increasing B, a considerable increase in τe from 0.9 to 25 ns is observed. For high B and low values of the filling factor ν, the energy relaxation rate τ −1e oscillates. The depth of these oscillations and the positions of maxima depend on the filling factor ν. For ν>5, the relaxation rate τ −1e is maximum when the Fermi level lies in the region of the localized states between the Landau levels. For lower values of ν, the relaxation rate is maximum at half-integer values of τ −1e when the Fermi level is coincident with the Landau level. The characteristic features of the dependence τ −1e (B) are explained by different contributions of the intralevel and interlevel electron-phonon transitions to the process of the energy relaxation of 2D electrons.
|
Verevkin, A. A., Ptitsina, N. G., Smirnov, K. V., Gol’tsman, G. N., Gershenzon, E. M., & Ingvesson, K. S. (1996). Direct measurements of energy relaxation times on an AlGaAs/GaAs heterointerface in the range 4.2–50 K. JETP Lett., 64(5), 404–409.
Abstract: The temperature dependence of the energy relaxation time τe (T) of a two-dimensional electron gas at an AlGaAs/GaAs heterointerface is measured under quasiequilibrium conditions in the region of the transition from scattering by acoustic phonons to scattering with the participation of optical phonons. The temperature interval of constant τe, where scattering by the deformation potential predominates, is determined. In the preceding, low-temperature region, where piezoacoustic and deformation-potential-induced scattering processes coexist, τ e decreases slowly with increasing temperature. Optical phonons start to participate in the scattering processes at T∼25 K (the characteristic phonon lifetime was equal to τLOτ4.5 ps). The energy losses calculated from the τe data in a model with an effective nonequilibrium electron temperature agree with the published data obtained under strong heating conditions.
|
Smirnov, K. V., Vakhtomin, Y. B., Divochiy, A. V., Ozhegov, R. V., Pentin, I. V., & Gol'tsman, G. N. (2010). Infrared and terahertz detectors on basis of superconducting nanostructures. In IEEE (Ed.), Microwave and Telecom. Technol. (CriMiCo), 20th Int. Crimean Conf. (pp. 823–824).
Abstract: Results of development of single-photon receiving systems of visible, infrared and terahertz range based on thin-film superconducting nanostructures are presented. The receiving systems are produced on the basis of superconducting nanostructures, which function by means of hot-electron phenomena.
|
Kitaeva, G. K., Kornienko, V. V., Kuznetsov, K. A., Pentin, I. V., Smirnov, K. V., & Vakhtomin, Y. B. (2019). Direct detection of the idler THz radiation generated by spontaneous parametric down-conversion. Opt. Lett., 44(5), 1198–1201.
Abstract: We study parametric down-conversion (PDC) of optical laser radiation in the strongly frequency non-degenerate regime which is promising for the generation of quantum-correlated pairs of extremely different spectral ranges, the optical and the terahertz (THz) ones. The possibility to detect tenuous THz-frequency photon fluxes generated under low-gain spontaneous PDC is demonstrated using a hot electron bolometer. Then experimental dependences of the THz radiation power on the detection angle and on the pump intensity are analyzed.
|
Vorobyov, V. V., Kazakov, A. Y., Soshenko, V. V., Korneev, A. A., Shalaginov, M. Y., Bolshedvorskii, S. V., et al. (2017). Superconducting detector for visible and near-infrared quantum emitters [Invited]. Opt. Mater. Express, 7(2), 513–526.
Abstract: Further development of quantum emitter based communication and sensing applications intrinsically depends on the availability of robust single-photon detectors. Here, we demonstrate a new generation of superconducting single-photon detectors specifically optimized for the 500–1100 nm wavelength range, which overlaps with the emission spectrum of many interesting solid-state atom-like systems, such as nitrogen-vacancy and silicon-vacancy centers in diamond. The fabricated detectors have a wide dynamic range (up to 350 million counts per second), low dark count rate (down to 0.1 counts per second), excellent jitter (62 ps), and the possibility of on-chip integration with a quantum emitter. In addition to performance characterization, we tested the detectors in real experimental conditions involving nanodiamond nitrogen-vacancy emitters enhanced by a hyperbolic metamaterial.
|
Lobanov, Y. V., Vakhtomin, Y. B., Pentin, I. V., Rosental, V. A., Smirnov, K. V., Goltsman, G. N., et al. (2021). Time-resolved measurements of light–current characteristic and mode competition in pulsed THz quantum cascade laser. Optical Engineering, 60(8), 1–8.
Abstract: Quantum cascade lasers (QCL) are widely adopted as prominent and easy-to-use solid-state sources of terahertz radiation. Yet some applications require generation and detection of very sharp and narrow terahertz-range pulses with a specific spectral composition. We have studied time-resolved light-current (L–I) characteristics of multimode THz QCL operated with a fast ramp of the injection current. Detection of THz pulses was carried out using an NbN superconducting hot-electron bolometer with the time constant of the order of 1 ns while the laser bias current was swept during a single driving pulse. A nonmonotonic behavior of the L–I characteristic with several visually separated subpeaks was found. This behavior is associated with the mode competition in THz QCL cavity, which we confirm by L–I measurements with use of an external Fabry–Perot interferometer for a discrete mode selection. We also have demonstrated the possibility to control the L–I shape with suppression of one of the subpeaks by simply adjusting the off-axis parabolic mirror for optimal optical alignment for one of the laser modes. The developed technique paves the way for rapid characterization of pulsed THz QCLs for further studies of the possibilities of using this approach in remote sensing.
|
Baeva, E. M., Sidorova, M. V., Korneev, A. A., Smirnov, K. V., Divochy, A. V., Morozov, P. V., et al. (2018). Thermal properties of NbN single-photon detectors. Phys. Rev. Applied, 10(6), 064063 (1 to 8).
