Abstract: We experimentally demonstrate a supercurrent-assisted, hotspot-formation mechanism for ultrafast detection and counting of visible and infrared photons. A photon-induced hotspot leads to a temporary formation of a resistive barrier across the superconducting sensor strip and results in an easily measurable voltage pulse. Subsequent hotspot healing in ∼30 ps time frame, restores the superconductivity (zero-voltage state), and the detector is ready to register another photon. Our device consists of an ultrathin, very narrow NbN strip, maintained at 4.2 K and current-biased close to the critical current. It exhibits an experimentally measured quantum efficiency of ∼20% for 0.81 μm wavelength photons and negligible dark counts.

Abstract: The ps optical response of ultrathin NbN photodetectors has been studied by electro-optic sampling. The detectors were fabricated by patterning ultrathin (3.5 nm thick) NbN films deposited on sapphire by reactive magnetron sputtering into either a 5×10 μm2 microbridge or 25 1 μm wide, 5 μm long strips connected in parallel. Both structures were placed at the center of a 4 mm long coplanar waveguide covered with Ti/Au. The photoresponse was studied at temperatures ranging from 2.15 K to 10 K, with the samples biased in the resistive (switched) state and illuminated with 100 fs wide laser pulses at 395 nm wavelength. At T=2.15 K, we obtained an approximately 100 ps wide transient, which corresponds to a NbN detector response time of 45 ps. The photoresponse can be attributed to the nonequilibrium electron heating effect, where the incident radiation increases the temperature of the electron subsystem, while the phonons act as the heat sink. The high-speed response of NbN devices makes them an excellent choice for an optoelectronic interface for superconducting digital circuits, as well as mixers for the terahertz regime. The multiple-strip detector showed a linear dependence on input optical power and a responsivity =3.9 V/W.

Abstract: A readout circuit using superconducting single-flux-quantum (SFQ) circuits has been developed to realize an independently addressable array of superconducting single-photon detectors (SSPDs). We tested the SFQ readout circuits by connecting with SSPDs. The error rates of readout circuits were below 10–5 for input signal amplitude of greater than 18.2 μA. Detection efficiencies (DEs) for single-photon incidents were measured both with and without the connection of a readout circuit. The observed DEs traced almost the same curves regardless of the connection of the readout circuit, except that the SSPD is likely to latch by connecting the readout circuit.

Abstract: We demonstrate efficient nanowire superconducting single photon detectors (SSPDs) based on NbN thin films grown on GaAs. NbN films ranging from 3 to 5 nm in thickness have been deposited by dc magnetron sputtering on GaAs substrates at 350 °C. These films show superconducting properties comparable to similar films grown on sapphire and MgO. In order to demonstrate the potential for monolithic integration, SSPDs were fabricated and measured on GaAs/AlAs Bragg mirrors, showing a clear cavity enhancement, with a peak quantum efficiency of 18.3% at λ = 1300 nm and T = 4.2 K.