Kawamura, J., Blundell, R., Tong, C. - Y. E., Gol'tsman, G., Gershenzon, E., Voronov, B., et al. (1997). Phonon-cooled NbN HEB mixers for submillimeter wavelengths. In Proc. 8th Int. Symp. Space Terahertz Technol. (pp. 23–28).
Abstract: The noise performance of receivers incorporating NbN phonon-cooled superconducting hot electron bolometric mixers is measured from 200 GHz to 900 GHz. The mixer elements are thin-film (thickness — 4 nm) NbN with —5 to 40 pm area fabricated on crystalline quartz sub- strates. The receiver noise temperature from 200 GHz to 900 GHz demonstrates no unexpected degradation with increasing frequency, being roughly TRx ,; 1-2 K The best receiver noise temperatures are 410 K (DSB) at 430 GHz, 483 K at 636 GHz, and 1150 K at 800 GHz.
|
|
|
Ekström, H., Kollberg, E., Yagoubov, P., Gol'tsman, G., Gershenzon, E., & Yngvesson, S. (1997). Phonon cooled ultra thin NbN hot electron bolometer mixers at 620 GHz. In Proc. 8th Int. Symp. Space Terahertz Technol. (pp. 29–35).
Abstract: We have measured the noise performance and gain bandwidth of 35 A thin NbN hot-electron mixers integrated with spiral antennas on silicon substrate lenses at 620 GHz. A double-sideband receiver noise temperature less than 1300 K has been obtained with a 3 dB bandwidth of GHz. The gain bandwidth is 3.2 GHz. A lower noise temperature of 1100 K has been achieved with an improved set-up. The mixer output noise dominated by thermal fluctuations is about 50-60 K, and the SSB receiver and intrinsic conversion gain is about -18 and -12 dB, respectively. Without mismatch losses and excluding the loss from the beamsplitter, we expect to achieve a receiver noise temperature of less than 700 K.
|
|
|
Gerecht, E., Musante, C. F., Wang, Z., Yngvesson, K. S., Waldman, J., Gol'tsman, G. N., et al. (1997). NbN hot electron bolometric mixer for 2.5 THz: the phonon cooled version. In Proc. 8th Int. Symp. Space Terahertz Technol. (pp. 258–271).
Abstract: We describe an investigation of a NbN HEB mixer for 2.5 THz. NbN HEBs are phonon-cooled de-. vices which are expected, according to theory, to achieve up to 10 GHz IF conversion gain bandwidth. We have developed an antenna coupled device using a log-periodic antenna and a silicon lens. We have demon- strated that sufficient LO power can be coupled to the device in order to bring it to the optimum mixer oper- ating point. The LO power required is less than 1 microwatts as measured directly at the device. We also describe the impedance characteristics of NbN devices and compare them with theory. The experimental results agree with theory except for the imaginary part of the impedance at very low frequencies as was demonstrated by other groups.
|
|
|
Hübers, H. - W., Semenov, A., Schubert, J., Gol'tsman, G., Voronov, B., & Gershenzon, E. (2000). Performance of the phonon-cooled hot-electron bolometric mixer between 0.7 THz and 5.2 THz. In Proc. 8-th Int. Conf. on Terahertz Electronics (pp. 117–119).
Abstract: We report on the phonon cooled NbN hot electron bolometer as mixer in the terahertz frequency range. Its hybrid antenna consists of a hyperhemispheric silicon lens and a logarithmic-spiral feed antenna. Noise temperatures have been measured between 0.7 THz and 5.2 THz. A quarter wavelength layer of Parylene works as antireflection coating for the silicon lens and reduces the noise temperature by about 30. It was found that the antenna pattern at 2.5 THz is determined by the feed antenna and not by the diameter of the lens.
|
|
|
Yagubov, P., Gol'tsman, G., Voronov, B., Seidman, L., Siomash, V., Cherednichenko, S., et al. (1996). The bandwidth of HEB mixers employing ultrathin NbN films on sapphire substrate. In Proc. 7th Int. Symp. Space Terahertz Technol. (pp. 290–302). Charlottesville, Virginia, USA.
Abstract: We report on some unusual features observed during fabrication of ultrathin NbN films with high Tc. The films were used to fabricate HEB mixers, which were evaluated for IF bandwidth measurements at 140 GHz. Ultrathin films were fabricated using reactive dc magnetron sputtering with a discharge current source. Reproducible parameters of the films are assured keeping constant the difference between the discharge voltage in pure argon, and in a gas mixture, for the same current. A maximum bandwidth of 4 GHz at optimal LO and dc bias was obtained for mixer chip based on NbN film 35 A thick with Tc = 11 K.
|
|