Men’shchikov, E. M., Gogidze, I. G., Sergeev, A. V., Elant’ev, A. I., Kuminov, P. B., Gol’tsman, G. N., et al. (1997). Superconducting fast detector based on the nonequilibrium inductance response of a film of niobium nitride. Tech. Phys. Lett., 23(6), 486–488.
Abstract: A new type of fast detector is proposed, whose operation is based on the variation of the kinetic inductance of a superconducting film caused by nonequilibrium quasiparticles created by the electromagnetic radiation. The speed of the detector is determined by the rate of multiplication of photo-excited quasiparticles, and is nearly independent of the temperature, being less than 1 ps for NbN. Models based on the Owen-Scalapino scheme give a good description of the experimentally determined dependence of the power-voltage sensitivity of the detector on the modulation frequency. The lifetime of the quasiparticles is determined, and it is shown that the reabsorption of nonequilibrium phonons by the condensate has a substantial effect even in ultrathin NbN films 5 nm thick, and results in the maximum possible quantum yield. A low concentration of equilibrium quasiparticles and a high quantum yield result in a detectivity D*=1012 W−1·Hz1/2 at a temperature T=4.2 K and D*=1016 W−1·cm· Hz1/2 at T=1.6 K.
|
|
|
Boreman, G. D. (1997). Infrared microantennas. SPIE, 3110, 882–885.
Abstract: We present results of mesurments of the polarization response of asymetric spiral antennas coupled Ni-NiO-Ni diodes, over the wavelength range 10.2 to 10.7 μm. The feed structure of the antenna imposes an elliptical polarization singature that is different from the circular polarization expected from a symmetric spiral. We develop a lossy-transmission-line model yielding the measured polarization response. A combination of a balanced and an unbalanced mode is required. Reflected current waves from the arm ends are significant.
|
|
|
Cherednichenko, S., Yagoubov, P., Il'In, K., Gol'tsman, G., & Gershenzon, E. (1997). Large bandwidth of NbN phonon-cooled hot-electron bolometer mixers on sapphire substrates. In Proc. 8th Int. Symp. Space Terahertz Technol. (pp. 245–257).
Abstract: The bandwidth of NbN phonon-cooled hot electron bolometer mixers has been systematically investigated with respect to the film thickness and film quality variation. The films, 2.5 to 10 mm thick, were fabricated on sapphire substrates using DC reactive magnetron sputtering. All devices consisted of several parallel strips, each 1 1.1 wide and 211 long, placed between Ti-Au contact pads. To measure the gain bandwidth we used two identical BWOs operating in the 120-140 GHz frequency range, one functioning as a local oscillator and the other as a signal source. The majority of the measurements were made at an ambient temperature of 4.5 K with optimal LO and DC bias. The maximum 3 dB bandwidth (about 4 GHz) was achieved for the devices made of films which were 2.5-3.5 nm thick, had a high critical temperature, and high critical current density. A theoretical analysis of bandwidth for these mixers based on the two-temperature model gives a good description of the experimental results if one assumes that the electron temperature is equal to the critical temperature.
|
|
|
Kawamura, J., Blundell, R., Tong, C. - Y. E., Gol'tsman, G., Gershenzon, E., Voronov, B., et al. (1997). Phonon-cooled NbN HEB mixers for submillimeter wavelengths. In Proc. 8th Int. Symp. Space Terahertz Technol. (pp. 23–28).
Abstract: The noise performance of receivers incorporating NbN phonon-cooled superconducting hot electron bolometric mixers is measured from 200 GHz to 900 GHz. The mixer elements are thin-film (thickness — 4 nm) NbN with —5 to 40 pm area fabricated on crystalline quartz sub- strates. The receiver noise temperature from 200 GHz to 900 GHz demonstrates no unexpected degradation with increasing frequency, being roughly TRx ,; 1-2 K The best receiver noise temperatures are 410 K (DSB) at 430 GHz, 483 K at 636 GHz, and 1150 K at 800 GHz.
|
|
|
Kerr, A. R., Feldman, M. J., & Pan, S. - K. (1997). Receiver noise temperature, the quantum noise limit, and zero–point fluctuations. In Proc. 8th Int. Symp. Space Terahertz Technol. (pp. 101–111).
|
|