Abstract: We investigate thermal properties of a NbN single-photon detector capable of unit internal detection efficiency. Using an independent calibration of the coupling losses, we determine the absolute optical power absorbed by the NbN film and, via resistive superconductor thermometry, the temperature dependence of the thermal resistance Z(T) of the NbN film. In principle, this approach permits simultaneous measurement of the electron-phonon and phonon-escape contributions to the energy relaxation, which in our case is ambiguous because of the similar temperature dependencies. We analyze Z(T) with a two-temperature model and impose an upper bound on the ratio of electron and phonon heat capacities in NbN, which is surprisingly close to a recent theoretical lower bound for the same quantity in similar devices.
|
Antipov, S. V., Svechnikov, S. I., Smirnov, K. V., Vakhtomin, Y. B., Finkel, M. I., Goltsman, G. N., et al. (2001). Noise temperature of quasioptical NbN hot electron bolometer mixers at 900 GHz. Physics of Vibrations, 9(4), 242–245.
|
Kaurova, N. S., Finkel, M. I., Maslennikov, S. N., Vahtomin, Y. B., Antipov, S. V., Smirnov, K. V., et al. (2004). Submillimeter mixer based on YBa2Cu3O7-x thin film. In Proc. 1-st conf. Fundamental problems of high temperature superconductivity (291). Moscow-Zvenigorod.
|
Smirnov, K. V., Vachtomin, Y. B., Antipov, S. V., Maslennikov, S. N., Kaurova, N. S., Drakinsky, V. N., et al. (2003). Noise and gain performance of spiral antenna coupled HEB mixers at 0.7 THz and 2.5 THz. In Proc. 14th Int. Symp. Space Terahertz Technol. (pp. 405–412).
Abstract: Noise and gain performance of hot electron bolometer (HEB) mixers based on ultrathin superconducting NbN films integrated with a spiral antenna was studied. The noise temperature measurements for two samples with different active area of 3 p.m x 0.24 .tni and 1.3 1..tm x 0.12 1.tm were performed at frequencies 0.7 THz and 2.5 THz. The best receiver noise temperatures 370 K and 1600 K, respectively, have been found at these frequencies. The influence of contact resistance between the superconductor and the antenna terminals on the noise temperature of HEB is discussed. The noise and gain bandwidth of 5GHz and 4.2 GHz, respectively, are demonstrated for similar HEB mixer at 0.75 THz.
|
Vachtomin, Y. B., Antipov, S. V., Maslennikov, S. N., Smirnov, K. V., Polyakov, S. L., Kaurova, N. S., et al. (2004). Noise temperature measurements of NbN phonon-cooled hot electron bolometer mixer at 2.5 and 3.8 THz. In Proc. 15th Int. Symp. Space Terahertz Technol. (pp. 236–241). Northampton, Massachusetts, USA.
Abstract: We present the results of noise temperature measurements of NbN phonon-cooled HEB mixers based on a 3.5 nm NbN film deposited on a high-resistivity Si substrate with a 200 nm – thick MgO buffer layer. The mixer element was integrated with a log-periodic spiral antenna. The noise temperature measurements were performed at 2.5 THz and at 3.8 THz local oscillator frequencies for the 3 µm x 0.2 µm active area devices. The best uncorrected receiver noise temperatures found for these frequencies are 1300 K and 3100 K, respectively. A water vapour discharge laser was used as the LO source. We also present the results of direct detection contribution to the measured Y-factor and of a possible error of noise temperature calculation. This error was more than 8% for the mixer with in-plane dimensions of 2.4 x 0.16 µm 2 at the optimal noise temperature point. The use of a mesh filter enabled us to avoid the effect of direct detection and decrease optical losses by 0.5 dB. The paper is concluded by the investigation results of the mixer polarization response. It was shown that the polarization can differ from the circular one at 3.8 THz by more than 2 dB.
|
Svechnikov, S. I., Finkel, M. I., Maslennikov, S. N., Vachtomin, Y. B., Smirnov, K. V., Seleznev, V. A., et al. (2006). Superconducting hot electron bolometer mixer for middle IR range. In Proc. 16th Int. Crimean Microwave and Telecommunication Technology (Vol. 2, pp. 686–687).
Abstract: The developed directly lens coupled hot electron bolometer (HEB) mixer was based on 5 nm superconducting NbN deposited on GaAs substrate. The layout of the structure, including 30x20 mcm^2 active area coupled with a 50 Ohm coplanar line, was patterned by photolithography. The responsivity of the mixer was measured in a direct detection mode in the 25-64 THz frequency range. The noise performance of the mixer and the directivity of the receiver were investigated in a heterodyne mode. A 10.6 mum wavelength CW CO2 laser was utilized as a local oscillator.
|