Verevkin, A. A., Ptitsina, N. G., Smirnov, K. V., Voronov, B. M., Gol’tsman, G. N., Gershenson, E. M., et al. (1999). Multiple Andreev reflection in hybrid AlGaAs/GaAs structures with superconducting NbN contacts. Semicond., 33(5), 551–554.
Abstract: The conductivity of hybrid microstructures with superconducting contacts made of niobium nitride to a semiconductor with a two-dimensional electron gas in a AlGaAs/GaAs heterostructure has been investigated. Distinctive features of the behavior of the conductivity indicate the presence of multiple Andreev reflection at scattering centers in the normal region near the superconductor-semiconductor boundary.
|
|
|
Verevkin, A., Zhang, J., Pearlman, A., Slysz, W., Sobolewski, R., Korneev, A., et al. (2004). Ultimate sensitivity of superconducting single-photon detectors in the visible to infrared range.
Abstract: We present our quantum efficiency (QE) and noise equivalent power (NEP) measurements of the meandertype ultrathin NbN superconducting single-photon detector in the visible to infrared radiation range. The nanostructured devices with 3.5-nm film thickness demonstrate QE up to~ 10% at 1.3–1.55 µm wavelength, and up to 20% in the entire visible range. The detectors are sensitive to infrared radiation with the wavelengths down to~ 10 µm. NEP of about 2× 10-18 W/Hz1/2 was obtained at 1.3 µm wavelength. Such high sensitivity together with GHz-range counting speed, make NbN photon counters very promising for efficient, ultrafast quantum communications and another applications. We discuss the origin of dark counts in our devices and their ultimate sensitivity in terms of the resistive fluctuations in our superconducting nanostructured devices.
|
|
|
Korneev, A., Minaeva, O., Rubtsova, I., Milostnaya, I., Chulkova, G., Voronov, B., et al. (2005). Superconducting single-photon ultrathin NbN film detector. Quantum Electronics, 35(8), 698–700.
Abstract: Superconducting single-photon ultrathin NbN film detectors are studied. The development of manufacturing technology of detectors and the reduction of their operating temperature down to 2 K resulted in a considerable increase in their quantum efficiency, which reached in the visible region (at 0.56 μm) 30%—40%, i.e., achieved the limit determined by the absorption coefficient of the film. The quantum efficiency exponentially decreases with increasing wavelength, being equal to ~20% at 1.55 μm and ~0.02% at 5 μm. For the dark count rate of ~10-4s-1, the experimental equivalent noise power was 1.5×10-20 W Hz-1/2; it can be decreased in the future down to the record low value of 5×10-21 W Hz-1/2. The time resolution of the detector is 30 ps.
|
|
|
Slysz, W., Wegrzecki, M., Bar, J., Grabiec, P., Górska, M., Latta, C., et al. (2005). Fiber-coupled quantum-communications receiver based on two NbN superconducting single-photon detectors. In A. Rogalski, E. L. Dereniak, & F. F. Sizov (Eds.), Proc. SPIE (Vol. 5957, 59571K (1 to 10)). SPIE.
Abstract: We present the design and performance of a novel, two-channel single-photon receiver, based on two fiber-coupled NbN superconducting single-photon detectors (SSPDs). The SSPDs are nanostructured superconducting meanders covering an area of 100 μm2 and are known for ultrafast and efficient counting of single, visible-to-infrared photons. Their operation has been explained within a phenomenological hot-electron photoresponse model. Our receiver is intended for fiber-based quantum cryptography and communication systems, operational at near-infrared (NIR) telecommunication wavelengths, λ = 1.3 μm and λ = 1.55 μm. Coupling between the NbN detector and a single-mode optical fiber was achieved using a specially designed, micromechanical photoresist ring, positioned directly over the SSPD active area. The positioning accuracy of the ring was below 1 μm. The receiver with SSPDs was placed (immersed) in a standard liquid-helium transport Dewar and kept without interruption for over two months at 4.2 K. At the same time, the optical fiber inputs and electrical outputs were kept at room temperature. Our best system reached a system quantum efficiency of up to 0.3 % in the NIR radiation range, with the detector coupling efficiency of about 30 %. The response time was measured to be about 250 ps and was limited by our read-out electronics. The measured jitter was close to 35 ps. The presented performance parameters show that our NIR single photon detectors are suitable for practical quantum cryptography and for applications in quantum-correlation experiments.
|
|
|
Goltsman, G., Korneev, A., Minaeva, O., Rubtsova, I., Chulkova, G., Milostnaya, I., et al. (2005). Advanced nanostructured optical NbN single-photon detector operated at 2.0 K. In M. Razeghi, & G. J. Brown (Eds.), Proc. SPIE (Vol. 5732, pp. 520–529). Spie.
Abstract: We present our studies on quantum efficiency (QE), dark counts, and noise equivalent power (NEP) of the latest generation of nanostructured NbN superconducting single-photon detectors (SSPDs) operated at 2.0 K. Our SSPDs are based on 4 nm-thick NbN films, patterned by electron beam lithography as highly-uniform 100÷120-nm-wide meander-shaped stripes, covering the total area of 10x10 μm2 with the meander filling factor of 0.7. Advances in the fabrication process and low-temperature operation lead to QE as high as 30-40% for visible-light photons (0.56 μm wavelength)-the saturation value, limited by optical absorption of the NbN film. For 1.55 μm photons, QE was 20% and decreased exponentially with the wavelength reaching 0.02% at the 5-μm wavelength. Being operated at 2.0-K temperature the SSPDs revealed an exponential decrease of the dark count rate, what along with the high QE, resulted in the NEP as low as 5x10-21 W/Hz-1/2, the lowest value ever reported for near-infrared optical detectors. The SSPD counting rate was measured to be above 1 GHz with the pulse-to-pulse jitter below 20 ps. Our nanostructured NbN SSPDs operated at 2.0 K significantly outperform their semiconducting counterparts and find practical applications ranging from noninvasive testing of CMOS VLSI integrated circuits to ultrafast quantum communications and quantum cryptography.
|
|